Diatomit ve hidrofob kil ile üretilen prefabrik yapı malzemesinin bazı özellikleri

Some properties of prefabricated building materials produced from ground diatomite and hydrophone clay

Journal Name:

  • Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi

Publication Year:

  • 2017
DOI: 
10.5505/pajes.2016.34467

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the effects of the mixture in different proportions on the physical and mechanical properties of hardened materials produced with diatomite (D) hydrophobic clay (HK) and cement (PC) were investigated at the prefabricated structural element production. For this purpose samples were prepared using cement rate of 10%, 20% and 30% and hydrophobic clay rate of 5%, 10% and 15% replacement of diatomite weight. The physical and mechanical properties of samples were tested after pressure is applied and 24 hours of steam curing. The combination of diatomite and hydrophobic clay produced samples with unit weight and compressive strength values of 1000-1300 kg/m3 and 4-18 MPa, respectively. Compared with conventional building materials of the products produced it was determined to have similar physical and mechanical properties.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, prefabrike yapı elemanı üretiminde diatomit (D) ve su itici özelliğe sahip hidrofob kilin (HK) çimento ile farklı oranlardaki karışımlarının fiziksel ve mekanik özelliklerine etkileri araştırılmıştır. Bu amaçla diatomit tozu yerine diatomit ağırlığının %5, %10 ve %15’i oranında hidrofob kil ve %10, %20 ve %30’u oranlarında da çimento kullanılarak örnekler hazırlanmıştır. Pres ve buhar kürü uygulanmış örnekler üzerinde basınç dayanımı, birim hacim ağırlık ve su emme özellikleri incelenmiştir. Diatomitin düşük oranlı çimento ve hidrofob kil ile karıştırılmasıyla üretilen örneklerin 1000-1300 kg/m3 birim hacim ağırlık ve 4-18 MPa arasında değişen basınç dayanımlarına sahip olduğu görülmüştür. Geleneksel yapı malzemeleriyle karşılaştırıldıklarında ise, benzer fiziksel ve mekanik özelliklere sahip olduğu belirlenmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-diatomit-hidrofob-kil-ile-uretilen-prefabrik-yapi-malzemesinin-bazi-ozellikleri.pdf
  • 3
245
249
  • Turkish

REFERENCES

References: 

[1] Baradan B. “Yapı Malzemesi II”. Dokuz Eylül Üniversitesi Mühendislik Mimarlık Fakültesi Yayınları, İzmir, Türkiye, 1991.
[2] Şahin S, Karaman S, Örüng İ, “Atık PVC katkili hafif betonlarin özellikleri ve tarımsal yapılarda kullanım olanakları”. Tekirdağ Ziraat Fakültesi Dergisi, 4(2), 137-144, 2007.
[3] Türkmen İ. Van-Erciş Pomzasından Üretilen Hafif Betonun Donma Çözülme Dayanıklılığının Araştırılması. Yüksek Lisans Tezi, Atatürk Üniversitesi, Erzurum, Türkiye, 1997.
[4] Düzgün OA. Çelik Liflerin Hafif Betonların Dayanımları Üzerine Etkisi. Yüksek Lisans Tezi, Atatürk Üniversitesi, Erzurum, Türkiye, 2001.
[5] Çelik Ç, Gürdal E. “Yerfıstığı kabuğunun agrega olarak kullanım olanakları”. ITÜ Dergisi/A Mimarlık, Planlama, Tasarım, 4(1), 37-46, 2005.
[6] Xu S, Wang J, Mac O, Zhao X, Zhang T. “Study on the lightweight hydraulic mortars designed by the use of diatomite as partial replacement of natural hydraulic lime and masonry waste as aggregate”. Construction and Building Materials, 73, 33-40, 2014.
[7] Ergün A. “Effects of the usage of diatomite and waste marble powder as partial replacement of cement on the mechanical properties of concrete”. Construction and Building Materials, 25(2), 806-812, 2011.
[8] Posi P, Lertnimoolchai S, Sata V, Chindaprasirt P. “Pressed lightweight concrete containing calcined diatomite aggregate”. Construction and Building Materials, 47, 896-901, 2013.
[9] Gökkonca EK. Diatomit Katkili Harçlarin Bazı Mekanik ve Fiziksel Özelliklerinin Değişiminin İncelenmesi. Yüksek Lisans Tezi, Pamukkale Üniversitesi, Denizli, Türkiye, 2010.
[10] Cong P, Chen S, Chen H. “Effects of diatomite on the properties of asphalt binder”. Construction and Building Materials, 30, 495-499, 2012.
[11] Mathers S. “Costa rican diatomite: A review of existing knowledge and future potential”. Revista Geologica de America Central, 10, 3-17, 1989.
[12] Ortaç K, Erdem M, Erdem B, Akdoğan E. “Farklı Tip Fonksiyonellik İçeren Organik/İnorganik Yapılar İle Kil Modifikasyonu ve Karakterizasyonu”. http://bildiri.anadolu.edu.tr/papers/bildirimakale/9936_b155q48.pdf (27.02.2016).
[13] Lin JJ, Chan Y, Lan Y. “Hydrophobic modification of layered clays and compatibility for epoxy nanocomposites”. Materials, 3(4), 2588-2605.
[14] Gerengi H, Kocak Y, Jazdzewska A, Kurtay M, Durgun H. “Electrochemical investigations on the corrosion behaviour of reinforcing steel in diatomite- and zeolite-containing concrete exposed to sulphuric acid”. Construction and Building Materials, (49) 471-477, 2013.
[15] Coppola L, Belz G, Dinelli G, Collepardi M. “Prefabricated building elements based on FGD gypsum and ashes from coal-fired electric generating plants”. Materials Structure, 29(5), 305-311, 1996.
[16] Al-Khaiat H, Haque MN. “Effect of initial curing on early strength and physical properties of a lightweight concrete”. Cement Concrete Research, 28(6), 859-66, 1998.
[17] Venkatarama BV, Lokrs SS, “Steam-Cured stabilized soil blocks for masonry construction”. Energy Build, 29(1), 29-33, 1998.
[18] Türk Standartları Enstitüsü. “Kâgir Birimler-Özellikler- Bölüm 3: Beton Kâgir Birimler (Yoğun ve Hafif Agregalı)”. Ankara, Türkiye, TS EN 771-3, 2011.
[19] Türk Standartları Enstitüsü. “Beton-Sertleşmiş Beton Deneyleri-Bölüm 7: Sertleşmiş Betonun Yoğunluğunun Tayini”. Ankara, Türkiye, TS EN 12390-7, 2002.
[20] Şahin S, Orung İ, Okuroğlu M, Karadutlu Y. “Properties of prefabricated building materials produced from ground pumice aggregate and binders”. Construction and Building Materials, 22(5), 989-992, 2008.
[21] Somayaji S. Civil Engineering Materials. 1th ed. Englewood Cliffs (NJ) USA, Prentice Hall, 1995.
[22] Ikeda K, Tomisaka T. “Fundamental studies on the preparation and strength of steam-cured porous materials made from mixture of fly ash, gypsum and lime”. Journal of the Ceramic Society of Japan, 97(1124), 468-474, 1989.
[23] Şahin S, Karaman S. “The properties of expanded polystyrene-pumice-gypsum blocks as a building material”. Journal of Tekirdag Agricultural Faculty, 9(1), 51-56, 2012.

Thank you for copying data from http://www.arastirmax.com