PLAZMA (İYON) NİTRÜRLEME YÖNTEMİ VE MALZEME ÖZELLİKLERİ ÜZERİNDEKİ ETKİSİ

Journal Name:

  • Havacılık ve Uzay Teknolojileri Dergisi

Publication Year:

  • 2003

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
The surfaces of parts manufactured from steels and other alloys are subjected to higher stresses, greater abrasive forces and more direct environmental exposure than are the part interiors. When aggressive forces reach the limits of a material’s resistance, surface initiated fracture, fatigue, wear and corrosion occur. For these reasons, surface modification and enhancement have long been applied to steels. Ion (plasma) nitriding is one of the most widely used advanced surface modification techniques applied to steels. It has been used in the fabrication of components for the automobile industry, metallurgical industry and tool manufacturing. The purpose of this paper is to briefly review the plasma nitriding which is now being applied to steels. In particular, the benefits, limitations and processing principles are described.
Bookmark/Search this post with
Abstract (Original Language): 
Makina elemanları kendilerinden beklenilen fonksiyonları yerine getirirken, parçaların yüzeyleri iç kısımlarına nazaran daha yüksek gerilme ve daha yüksek aşındırıcı kuvvetlere maruz kalır. Bu gerilme ve kuvvetler malzemenin yüzey dayanım sınırını aşınca malzeme yüzeyinde kırılmalar başlar ve böylece aşınma ve korozyon oluşur. Bu nedenle daha uzun bir ömür için bu tür etkilere maruz kalan malzemelerin yüzey dayanımları arttırılmalıdır. İyon (plazma) nitrürleme yöntemi bu amaçla kullanılan bir yöntemdir. Özellikle otomotiv sanayinde, metalurji sektöründe ve takım imalat sanayinde uygulama alanı bulan iyon (plazma) nitrürleme yöntemi, çeliklerin yüzey sertleştirilmesinde yaygınca kullanılmaktadır. Bu çalışmanın amacı plazma nitrürleme yönteminin temel prensiplerini, avantajlarını, uygulama sınırlarını ve yöntemle ilgili güncel gelişmeleri incelemektir.
FULL TEXT (PDF): 
PDF icon arastirmax-plazma-iyon-nitrurleme-yontemi-malzeme-ozellikleri-uzerindeki-etkisi.pdf
  • 2
41
48
  • Turkish

REFERENCES

References: 

[1] Thelning K.E., “Steel and Heat Treating” Marcel
Decler Inc., New York, 260-320, 1994.
[2] Menthe, E., Rie K.T., Schultze J.W., Simson
S.,“Structure and properties of plasma-nitrided
stainless steel” Surface and Coating Technology, 74-
75, 412-416, 1995.
[3] Özbaysal, K., İnal O.T., Romig A.D., “Ionnitriding
behaviour of several tool steels”, Materials
Science and Engineering, A-78, 179-191, 1986.
[4] Sun,Y. Bell, T., “Plasma surface engineering of
low alloy steels”, Materials Science and Engineering,
A-140, 419-434, 1991.
[5] Karamış, M.B., “An investigation of the properties
and wear behavior of plasma-nitrided hot working
steel (H13)” Wear, 150, 331-342, 1991.
[6] Karamış, M.B., Gerçekçioğlu, E., “Wear
behaviour of plasma nitrided steels at ambient and
elevated temperatures”, Wear, 243, 76-84, 200.
[7] Berg, M., Budtz-Jorgensen,C.V., Schweitz K.O.,
“On plasma nitriding of steels”, Surface and Coating
Technology, 124, 25-31, 2000.
[8] Alves, C., Silva, E.F., Martinelli A.E., “Effect of
workpiece geometry on the uniformity of nitrided
layers”, Surface and Coating Technology, 139, 1-5,
2001.
[9] Jeong, B.Y., Kim, M., “Effect of the process
parameters on the layer formation behavior of plasma
nitrided steels”, Surface and Coating Technology,
141, 182-186, 2001.
[10] Çelik, A., Karadeniz S., “Investigation of
compound layer formed during ion nitriding of AISI
4140 Steel”, Surface and Coatings Technology, 80,
283-286, 1996.
[11] Park, J.S., Lee, S.Z., Kim, J.H., Lee K.N.,
“Tribological characteristics of ion nitrided sintered
steels”, Surface and Coatings Technology, 114, 169-
173, 1999.
[12] Michel, H., Czerwiec, T., Gantois, M., Ablitzer,
D., Ricard A., “Progress in the analysis of the
mechanisms of ion nitriding”, Surface and Coatings
Technology, 72, 103-111, 1995.
[13] Pranevicius, L., Templier, C., Meheust, J.P., “On
the mechanism of ion nitriding of an austenitic
stainless steel”, Surface and Coatings Technology,
135, 250-257, 2001.
[14] Fancey, K.S., Leyland, A., Egerton, D., Torres,
D., Matthews A., “The influence of process gas
characteristics on the properties of plasma nitrided
steel”, Surface and Coatings Technology, 76-77, 694-
699, 1995.
[15] Lee, C.K., Shih, H.C., “Structure and corrosive
wear resistans of plasma nitrided alloy steels”,
Corrosion, 50, 848-856, 1994.
[16] Çelik A., Efeoğlu İ., Alsaran A., “İyon nitrürleme
işleminden sonra ısıl işlemin iç yapıya etkisinin
araştırılması”, Bilim Günleri Sempozyumu-Denizli,
150-156, 1999.
[17] Alsaran, A., Çelik, A., “Structural
characterization of ion nitrided AISI 5140 low alloy
steel”, Materials Characterization, 35, 234-239, 1998.
[18] Musil, J., Vlcek, J., Ruzicka M., “Recent progress
in plasma nitriding”, Vacuum, 59, 940-951, 2000.
[19] Alsaran, A., Çelik, A., Çelik, C. Efeoğlu, İ.,
“İyon nitrürasyon ile yüzey sertleştirme işleminde
Plazma (iyon) Nitrürleme Yöntemi ve Malzeme Özellikleri Üzerindeki Etkisi
ÖZDEMİR, ERTEN
48
optimum çalışma şartlarının belirlenmesi”, 9.ncu
Uluslararası Makina Tasarım ve İmalat Kongresi,
ODTÜ, 2000.
[20] Metin, E., İnal, O.T., “Formation and growth of
iron nitrides during ion-nitriding”, Journal of
Materials Science, 22, 2783-2788, 1987.
[21] Çelik, A., Efeoğlu, İ., Sakar G., “Microstructure
and structural behavior of ion-nitrided AISI 8620
Steel”, Materials Characterization, 46, 39-44, 2001.

Thank you for copying data from http://www.arastirmax.com