DÖKÜM KURONLARDA DİŞ KESİMİNİN TUTUCULUĞA ETKİSİ

EFFECTS OF TOOTH PREPARATION, ON RETENTION OF CAST CROWNS

Journal Name:

Publication Year:

Keywords (Original Language):

Abstract (2. Language): 
In this study various degrees of occlusal convergence, which taken into consideration the length and diameter of cast crown preparations, was designed to obtain adequate resistance form. In order to test the validity of the resistance form, six groups of stainless steel dies were prepared. The crown's were prepared and casted with Cr-Ni alloy. 30 of this specimens were chemically etched and then cemented. Retention strength of each crown was tested in tension zones using an Instron testing machine, the results for each test group were listed in tables. Increase in tooth diameter and decrease in convergence degree result in retention increase on the other hand increase in etched crown retention was noticed. But retention of prepared etched crowns with an angle of 14 degree has not shown a significant difference.
Abstract (Original Language): 
Bu çalışmada, çeşitli derecelerde eğim gösteren döküm kuron preparasyonlarınm, uzunluk ve çaplarının değişkenliğine bağlı yeterli tutuculuk özellikleri araştırıldı. Maksimum tutuculuk özelliğinin elde edilebilmesi amacıyla değişen Özellikte toplam 60 adet diş preparasyon örnekleri paslanmaz çelikten hazırlandı. Bu örnekler üzerine hazırlanan kuron protezlerinin Cr-Ni alaşımından dökümleri yapıldı. 30 adet kuron protezlerinin içine kimyasal dağlama (etching) işlemi yapıldı. Tüm kuronlar paslanmaz çelikten hazırlanan diş örnekleri üzerine simante edildikten sonra, Instron Universal test cihazıyla çekme kuvveti ile dikey yönde uygulandı. Sonuçta dişin çapının artması, buna karşılık eğimin azalması ile tutuculuğun arttığı gözlendi. Ancak 14 derece eğimli diş preparasyonu üzerine hazırlanan kuronların kimyasal dağlama (etching) yapılmasıyla tutuculuk özelliklerinden anlamlı bir farklılık görülmedi.
305
311

REFERENCES

References: 

1- Chan CK, Boyer BD, Denehy GE, Aunan DC. Effect of metal etching on crown retention. / Prost Dent 1986: 55: 18-24.
2- Ferrari M, Cagidiaco MC, Borracchini A, Bertelli E. Evaluation of a chemical etching solution for nickel-chroniium-berylli-um and chromium-cobalt alloys. J Prost Dent 1989: 62: 516-22.
3- Foroozesh Y,
Poyrazoğl
u E, Altıntaş S. Döküm metal kuronlarda diş preparasyonu, metal alaşımları ve simanların retansi-yona elkileri. DişKlİn 1991: 4: 16-21.
4- Oldham DF, Swartz MS, Phillips RW. Retentive properties of dental cements. J Prost Dent 1991: 59. 281-8.
5- Parker MH, Gunderson RB, Gardner FM, Calverley MJ. Quantitative determination of taper adequate to provide resistance form./Prost Dent 1988: 59. 281-6.
6- Potts RG, Shillingburg TH, Duncanson MG. Retantion and resistance of preparations for cast restorations. / Prost Dent 1980. 43: 303-7.
7- Weed RM, Baez RJ. Method for determining adequate resistance form of complete cast crown preparations. J Prost Dent 1984. 52. 330-7.
8- Willey RL. Retention in the preparation of teeth for cast res-toralions. J Prost Dent 1976: 35. 526-30.
9- Worly JL, Hamm RC, Fraunhofer JA. Effects of cement on crown retention. J Prost Dent 1982. 48. 289-93.

Thank you for copying data from http://www.arastirmax.com