Ayçiçeği (Helianthus annuus L.) Saplarından Üre-Formaldehit Tutkalı ile Yongalevha Üretimi

Manufacturing of Particleboard from Sunflower Stalks (Helianthus annuus L.) Using Urea-Formaldehyde Resin

Journal Name:

  • Kahramanmaraş Sütçü İmam Üniversitesi Doğa Bilimleri Dergisi

Publication Year:

  • 2002

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the technological properties of sunflower stalks (Helianthus annuus L.) (100 %) particleboards (700 kg/m3 ) produced using urea formaldehyde for general purpose under the laboratory conditions were investigated. The result showed that the mean value of bending strength, modulus of elasticity, internal bond strength and resistance to axial withdrawal strength of the specimens ranged from 14.3 to 17.5 N/mm2 , from 1941 to 2431 N/mm2 , from 0.26 to 0.46 N/mm2 and from 447.5 to 796.8 N, respectively. The increasing in thickness and water absorption for 24 hours also ranged from 19 to 42 % and from 77 to 95 %, respectively. It was understood that particleboards as suitable for standard produced from sunflower stalks. The study suggests that the sunflower stalks (3 billion tone/year), which were efficiently utilized in the industry, can be important raw materials to be used in the particleboard industry of Turkey
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, laboratuar şartlarında genel amaçlar için ayçiçeği saplarından (%100) (Helianthus annuus L.) üre formaldehit tutkalı kullanılarak üretilen yongalevhaların (700 kg/m3 ) teknolojik özellikleri incelenmiştir. Denemelerde, 24 saat suda bekletme sonucu kalınlık artışı % 19-42, su alma miktarı % 78-95, eğilme direnci 14.3-17.5 N/mm2 , elastikiyet modülü 1941-2431 N/mm2 , vida tutma gücü 447-796 N, yüzeye dik çekme direnci 0.26-0.46 N/mm2 olarak elde edilmiştir. Ayçiçeği saplarından üretilen yongalevhalarda tutkal kullanım oranı, pres basıncı ve pres süresinin artırılması ile teknolojik özelliklerinde iyileşme sağlanmıştır. Sonuçlar, ayçiçeği saplarından genel amaçlı ve kapalı ortamlar için yongalevha üretilebileceğini göstermiştir. Böylece, yeterince değerlendirilemeyen yaklaşık 3 milyon (ton/yıl) ayçiçeği sapı, Türkiye yongalevha endüstrisi için yeni bir hammadde kaynağı olabilecektir.
FULL TEXT (PDF): 
PDF icon arastirmax-aycicegi-helianthus-annuus-l.saplarindan-ure-formaldehit-tutkali-ile-yongalevha-uretimi.pdf
  • 2
49
56
  • Turkish

REFERENCES

References: 

Anonim, 1997. TS 642-ISO 554, Kondisyonlama ve/veya Deney İçin Standart
Atmosfer-Özellikler, TSE, Ankara.
Anonim, 1999. TS-EN 312-2, Yongalevhalar, Özellikler-Bölüm 2: Kuru Şartlarda
Kullanılan Genel Amaçlı Yongalevhaların Özellikleri, TSE, Ankara.
Anonim, 1999. TS-EN 312-3, Yongalevhalar, Özellikler-Bölüm 3: Kuru Şartlarda
Kapalı Ortamlarda Kullanılan (Mobilya Dahil) Yongalevhaların Özellikleri,
TSE, Ankara.
Anonim, 1999. TS-EN 326-1, Ahşap Esaslı Levhalar, Numune Alma Kesme ve
Muayene, Bölüm 1: Deney numunelerinin Seçimi, Kesimi ve Deney
Sonuçlarının Gösterilmesi, TSE, Ankara.
Anonim, 1999.TS-EN 310, Wood- based panels- Determination of modulus of
elasticity in bending and of bending strength, TSE, Ankara.
Anonim, 1999. TS-EN 319, Yonga ve Lif Levhalar, Levha Yüzeyine Dik Çekme
Direncinin Tayin Edilmesi, TSE, Ankara.
Anonim, 1993. ASTM-D 1037, American Society for Testing and Materials.
Standard Methods of Evaluating the Properties of Wood Base Fiber and Particle
Panel Materials, West Conshohocken, Pa.
Bektaş, İ., Y. Göker, H. Kalaycıoğlu, C. Güler, ve M. Nacar, 2001. Ayçiçeği
(Helianthus annuus L.) Saplarından Yongalevha Üretimi. Devlet Planlama
Teşkilatı Araştırma Projesi, Proje No: 98K/122160, Kahramanmaraş, 47 s.
BS 1811. 1969. Methods of Test for Wood Chipboard and Other Particleboards,
British Standarts Institution, London.
BS 2604. 1970. Resin-Bonded Wood Chipboard, British Standards Institution,
England.
Chow, P., J.J. Janoviak and E.W. Price, 1996. The Internal Bond and Shear Strength
of Hardwood Veneered Particleboard Composites, Wood and Fiber Science,
Vol: 18 (1), pp. 99-106.
Gertjejansen, R.O. 1972. Properties of Particleboard from Sunflower Stalks and
Aspen Planer Shavings. University of Minnesota Agriculture Experiment
Station, Technical Bulletin, No: 311, USA, pp. 8.
Anonim, 1997. TS 642-ISO 554, Kondisyonlama ve/veya Deney İçin Standart
Atmosfer-Özellikler, TSE, Ankara.
Anonim, 1999. TS-EN 312-2, Yongalevhalar, Özellikler-Bölüm 2: Kuru Şartlarda
Kullanılan Genel Amaçlı Yongalevhaların Özellikleri, TSE, Ankara.
Anonim, 1999. TS-EN 312-3, Yongalevhalar, Özellikler-Bölüm 3: Kuru Şartlarda
Kapalı Ortamlarda Kullanılan (Mobilya Dahil) Yongalevhaların Özellikleri,
TSE, Ankara.
Anonim, 1999. TS-EN 326-1, Ahşap Esaslı Levhalar, Numune Alma Kesme ve
Muayene, Bölüm 1: Deney numunelerinin Seçimi, Kesimi ve Deney
Sonuçlarının Gösterilmesi, TSE, Ankara.
Anonim, 1999.TS-EN 310, Wood- based panels- Determination of modulus of
elasticity in bending and of bending strength, TSE, Ankara.
Anonim, 1999. TS-EN 319, Yonga ve Lif Levhalar, Levha Yüzeyine Dik Çekme
Direncinin Tayin Edilmesi, TSE, Ankara.
Anonim, 1993. ASTM-D 1037, American Society for Testing and Materials.
Standard Methods of Evaluating the Properties of Wood Base Fiber and Particle
Panel Materials, West Conshohocken, Pa.
Bektaş, İ., Y. Göker, H. Kalaycıoğlu, C. Güler, ve M. Nacar, 2001. Ayçiçeği
(Helianthus annuus L.) Saplarından Yongalevha Üretimi. Devlet Planlama
Teşkilatı Araştırma Projesi, Proje No: 98K/122160, Kahramanmaraş, 47 s.
BS 1811. 1969. Methods of Test for Wood Chipboard and Other Particleboards,
British Standarts Institution, London.
BS 2604. 1970. Resin-Bonded Wood Chipboard, British Standards Institution,
England.
Chow, P., J.J. Janoviak and E.W. Price, 1996. The Internal Bond and Shear Strength
of Hardwood Veneered Particleboard Composites, Wood and Fiber Science,
Vol: 18 (1), pp. 99-106.
Gertjejansen, R.O. 1972. Properties of Particleboard from Sunflower Stalks and
Aspen Planer Shavings. University of Minnesota Agriculture Experiment
Station, Technical Bulletin, No: 311, USA, pp. 8.

Thank you for copying data from http://www.arastirmax.com