Kavak Odunundan Etanol-Su Yöntemiyle Çözünebilir Hamur Üretimi Olanaklarının Araştırılması

Dissolving Pulp Obtaining Possibilities by Organosolv PulpFrom Poplar Wood

Journal Name:

  • Kahramanmaraş Sütçü İmam Üniversitesi Doğa Bilimleri Dergisi

Publication Year:

  • 2002
Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, it was showed that it is possible to produce the dissolving pulp from fast growing species such as poplar by using organosolv pulping process with or without catalysts. In order to find optimum cooking conditions, 4 control and 30 different cooking experiments were done. The effects of ethanol ratio, cooking temperature and time as well as catalyst ratio were studied. After cooking, pulps produced were bleached by using chlorite delignification technique, following purification by cold-alkali extraction. The obtained results show that with the catalyst ratio exceeding 0.01 %, the pulp yield reduced to unacceptable level. Indicating that the high catalyst ratio is not suitable for pulp production under studied conditions. The best pulping result was taken at 40% ethanol consistency, 180 o C pulping temperature and 150 min reaction time without addition of and catalyst to pulping liquor. After bleaching and alkali purification, the properties of pulp produced were as follows; 30.7% yield, 95.67 % α-cellulose content, 677 cm3 /g viscosity, 82.87 % brightness, 1.80 % pentosans, 0.33 % copper number, 0.14 % ash ratio. It is concluded that the pulp meets the quality requirements for the dissolving grade pulp.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, çözücü olarak etanol-su karışımı kullanılarak hızlı gelişen türlerden olan kavak odunu ile çözünebilir hamur üretimi olanakları araştırılmıştır. En uygun pişirme koşullarını belirlemek için pişirme çözeltisindeki etanol oranı, pişirme sıcaklığı ve süresi, katalizör oranı sistematik olarak değiştirilip 30 adet ve kontrol pişirmesi olarak 4 olmak üzere toplam 34 adet pişirme yapılmıştır. Pişirme sonrası elde edilen hamurlar ağartma ve soğuk alkali saflaştırma işlemine tabi tutulmuştur. Elde edilen bulgularda, %0.01’den fazla oranda katalizör kullanılarak yapılan pişirmelerde aşırı degradasyon oluştuğu ve verimin kabul edilemeyecek derecede düştüğü görülmüştür ve yüksek konsantrasyonlu katalizör oranının üretim için uygun olmadığı ortaya çıkmıştır. Sonuç olarak optimum hamur özellikleri; katalizör kullanılmadan (%0.00), etanol oranı % 40, çözelti / yonga oranı 8 / 1, maksimum sıcaklık 180 0 C ve maksimum sıcaklıkta pişirme süresi 150 dakika olan pişirmede elde edilmiştir. Ağartma ve alkali saflaştırma sonrası elde edilen çözünebilir hamurların başlangıçta kullanılan oduna göre verimi %30.74, alfa-selüloz %95.67 pentozanlar %1.80, viskozite 677 cm3 /g, parlaklık %82.87, bakır sayısı %0.33 ve kül oranı 0.14 olarak bulunmuştur. Sonuç olarak en uygun koşulda elde edilen kavak odunu organosolv hamurlarından elde edilen çözünebilir hamurun selüloz türevleri endüstrisinin kabul ettiği özellikleri karşıladığı görülmüştür.
FULL TEXT (PDF): 
PDF icon arastirmax-kavak-odunundan-etanol-su-yontemiyle-cozunebilir-hamur-uretimi-olanaklarinin-arastirilmasi.pdf
  • 1
72
85
  • Turkish

REFERENCES

References: 

Anonim, 1988. Pulps-Viscosity in Cupri-Ethylenediamine Solution, SCAN-CM 15:88,
Scandinavian Pulp, Paper and Board Testing Committee, Sweden.
Anonim, 1992. Tappi Test Methods 1992-1993. Tappi Press Atlanta, GA, USA.
Bostancı, Ş., 1985. Utilisation Possibilities of Alder Wood in Pulp and Paper Industry,
TUBITAK-TAOG Project Report No: 9, Ankara, p.83.
Browning, B.L., 1967. Methods of Wood Chemistry, Vol. 1-2, Interscience Publishers,
NY, USA.
Eroğlu, H. ve M. Usta, 1989. Investigations on Utilisation Possibilities of White Willow
(Salix alba L.) Wood in Pulp and Paper Industry, Journal of Agriculture and Forestry
of TUBITAK, 13(2): 235-245.
Fengel, D. ve G. Wegener, 1984. Wood: Chemistry, Ultrastructure, Reactions, Walter de
Gruyter, 613 s., Berlin
Huş, S., T. Tank ve E. Göksel, 1975. Fiber Morphology of Eucalyptus Camaldulensis
Wood and Utilisation Possibilities of its for Semichemical Pulping, TUBITAK
TOAG Research Report No:275/6, Ankara.
Kerr, A. J. ve V.D. Arwood, 1976. Prehydrolysis-Kraft Pulping of New Zealand beech,
Appita, 30(2): 135-142.
Kırcı, H., 1987. Investigations on the Utilisations Possibilities of Locust Wood (Robinia
pseudoacacia L.) in the Pulp and Paper Industry., Journal of Forestry Faculty of
KTU, 10(2): 64-90.
Kin, Z., 1990. The Acetolysis of Beech Wood. Tappi J., 73(11): 237-238.
Kleinert, T,N, 1974. Organosolv Pulping with Aqueous Alcohol. Tappi J,57(8)99-102.
Koll, P. ve H. Lenhardt, 1987. Organosolv-Aufschluss von Birkenholz in Einem
Durchstrmten Reaktor. Holzforschung, 41(2): 89-96.
Lora, J. H. ve S. Aziz, 1985. Organosolv Pulping: a Versatile Approach to Wood
Refining. Tappi J., 68(8): 94-97.
Nelson, P. J. ve G.M. Ivrine, 1992. Tearing Resistance in Soda-AQ and Kraft Pulps.
Tappi J., 75(1): 163-166.
Olsen, F., 1938 Purification of Cellulose, Industrial and Engineering Chemistry, 30(5):
524-526.,
Paszner, L. ve H.J. Cho, 1989. Organosolv Pulping: Acidic Catalysis Options and their
Effect on Fiber Quality and Delignification, Tappi J.,72(2):135-142.
Paszner, L. ve P.C. Chang, 1983. Productions of High-Yield Dissolving Pulp by the
Catalysed Organosolv Process. In Proceedings of International Dissolving and
Speciality Pulps Conference, Boston, 81-88.
Peter, W. ve O. Hoglinger, 1986. Herstellung von Kunstfaserzellstoff Nach dem
Organosolv-Aufschlussverfahren. Lenzinger Ber, 61: 12-16.
Rabinovich, H.T.S. ve J. Bueno. 1986. Obtaining Soluble Pulp of Eucalyptus Globulus
by Sulphate Process with Prehydrolysis, Revista Forestales del Peru, 13(2): 27-35.
Saake, B., R. Lehnen, S. Lummitsch ve H.H. Nimz, 1995. Production of Dissolving
and Paper Grade Pulps by the Formacell Process. Paper presented at the 8th
International Symposium on Wood and Pulping Chemistry, Book:2, Helsinki,
Finland, pp 237-242.
Saake, B., R. Lehnen, E. Schmekal, A. Neubauer ve H.H. Nimz, 1998. Bleaching of
Formacell Pulp from Aspen Wood with Ozone and Peracetic acid in Organic
Solvents. Holzforschung, 52(6): 643-650.
Sabatier, J., A. Irulegui ve J. Tomas, 1989. Ethanolic Pulping of Sugar Cane Bagasse.
Paper presented at 1989 International Symposium on Wood and Pulping Chemistry,
Raleigh, NC, pp. 781-783.
Solantausta, Y., 1985. The Solubilization of Wood in Potentially Wood Derivable
Solvents. VTT Research Report 376, p. 83.
Tank, T., 1978. Investigations on some Properties of Plane Wood in Relation with Pulp
and Paper Industry, Istanbul University Press, Book No: 2779/290, Istanbul.
Tank, T., 1980. NSSC Pulping Characteristics of Beech and Hornbeam Woods, Istanbul
University Press, Book No: 2779-231, Istanbul, 1980.
Wise, L. E. ve C. C. John, 1952. Wood Chemistry, Vol 1-2, Reinhold Publication co.,
NY, USA.

Thank you for copying data from http://www.arastirmax.com