KAN KONTAMİNASYONUNUN DAİMİ VE GEÇİCİ YAPIŞTIRMA SİMANLARININ KOMPRESSİF DAYANIKLILIK VE SERTLİĞİNE ETKİSİNİN İNCELENMESİ

EFFECT OF BLOOD CONTAMINATION ON THE COMPRESSIVE STRENGTH AND HARDNESS OF PERMANENT AND TEMPORARY LUTING CEMENTS

Journal Name:

  • Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 2006

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
The purpose of this study was to evaluate the effect of blood contamination on the compressive strength and hardness of temporary and permanent luting cements. A total of 120 specimens, 20 specimens (6 mm diameter, 12 mm height) for each dental cement were prepared. Half of samples for each material were contaminated with blood during mixing procedure. The samples of control group were not contaminated with blood. After 24 hours, compressive strength and hardness test (Vickers) were applied. According to the results of the compressive strength test, when control groups and groups have blood contamination were compared, the difference was found to be statisticaly significant. The results of hardness test showed that blood contamination had decreased the hardness values of luting cements.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışma, kaan kontamnnasyonunun geçici ve daimi oaarak kulan lan yapıştırıcı simanların kompressff dayanıklılık ve sertlikleri üzerine etkisini ince/emek amacıyla yapılmıştır. Her brr simandan 20 adet (6 mm çapında, 12 mm yüksekiğnnde) olmak üzere toplam 120 adet siman örnek hazırlanmıştır. Hazırlanan örneklerin yarısı karıştırma işlemi sırasında kan i/e kontamine edilmiş, kalan örnekler kan ile kontamine edilmemiş kontrol grubunu oluşturmuştur. Örnekler nazlandıktan 24 saat sonra, kompressff dayanıkHık ve sertlik testi (Vickers) uygulanmıştır. Kompressff dayanıkHık test sonuçlarına göre; kontrol grubu ve kan kontamnnasyonlu grupaar karşılaştırıldığında istatistiksel olarak önemi farklık bulunduğu beirlenmiştir. Sertlik testi sonuçları ise kan kontamnnasyonunun yapıştırıcı simanların sertliklerinde azalmaya neden olduğunu göstermektedir.
FULL TEXT (PDF): 
PDF icon arastirmax-kan-kontaminasyonunun-daimi-gecici-yapistirma-simanlarinin-kompressif-dayaniklilik-sertligine-etkisinin-incelenmesi.pdf
  • 2
10-15
  • Turkish

REFERENCES

References: 

1. Philips RW, Swartz ML, Lund MS, Moore RK, Vickery C. In vivo disintegration of iuting cements. JADA 1987; 114: 489-92.
2. Mesu FP. Degradation of luting cements measured in vitro. J Dent Res 1982; 61: 665-72.
3. GaRey DJ, Tjan AHL, James RA, Caputo AAA. Effects of thermocycinng, load-cyciing, and blood contamination on cemented imp/ant abutments. JProsthet Dent 1994; 71:124-32.
4.
Güldağ MÜÜ, Duymuş Yeşil Z. Tükürük kontaminasyonunun geçici ve daimi oaarak kul/anılan attı tür simanın kompressif dayanıkHık ve sertliğine etkisi. Atatürk ÜÜniv Diş Hek Fak Derg 1998; 8: 44-9.
5.
Zaimoğlu A, Can G, Ersoy AE, Aksu L. Diş hekimiğnnde maddeeer bilgisi. Ankara Üniversitesi Basımevi, Ankara, 1993: 305-54.
6.
Keyf F, Anıl N. Kan kontamnnasyonunun üç tür simanın kompressff dayanıkHık ve sertiğnne etkisi. Hacettepe Dış Hek Fak Derg 1997; 21:71-74.
7. Cragg RG. Restorative dental materials. 6 th ed. The CV Mosby, St. Louis, 1980: 94-98, 131-150.
8. Smith BGN. Planning and making crown and bridges. 2 nd ed. Dunttz, London 1990:129-130.
9. Smith DC. Dental cements. In: O'Brien WJ. Dental materials: Properties and selection. Quintessence Pubishnng Co, Chicago 1989; 213-243.
10. Ishikawa K, Takagi S, Chow LC, Ishikawa Y, Eanes ED, Asaoka K. Behavior of calcium phosphate cement in simulated blood plasma in vttro. Dent Mater 1994; 10:26-32.
11.
Yıldız N, Akbulut Ö, Brrcan H. İstatistiğe giriş. Uygulamalı temel bilgi/er çözümlü ve cevaplı sorular. Erzurum, 1999:30.
Atatürk Üniv. Diş Hek. Fak. Derg.
Cilt: 16, Sayı: 2, Yıl: 2006, Sayfa: 10-15
ALADAĞ, YEŞİL DUYMUŞ
12. Branco R, Hegdahl T. Physical properties of some znnc phosphate and polycarboxylate cements. Acta Odontol Scand 1983; 41:349-53.
13. Jorgensen KD, Hoist K. The relationship between the retention of cemented veneer crowns and the crushing strength of crowns and the crushing strength of cements. Acta Odont Scand 1967; 25: 355-9.
14. Stewens L. The properties of four fixed prosthodontic resin composite luting agents. In t J Prosthodont 1993; 6:384-88.
15. American Dental Association Councl on Dental Materials: New American Dental Association Specification No: 8 for Zinc Oxide- Eugenol Type Restorative Materials. JADA 1977; 95: 991-5.
16. American Dental Association Council on Dental Materials: Revised American National Standarts Instttute/Amerkkan Dental Association Specification No: 8 for Zinc Phosphate Cement. JADA 1978; 96:121-23.
17. Christensen GJ. Why is glass ionomer cement so popuaar? JADA 1994; 125:1257-1258.
18. Oin PS, Rudney JD, Hill EME. Retentive strength of six temporary dental cements. Quintessence Int 1990; 21:197-200.
19. Pas/ey EL, Tao L, Pashley DH. The sealing properties of temporary filing materials. J Prosthet Dent 1988; 60:292-7.

Thank you for copying data from http://www.arastirmax.com