Kestane Odununun Laminasyon Özelliklerinin Belirlenmesi

The Determination of Lamination Properties of the Chestnut Wood

Journal Name:

Publication Year:

Keywords (Original Language):

Abstract (2. Language): 
In this study, it was researched that the difference of lamination layer, glue types and the effect of modification of glues upon the bending resistance. For this purpose, having examined the properties of the chestnut wood, an alternative wood in our country was researched as a substitution for the other kind of wood. The sample prepared from chestnut wood as 3,4 and 5 layers each of which were 22x50x500 mm in lenght were glued with polivinilacetat , poliüretan and ureaformaldehyde glues and the modification of these glues with borax acide. Bending tests were applied to the previously prepared samples according to DIN 52186. At the end of the tests, the differences at lamination layers were observed at the sample of 4 and 5 layers according to %5 importance degree. The differences were proved by applying Tukey test to the groups that were made variance analysis. The glue types or modification of glues with borax were had no effect on samples.
Abstract (Original Language): 
Bu çalışmada, laminasyon katman farkı, tutkal çeşidi ve tutkal modifikasyonunun eğilme direncine etkileri araştırılmıştır. Kestane ağacının özellikleri tespit edilerek, laminasyonda diğer ağaç türlerine alternatif olup olamayacağı araştırılmıştır. 3, 4 ve 5 katmanlı 20x20x300 mm boyutundaki ahşap levhalar kestane ağacından elde edilmiş, polivinil asetat, poliüretan ve üre formaldehit tutkalları ile bu tutkallara borik asit ilave edilerek numuneler hazırlanmıştır. Deneyler sonucunda, laminasyon katmanlarında % önem seviyesine göre 4 ve 5 katlı örneklerde farklılıklar görülmüştür. Varyans analizi yapılan gruplara Tukey testi uygulanarak farklılıklar ispat edilmiştir. Tutkal çeşitleri ve tutkalın borla modifikasyonun eğilme direncine etkisinin olmadığı görülmüştür.
15-25

REFERENCES

References: 

Altınok. M., 1995. Tutkallar ve Tutkallama Teknikleri. Yüksek Lisans Ders Notları, 17
s.. Gazi Üniversitesi, Ankara. Bridaux,V., B. Clıarrier, N. Fauroux, F. Clıarrier and J. Goncalez, 2001. Addition
of boron based compound in the lvl glueline, effect on the mechanical properties
and the leaching of boron. Holzforschung. 55: 559-562. Bozkurt, A.Y., A. Kurtoğlıı, 1979. Yapıştırılmış tabakalı ağaç yapı elemanları.
İstanbul Üniversitesi Orman Fakültesi Dergisi Seri B.
29 (2): 39-59. Chung, Y., 1968. Glueabilty of southern pie early wood and late wood. Forest Products
Journal. 18. 32-36.
Eckelman, C.A., 1993. Potential uses of laminated veneer lumber in furniture. Forest
Product Journal. 43: 19-24. F.P.L., 1987. Handbook of Wood Based Materials for Engineers, Architects and
Builder. Forest Product Laboratory, Forest Service, U.S., Department of
Agriculture.
Marra, A. A., 1992. Tecnology of Wood Bonding. New York.
Marx, CM., and R. C. Moody, 1982. Effect of lumber width and tension laminated quality on the bending streight of four ply laminated beans. Forest Products Journal. 32 (1).
Mc Namara, \V. S. and D. Waters, 1970. Comparison of the rate glue-line strenght
development for oak and maple. Forest Product Journal. 20: (3). Örs, Y. ve H. Keskin, 2001, Ağaç Malzeme Bilgisi. Gazi Üniversitesi Yayın No:
2000/352.
Atla
s Yayıncılık No: 2, İstanbul. Taşçı, A., 1993. Bollanmış Çeliklerin Aşınma ve Korozyon Dayanımları. Yüksek
Lisans Tezi. İstanbul Üniversitesi, Fen Bilimleri Enstitüsü. İstanbul. Topal, A., 2001, Petrol Orada İse Bor Burada . 10-15 s., Yeni Avrasya Dergisi. TSE 53. Odunun Fiziksel Özelliklerinin Tayini İçin Numune Alma, Muayene ve Deney
Metotları. Türk Standartları Enstitüsü, Ankara. TSE 2474. Odunun Statik Eğilme Dayanımının Tayini. Türk Standartları Enstitüsü,
Ankara.

Thank you for copying data from http://www.arastirmax.com