Polimer ilaveli harçlarda sülfat etkisinin ve alkali silis reaksiyonunun incelenmesi

Investigation of sulfate resistance and alkali silica reaction in polymer-incorporating mortars

Journal Name:

  • Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi

Publication Year:

  • 2016
DOI: 
10.5505/pajes.2015.78557

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, sulfate resistance and alkali silica reaction in mortars incorporating polymer were investigated. In this aim, normal portland cement and styrene-acrylic polymer emulsion were used. Mortar mixtures were prepared by replacing cement, with 0, 5, 10 and 15% polymer, by weight. 28-days compressive and flexural strength, water absorption and water sorptivity, porosity and unit weight of prepared mortar specimens were determined. Besides, sulfate resistance and alkali silica reaction resistance of prepared mortar mixtures were determined according to ASTM C1012 and ASTM C1260, respectively. Results obtained in polymeric mortar mixtures were comparatively evaluated with control mortar mixture.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, polimer ilaveli harçların sülfat etkisine ve alkali silika reaksiyonuna karşı direnci incelenmiştir. Bu amaçla, bağlayıcı olarak normal portland çimentosu ve stiren-akrilik polimer emülsiyonu kullanılmıştır. Polimer ağırlıkça %0, 5, 10 ve 15 oranlarında çimento yerine ikame edilerek harç karışımları hazırlanmıştır. Hazırlanan harç örneklerinin 28 günlük basınç ve eğilme dayanımları, kılcal yolla su emme, porozite, birim ağırlık gibi özellikleri belirlenmiştir. Ayrıca harç karışımlarının ASTM C1012 standardına göre sülfat direnci, ASTM C1260 standardına göre alkali silis reaksiyonuna karşı direnci saptanmıştır. Polimer ilaveli harçlarda elde edilen sonuçlar kontrol harcı ile kıyaslamalı olarak değerlendirilmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-polimer-ilaveli-harclarda-sulfat-etkisinin-alkali-silis-reaksiyonunun-incelenmesi.pdf
  • 6
413
417
  • Turkish

REFERENCES

References: 

[1] Özden ÇA. Polimer Betonların Donma-Çözülme Etkisine Dayanıklılığı. Yüksek Lisans Tezi, Namık Kemal Üniversitesi, Fen Bilimler Enstitüsü, Tekirdağ, Türkiye, 2010.
[2] Baradan B, Yazıcı H, Aydın S. Beton. İzmir, Türkiye, DEU Mühendislik Fakültesi Yayınları, 2012.
[3] Del Vecchio, FJC, Reis, JM, Da Costa Mattos, HS. “Elasto-Viscoplastic behaviour of polyester polymer mortars under monotonic and cyclic compression”. Polymer Testing, 35, 62-72, 2014.
[4] Fowler DW. “Polymers in concrete: A vision for the 21st century”. Cement and Concrete Composites, 21(5-6), 449-452, 1999.
[5] Gorninski JP, Dal Molin DC, Kazmierczak CS. “Study of the modulus of elasticity of polymer concrete compounds and comparative assessment of polymer concrete and Portland cement concrete”. Cement and Concrete Research, 34(11), 2091-2095, 2004.
[6] Ohama Y. “Recent progress in concrete-polymer composites”. Advanced Cement Based Materials, 5(2), 31-40, 1997.
[7] Rebeiz KS. “Precast use of polymer concrete using unsaturated polyester resin based on recycled PET waste”. Construction and Building Materials, 10(3), 215-220, 1995.
[8] Rebeiz KS. “Time-temperature properties of polymer concrete using recycled PET”. Cement and Concrete Composites, 17(2), 111-124, 1995.
[9] Soykan O, Özel C. “Polimer betonlarda kür süresinin fiziksel ve mekanik özelliklere etkisi”. Cumhuriyet Üniversitesi Fen Fakültesi Fen Bilimleri Dergisi, 35(2), 33-41, 2014.
[10] İnan, G. Değişik Tip Çimentoların ve Bunlarda Üretilen Betomların Sülfat Direnci. Yüksek Lisans Tezi, Ege Üniversitesi, Fen Bilimler Enstitüsü, İzmir, Türkiye, 2002.
[11] Al-Amoudi OSB. “Attack on plain and blended cements exposed to aggressive sulfate environments”. Cement and Concrete Composites, 24(3-4), 305-316, 2002.
[12] DePuy GW. Significance of Tests and Properties of Concrete and Concrete-Making Materials (Chemical Resistance of Concrete), American Society for Testing and Materials, Fredericksburg, 1994.
[13] Erdoğan TY. Beton. Ankara, Türkiye, ODTÜ Geliştirme Vakfı Yayıncılık ve İletişim AŞ. Yayını, 2003.
[14] Akman S. Yapı Malzemeleri. İstanbul, Türkiye, İTÜ İnşaat Fakültesi Matbaası, 1990.
[15] ASTM C1260. “Standard Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method)”.
[16] ASTM C128. “Standard Test Method for Relative Density (Specific Gravity) and Absorption of Fine Aggregate”.
[17] ASTM C29. “Standard Test Method for Bulk Density (Unit Weight) and Voids in Aggregate”.
Genleşme (%)Genleşme (%)Genleşme (%)Genleşme (%)Genleşme (%)Genleşme (%)Genleşme (%)Genleşme (%)Genleşme (%)
Zaman, (Gün) Zaman, (Gün) Zaman, (Gün) Zaman, (Gün) Zaman, (Gün) Zaman, (Gün) Zaman, (Gün) Zaman, (Gün)
[18] ASTM C642. “Standard Test Method for Density, Absorption, and Voids in Hardened Concrete1”.
[19] ASTM C1585. “Standard Test Method for Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes”.
[20] ASTM C1012. “Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution”.
[21] Şengül Ö, Doğan ÜA. “Polimer katkılı betonların mekanik ve durabilite özellikleri”. 5. Ulusal Beton Kongresi, İstanbul, Türkiye, 1-3 Ekim 2003.
[22] Saccani A, Motori A. “The effect of polymer addition on alkali silica reactions in cementitious mortars”. Materials and Structures, 34(6), 373-377, 2001.

Thank you for copying data from http://www.arastirmax.com