SICAK DALDIRMA YÖNTEMİ İLE ALÜMİNYUM KAPLANAN ÇELİK MALZEMELERDE YÜKSEK SICAKLIK OKSİDASYONUNUN İNCELENMESİ

THE INVESTIGATION OF HIGH TEMPERATURE OXIDATION IN ALUMINIUM COATINGS USING HOT DEEP METHOD ON STEEL MATERIALS

Journal Name:

  • Dokuz Eylül Üniversitesi Mühendislik Fakültesi Fen ve Mühendislik Dergisi

Publication Year:

  • 2009

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the surface of SAE 1020 and AISI 316 were applied to aluminium (Al) coating by hot deep method. The oxidation resistance and microstructures were investigated of Al coating applied to the surface of different steels. Sample surfaces were coated with Al at the temperature of 750 °C in 10 minutes durations. Experimental samples were subjected to at the 800 °C temperature and diffusion tempering with 1 and 6 hours durations. The changes in the thickness of diffusion layer and microstructure of the surface, as a result of the processes applied, were examined. Weight variations in the samples oxidized in atmospheric conditions under the temperature of 900 °C with varying durations have also been measured. It was found that steel material which changes of little weight of the samples coated with Al resisted more than without coated Al for oxidation. It was indicated that coated with Al surface of steel protected from oxidation The changes of elements Fe, C, Al, Ni and Cr were investigated by microprobe analyses in surface region.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, genel yapı çeliği (Ç1020) ve paslanmaz çelik (AISI 316) malzemelerin yüzeyine sıcak daldırma yöntemiyle alüminyum (Al) kaplama uygulanmıştır. Yüzeyde oluşan Al kaplamanın mikroyapısı incelenerek, yüksek sıcaklık oksitlenmesine karşı gösterdiği direnç incelenmiştir. Numuneler 750 °C’deki sıvı Al içinde 10 dakika süreyle bekletilerek yüzeyleri Al ile kaplanmıştır. Daha sonra bu numunelere 800 °C sıcaklıkta 1 ve 6 saat süre ile nötr ortamda difüzyon tavlaması uygulanmıştır. Elementlerin difüzyonu, difüzyon tabakası kalınlığı ve oksitlenmeye karşı gösterdiği direnç incelenmiştir. Al kaplama yapılan ve yapılmayan numuneler 900 °C sıcaklıkta ve farklı sürelerde yüksek sıcaklık oksidasyonuna maruz bırakılarak yüzeyde oluşan ağırlık değişimleri ölçülmüştür. Al kaplanmış çelik numunelerde önemli miktarda ağırlık değişimi olmaması, Al kaplamanın çeliği oksitlenmeden koruduğunu göstermiştir. Malzemelerin bileşimindeki Fe, C, Al, Ni ve Cr elementlerinin Al kaplama ve difüzyon tabakasındaki değişimleri mikroprob analizi ile incelenmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-sicak-daldirma-yontemi-ile-aluminyum-kaplanan-celik-malzemelerde-yuksek-sicaklik-oksidasyonunun-incelenmesi.pdf
  • 31
1-9
  • Turkish

REFERENCES

References: 

Awan G. H., (2007): “The Morphology of Coating-Substrate Interface in Hot-Dip-Aluminized
Steels”, University of Engineering and Technology Lahore, PhD Thesis,
Awan G. H., Ahmed F., Ali L., Shuja M. S., Hasan F., (2008): “Effect of Coating-thickness on
the Formability of Hot Dip Aluminized Steel”, Pak. J. Engg. Appl. Sci. Vol. 2. pp.14-21.
An, J., Liu, Y.B., Zhang, M.Z., Yang, B., (2002): ”Effect of Si on the interfacial bonding
strength of Al–Pb alloy strips and hot-dip aluminized steel sheets by hot Rolling”, Journal
of Materials Processing Technology 120, pp. 30–36.
Bondareko, G.G., Borodulin, I.N., (1985): “Improving the Heat Resistance of Austenitic
Steels by Thermomechanical Treatment Method”, Metal Science and Heat Treatment 27,
pp. 624–627.
Çakır, A., (1998): “Korozyon Açısından Tasarım ve Malzeme Seçimi” 6. Korozyon
Sempozyumu, İzmir.
Çakır, A., (1990): “Metalik Korozyon İlkeleri ve Kontrolü”, s. 223-231, MMO Yayını.
Drewolt, R., (1969): “Diffusion Coatings for the Protection of Iron and Steel”, Anti
Corrosion, pp. 11-15.
Fang H.W., Li K.Y., Su T.L., Yang T.C.K., Chang J.S., Lin P.L., Chang W.C., (2008): “Dip
coating assisted polylactic acid deposition on steel surface: Film thickness affected by
drag force and gravity”, Materials Letters, Vol 62, Iss. 21-22, pp. 3739-3741.
Feliu, S., Barranco, V., (2003): “XPS study of the surface chemistry of conventional hot-dip
galvanised pure Zn, galvanneal and Zn–Al alloy coatings on steel”, Acta Materialia 51 pp.
5413–5424.
Glasbrenner, H., Nold, E., Voss, Z., (1997): “The influence of alloying elements on the hotdip
aluminizing process and on the subsequent high-temperature oxidation”, J Nuclear
Materials, pp. 24939–45.
Guillou L., Supiot Ph., Courtois V. L, (2008): “Oxidized barrier thin film from plasma grown
polysiloxane coating over austenitic stainless steel, Surface and Coatings Technology, Vol
202, Issue 17, pp 4233-4241.
Hocking, M.G., (1993): “Coatings Resistant to Erosive/Corrosive and Severe Environments”,
Surface and Coating Technology, 62, pp. 460-466.
Hwang, S. H., Song, J.H., Kim, Y.S., (2005): “Effects of carbon content of carbon steel on its
dissolution into a molten aluminium alloy”, Materials Science and Engineering A 390 pp.
437–443.
Kasaplar G., (2007): “Aluminyum Yüzeyindeki Oksit Tabakasının Okzalik Asit Anodizing
Yöntemiyle Geliştirilmesi”, Çukurova U. Fen Bil. Ens., Y L. Tezi.
Lee HY, Jung S.H, Lee SY, You YH, Ko, KH, (2005): “Correlation between Al2O3 particles
and interface of Al-Al2O3 coatings by cold spray”, Applied Surface Science. Vol. 252,
No. 5, pp. 1891-1898.
Pasinli, A., Köksal, N.S, (2004): “Alüminyum Kaplanan Çelik Malzemelerde Yüzey
Özelliklerinin İncelenmesi”, Mühendis ve Makina Dergisi, Sayı 536, S. 42–45.
Patermarakis, G., Moussoutzanis, K., (2003): “A Transport Phenomenon Analysis Criterion
Predicting Pitting Appearance During Al Anodizing In Sulphate Electrolytes”,
Chemical Engineering Communications, 190 (5): p. 1018–1040.
Stein-Fechner, K., Konys, J., Wederneyer, O., (1997),: “Investigations on the transformation
behaviour of the intermetallic phase (Fe, Cr)2Als formed on MANET II steel by
aluminizing”, J. Nucl. Mater. 249, pp. 33–38.
Tanaka J., Masumoto R., Ohsasa K., Narita T. (2002): “Effect of Mg and Si on the
Microstructure and Corrosion Behavior on Zn-Al Hot Dip Coatings on Low Carbon
Steel”, ISIJ International, Vol. 42, No:1, pp. 80-85.
Temel, A., (2002): “Alüminyum Alaşımlarının Korozyonu”, Makine Metal Teknolojileri
Dergisi, S.117.
Vagge S.T., Raja V.S. (2009): “Influence of strontium on electrochemical corrosion behavior
of hot-dip galvanized coating”, Surface and Coatings Technology, in Pres.
Yan, L., (2001): “Corrosion behaviour of hot dip zinc and zinc–aluminium coatings on steel in
seawater”, Bull. Mater. Sci., Vol. 24, No. 4, pp. 355–360.
Zhang Y., Pint BA., Garner GW., Cooley KM., Haynes JA, (2004): “Effect of cycle length on
the oxidation performance of iron aluminide coatings”, Surface and Coatings Technology,
Vol. 188-189, pp 35-40.
Zhaolin Z, Yedong H, Li L, Hongxi L, Yongnian D., (2009): “Low-temperature formation and
oxidation resistance of ultrafine aluminide coatings on Ni-base superalloy”, Surface and
Coatings Technology, Vol. 203, Issue 16, pp 2337-2342

Thank you for copying data from http://www.arastirmax.com