YAPI MALZEMESİ ÜRETİMİNDE GENLEŞTİRİLMİŞ PERLİT AGREGASI KULLANILABİLİRLİĞİNİN ARAŞTIRILMASI

INVESTIGATION OF AVAILABILITY OF EXPANDED PERLITE IN THE PRODUCTION OF CONSTRUCTION MATERIAL

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2014

Key Words:

Keywords (Original Language):

Author NameUniversity of Author
Abstract (2. Language): 
The aim of this study is investigation of wall stone reproducibility using expanded perlite aggregate as a main raw material. For this purpose, production parameters (burning period, burning temperature, pressing pressure ratio, chemical additive ratio, dimension analysis and water/solid (w/s) ratio and also engineering parameters such as weight per unit of volume, mechanical properties of produced control brick (with a dimension of 50x100x100 mm) were determined and optimized. The most effective values for the brick production were designated by changing optimization parameters like pressing pressure, burning temperature, burning period, holding (curing) time. As a result of the study, the lowest value of weight per unit of volume and the highest value of compressive strength were ascertained as 522.5±48.3 kg/m3 and 12.13±0.13 kg/cm2 respectively for the samples which were produced at 50 bar pressure and 200ºC temperature with 1 h burning period and w/s ratio of 1.0. However, obtained compressive strength values for the control sample produced without using binder were found to lower the standards of TS EN 771-1.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmanın amacı ana hammadde olarak genleştirilmiş perlit agregası kullanarak duvar örgü elemanı üretilebilirliğinin araştırılmasıdır. Bu amaçla üretilen kontrol numunesinin (50x100x100 mm ebadında) birim hacim ağırlık (BHA), mekanik özellikler gibi mühendislik özellikleri ile beraber, üretim parametreleri (pişme süresi, pişme sıcaklığı, sıkıştırma basınç oranı, kimyasal katkı oranı, boyut analizi ve su/katı oranı) belirlenerek optimize edilmiştir. Sıkıştırma basıncı, pişme sıcaklığı, pişme süresi, bekleme (kür) süresi gibi tasarım parametreleri değiştirilerek, numune üretimi için en etkin değerler belirlenmiştir. Çalışmalar sonucunda, su/katı oranı 1,0 olan, 50 bar basınçta üretilen ve 200ºC sıcaklıkta 1 saat süreyle pişirilen numunelerden en düşük birim hacim ağırlık 522,5±48,3 kg/m3 ve en yüksek basınç dayanımı 12,13±0,13 kg/cm2 olarak tespit edilmiştir. Ancak, doğal bağlayıcı kullanmadan üretilen kontrol numune için elde edilen basınç dayanımı değerleri TS EN 771-1 sınır değerlerinin altında bulunmuştur.
FULL TEXT (PDF): 
PDF icon arastirmax-yapi-malzemesi-uretiminde-genlestirilmis-perlit-agregasi-kullanilabilirliginin-arastirilmasi.pdf
  • 3
451
458
  • Turkish

REFERENCES

References: 

1. Çelik, A.G., Bor Katkılı Perlit Karışımlardan
Hafif Tuğla Üretimi ve Teknolojik
Özelliklerinin Belirlenmesi, Doktora Tezi,
Çukurova Üniversitesi, Fen Bilimleri Enstitüsü,
2010.
2. Çelik, A.G., Kılıç, A.M. ve Çakal, G.Ö.,
“Expanded Perlite Aggregate Characterization
For Use as a Lightweight Construction Raw
Material”, Physicochemical Problems of
Mineral Processing, Cilt 49, No 2, 689−700,
2013.
3. Çobanlı, M.R., Isı Direnci Yüksek Hafif Yapı
Malzemesi Üretimi, Yüksek Lisans Tezi,
Osmangazi Üniversitesi, Fen Bilimleri Enstitüsü,
1993.
4. Ayberk, M., “Perlitin Yapı Gereci Olarak
Kullanımı ve Yapı Maliyetine Etkisi”,
Endüstriyel Hammaddeler Sempozyumu,
İzmir, 203-206, 21-22 Nisan 1995.
5. http://www.conservationphysics.org/wallbuff/wal
lbuff.php
6. Shi, C., Wu, Y., Riefler, C. ve Wang, H.,
“Characteristics and Pozzolanic Reactivity of
Glass Powders”, Cement and Concrete
Research, Cilt 35, No 7, 987-993, 2005.
7. Low, N.M. ve Beadoin, J.J., “Mechanical
Properties and Microstructure of High Alumina
Cement- Based Binders Reinforced with Natural
Wollastonite Micro-Fibres”, Cement and
Concrete Research, Cilt 24, No 4, 650-660.
1994.
8. Jamei, M., Guiras, H., Chtourou, Y., Kallel, A.,
Romero, E. ve Georgopoulos, I., “Water
Retention Properties of Perlite as a Material with
Crushable Soft Particles”, Engineering Geology,
Cilt 122, No 3-4, 261–271, 2011.
9. Won, J.P., Kang, H.B., Lee, S.J., Lee, S.W. ve
Kang, J.W., “Thermal Characteristics of High-
Strength Polymer–Cement Composites with
Lightweight Aggregates and Polypropylene
Fiber”, Construction and Building Materials,
Cilt 25, No 10, 3810-3819, 2011.
10. Benk, A. ve Coban, A., “Possibility of Producing
Lightweight, Heat Insulating Bricks From
Pumice and H3PO4 or NH4NO3
- Hardened
Molasses Binder”, Ceramics International, Cilt
38, No 3, 2283-2293, 2012.
11. Munoz, P., Juárez, M.C., Morales, M.P. ve
Mendívil, M.A., “Improving The Thermal
Transmittance of Single-Brick Walls Built of
Clay Bricks Lightened with Paper Pulp”, Energy
and Buildings, Cilt 59, 171-180, 2013.
12. Karakoç, M.B., “Effect of Cooling Regimes on
Compressive Strength of Concrete with
Lightweight Aggregate Exposed to High
Temperature”, Construction and Building
Materials, Cilt 41, 21-25, 2013.
A.G. Çelik ve ark. Yapı Malzemesi Üretiminde Genleştirilmiş Perlit Agregası Kullanılabilirliğinin Araştırılması
458 Gazi Üniv. Müh. Mim. Fak. Der. Cilt 29, No 3, 2014
13. Demir, İ., “Alkali-Silika Reaksiyonu Etkisine
Maruz Aynı Oranda Silis Dumanı ve Uçucu Kül
İçeren Harçların Mekanik Özellikleri”, Journal
of the Faculty of Engineering and Architecture
of Gazi University, Cilt 25, No 4, 749-758,
2010.
14. Aydoğan, U., Bilen, M. ve Gürü, M., “Anortit
Seramik Malzeme Üretiminde Uçucu Kül ve
Borik Asitin Kullanılabilirliği”, Journal of the
Faculty of Engineering and Architecture of
Gazi University, Cilt 26, No 4, 761-769, 2011.
15. TS EN-771-1:Kagir Birimler-Tuğlalar, Deney
Metodları, 2010.
16. Brown, E.T., Rock Characterisation, Testing
and Monitoring, Pergamon Press, New York,
A.B.D.,ISRM, 1981.
17. TS 3529, Beton Agregalarında Özgül Ağırlık ve
Su Emme Oranı Tayini, Ankara,1980.
18. TS EN 933-1, Agregaların Geometrik Özellikleri
İçin Deneyler Kısım 2: Tane Boyutu Dağılım
Tayini-Deney Elekleri, Elek Göz Açıklıklarını
Anma Büyüklükleri, Ankara, 1996.
19. TS 699, Muayene ve Deney Metotları, Ankara,
2009.
20. TS 825, Binalarda ısı yalıtım kuralları, 81s,
Ankara,1998.

Thank you for copying data from http://www.arastirmax.com