Pim Bağlantılı Tabakalı Kompozit Levhalarda Fiber Takviye Açısının Hasar Tipine Etkisi

Effect of Fiber Orientation Angle on the Failure Mode of Pin Jointed Laminated Composite Plates

Journal Name:

  • Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi

Publication Year:

  • 2010

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the major aim is to investigate change effects of fiber orientation angles on the failure loads and failure modes for the pin jointed laminated composite plates. In the analysis, laminated composite plates with epoxy matrix resin reinforced unidirectional carbon fibers are used. The ply arrangements are chosen [90]4 and 9; fiber reinforced angle changes from 00 to 900 with 150 increments. The failure load and failure mode are analyzed experimentally and numerically. In the numerical analysis Ansys program is used. In the program, material properties are degraded using APDL code which is written for progressive failure analysis and contains Hashin failure criteria for laminated composite plates. In the experimental study, the maximum failure load for [150]4 laminae cofiguration, 749.917 N and minimum failure load for [600]4, 467.483 N laminae configuration are obtained. A good agreement between experimental and numerical solution is obtained.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, pim bağlantılı tabakalı kompozit levhalarda fiber takviye açısının değişiminin hasar yükleri ve hasar tipleri üzerindeki etkileri araştırılmıştır. Analizlerde tek yönlü karbon fiberlerle takviye edilmiş epoksi reçine matriksli tabakalı kompozit levhalar kullanılmıştır. Tabaka dizilimleri [9°]4 olmak üzere, 9; fiber takviye açısı 00 'den 900'ye kadar 150'lik artımlarla seçilmiştir. Levhaların farklı fiber takviye açılarındaki hasar yükü ve hasar tipleri deneysel ve sayısal olarak bulunmuştur. Sayısal çalışmada Ansys programı kullanılmıştır. Tabakalı kompozit levhaların ilerlemeli hasar analizi için Hashin hasar kriteri kullanan APDL kodları yazılarak malzeme indirgemeleri yapılmıştır. Deneysel çalışmada en büyük hasar yükü 749.917 N ile [150]4 tabaka dizilimi için ve en düşük hasar yükü ise 467.483 N ile [600]4 tabaka dizilimi için elde edilmiştir. Sayısal ve deneysel çalışma sonuçlarının uyumlu olduğu tespit edilmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-pim-baglantili-tabakali-kompozit-levhalarda-fiber-takviye-acisinin-hasar-tipine-etkisi.pdf
  • 2
213
220
  • Turkish

REFERENCES

References: 

Aktaş, A.
2005
. "Bearing Strength of Carbon Epoxy Laminates under Static and Dynamic Loading" Composite Structures. 67 (4), 485-489.
Aktaş,
A
. and Dirikolu, M. H. 2004. "An Experimental and Numerical Investigation of Strength Characteristics of Carbon-Epoxy Pinned-Joint Plates" Composites Science and Technology. 64 (10-11), 1605-1611.
İçten,
B.,M
. and Karakuzu, R. 2002. "Progressive Failure Analysis of Pin-Loaded Carbon-Epoxy Woven Composite Plates" Composites Science and Technology. 62 (9), 1259¬1271.
Karakuzu, R., Gülem, T. and İçten, B. M. 2006. "Failure Analysis of Woven Laminated Glass-Vinylester Composites with Pin-Loaded Hole" Composite Structures. 72 (1), 27-32.
ANSYS, 2007. ANSYS 11.0 Academic Teaching Introductory Help Menu.
Camanho, P. P. and Matthews, F. L. 1997. "Stress Analysis and Strength Prediction of Mechanically Fastened Joints in FRP : A Review" Composites. 28 (6), 529- 547.
Dursun, T. ve Özbay, M. 2008. "Tabakalı Kompozit Levhalarda Hasar İlerleme Modellemesi" Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi. 23 (1), 65-68.
Echavama, C., Haller, P. and Salenikovich, A.
2007
. "Analytical Study of a Pin-Loaded Hole in Elastic Orthotropic Plates" Composite Structures. 79 (1), 107-112.
İçten,
B.,M
. and Sayman, O. 2003. "Failure Analysis of Pin-Loaded Aluminum-Glass-Epoxy Sandwich Composite Plates" Composites Science and Technology. 63 (5), 727-737.
McCarthy, M., A., McCarthy, C., T., Lawlor, V., P. and Stanley, W. F. 2005. "Three-Dimensional Finite Element Analysis of Single-Bolt, Single-Lap Composite Bolted Joints: Part I-Model Development and Validation" Composite Structures 71 (2),
140-158.
Okutan, B. and Karakuzu, R. 2003. "The Strength of Pinned Joints in Laminated Composites" Composites Science and Technology. 63 (6), 893-905.
Tserpes, K.I. Papanikos, P. and Kermanidis, T.H. 2001. "A Three Dimensional Progressive Damage Model for Bolted Joints in Composite Laminates Subjected to Tensile Loading" Fatigue Fracture Engineering Materials and Structures. 24 (10), 663- 675.
Whitworth, H.,A., Othieno, M. and Barton, O. 2003. "Failure Analysis of Composite Pin Loaded Joints" Composite Structures. 59 (2), 261-266.

Thank you for copying data from http://www.arastirmax.com