DOKUMA BAZALT-CAM VE FINDIK KABUĞU TAKVİYELİ POLİMER KOMPOZİTLERİNİN EĞİLME DAYANIMI VE ISI GEÇİRGENLİKLERİNİN İNCELENMESİ

INVESTIGATION OF FLEXURAL STRENGTH AND HEAT CONDUCTIVI TY PROPERTIES OF WOWEN BASALT-GLASS AND HAZELNUT SHELL REINFORCED POLYMER COMPOSITES

Journal Name:

Publication Year:

Keywords (Original Language):

Abstract (2. Language): 
In this study, composite material reinforced with woven basalt and glass fibre and hazelnut shell, polyester resin was used as matrix. Weight ratios of hazelnut shells was 5%. 3 different size of hazelnut shells were used. Flexural strength and heat conductivity properties of the composites were inverstigated.
Abstract (Original Language): 
Bu çalışmada bazalt ve cam dokuma kumaş ve fındık kabuklarının takviye malzemesi olarak kullanılmasıyla polimer matrisli kompozitler üretilmiştir. Matris olarak thermoset polyester reçine kullanılmıştır. Takviye malzemesinin içerisindeki fındık kabuklarının oranı ağırlıkça %5dir. Ayrıca 3 farklı boyutta fındık kabuğu kullanılmıştır. Üretilen kompozitlerin eğilme dayanımı ve ısı geçirgenlik özellikleri incelenmiştir.
119-126

REFERENCES

References: 

Berozashvili M., (2001), ‘Continuous Reinforcing Fibers are Being Offered for
Construction, Civil Engineering and Other Composites Applications’ Adv. Mater.
Com. News, Compos Worldwide, 21, 6, 5–6.
Carmisciano S., De Rosa I.M., Sarasini F., Tamburrano A., Valente M., (2011),
‘Basalt Woven Fiber Reinforced Vinylester Composites: Flexural and Electrical
Properties’, Materials and Design, 32, 337-342
Czigány T., (2007), ‘Trends in Fiber Reinforcements – The Future Belongs to Basalt
Fiber’, Express Polymer Letter, 1, 59.
Militky J., Kovacic V., Jitka Rubnerova J., (2002), ‘Influence of Thermal Treatment
on Tensile Failure of Basalt Fibers’, Engineering Fracture Mechanics, 69, 1025–
1033.
Sim J, Park C., Moon Y., (2005), ‘Characteristics of Basalt Fiber as a Strengthening
Material for Concrete Structures’, Composites: Part B, 36, 504–512.
ASTM D7264 / D7264M - 07 Standard Test Method for Flexural Properties of
Polymer Matrix Composite Materials

Thank you for copying data from http://www.arastirmax.com