6063 alüminyu m alaşımının sertliği ve taneler arası korozyonu üzerine suni yaşlandırmanın etkisi

Effect of artificial aging on hardness and intergranular corrosion of 6063 Al alloy

Journal Name:

Publication Year:

DOI: 
10.5505/pajes.2016.05658

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the effect of artificial aging on hardness and the corrosion properties of6063 Al alloy was investigated. Time and temperature play a very important role in the precipitation hardening process of the Al-alloy. The results show that the variation in time and temperature have changed the hardness of aluminum alloy. Corrosion test revealed that the corrosion resistance of the alloy strongly depended on artificial aging times. The highest corrosion resistance for all artificial aging temperatures was observed at obtained the highest hardness value.
Abstract (Original Language): 
Bu çalışmada, 6063 alüminyum alaşımının sertliği ve korozyon özelliği üzerine suni yaşlandırmanın etkisi araştırılmıştır. Alüminyum alaşımının çökelme sertleşmesi prosesinde zaman ve sıcaklık önemli bir rol oynamaktadır. Sonuçlar, alüminyum alaşımının sertliğinin zaman ve sıcaklıktaki değişimler ile değiştiğini göstermektedir. Korozyon testi, alaşımın korozyon direncinin kuvvetli olarak suni yaşlandırma zamanına bağlı olduğunu göstermiştir. Tüm suni yaşlandırma sıcaklıkları için en yüksek korozyon direnci, elde edilen en yüksek sertlik değerinde gözlemlenmiştir.

REFERENCES

References: 

[1] Vargel C. Corrosion of Aluminium. 2nd ed. Kidlington, UK. Elsevier, 2004.
[2]
Noviko
v İİ. Metallerin Isıl İşlem Teorisi. 1. baskı. İstanbul, Türkiye, Nobel, 2012.
[3] Maisonnette D, Suery M, Nelias D, Chaudet P, Epicier T. "Effect of heat treatments on the microstructure and mechanical properties of a 6061 aluminium alloy". Materials Science a Engineering A, 528(6), 2718-2724,
2011.
[4] Li H, Zeng C, Han M, Liu J, Lu X. "Time-temperature-property curves for quench sensitivity of 6063 aluminum alloy". Transactions of Nonferrous Metals Society of China, 23(1), 38-45, 2013.
[5] Pratikno H. "Aging treatment to ıncrease the erosion-corrosion resistance of AA6063 alloys for marine application". Procedia Earth and Planetary Science, 14, 41-46, 2015.
[6] El-Menshawy K, El-Sayed A, El-Bedawy M, Ahmed HA, El-Raghy S. "Effect of aging time at low aging temperatures on the corrosion of aluminum alloy 6061". Corrosion Science, 54, 167-173, 2012.
[7] Li H, Mao Q, Wang Z, Miao F, Fang B, Song R, Zheng Z. "Simultaneously enhancing the tensile properties and intergranular corrosion resistance of Al-Mg-Si-Cu alloys by a thermo-mechanical treatment". Materials Science & Engineering A, 617, 165-174, 2014.
[8] Svenningsen G, Larsen MH, Walmsley JC, Nordlien JH, Nisancioglu K. "Effect of artificial aging on intergranular corrosion of extruded AlMgSi alloy with small Cu content". Corrosion Science, 48(6), 1528-1543, 2006.
[9] Svenningsen G, Larsen MH, Nordlien JH, Nisancioglu K. "Effect of high temperature heat treatment on intergranular corrosion of AlMgSi(Cu) model alloy". Corrosion Science, 48(1), 258-272, 2006.
[10]
Tür
k Standartları Enstitüsü. "Standart Arama". "https://intweb.tse.org.tr/Standard/Standard/Standard Ara.aspx (18.06.2016).
[11] Edwards GA, Stiller K, Dunlop GL, Couper MJ. "The Precipitation Sequence in Al-Mg-Si Alloys". Acta Metallurgica, 46(11), 3893-3904, 1998.
[12] Jones D. Principles and Prevention of Corrosion, 2nd ed. NJ,
USA, Prentice-Hall, 1996.

Thank you for copying data from http://www.arastirmax.com