EFFECT OF MECHANICAL ACTIVATION ON THE SODA ROASTING KINETICS OF CHROMITE
Journal Name:
- Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi
Keywords (Original Language):
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
Soda roasting kinetics of non-activated and mechanically activated chromite was investigated. It was determined that
the reaction was diffusion controlled between 700 – 900°C and chemical reaction controlled between 900 – 1200°C.
The activation energy of first step for soda roasting of non-activated chromite was 170 kJ/mol and this value
decreased to 141.8 kJ/mol for 30 min activated chromite and 79 kJ/mol for 120 min activated chromite. The activation
energies for the second step was calculated as 64.7 kJ/mol for non-activated chromite, 43 kJ/mol for 30 min activated
chromite and 25.1 kJ/mol for 120 min activated chromite. Mechanical activation reduced the activation energy for the
soda roasting of chromite.
Bookmark/Search this post with
Abstract (Original Language):
Mekanik aktive edilmemiş ve mekanik aktive edilmiş kromitin soda kavurması kinetiği incelenmiştir. Reaksiyonun
700-900°C aralığında difüzyon kontrollü, 900-1200°C aralığında ise kimyasal reaksiyon kontrollü olduğu tespit
edilmiştir. Mekanik aktive edilmemiş kromitin soda kavurmasında ilk kademenin aktivasyon enerjisi 170 kJ/mol olup
bu değer 30 dakika aktive edilmiş kromit için 141.8 kJ/mol, 120 dakika aktive edilmiş kromit için 79 kJ/mol değerine
düşmüştür. İkinci kademenin aktivasyon enerjileri ise aktive edilmemiş kromit için 64.7 kJ/mol, 30 dakika aktive
edilmiş kromit için 43 kJ/mol ve 120 dakika aktive edilmiş kromit için 25.1 kJ/mol olarak hesaplanmıştır. Mekanik
aktivasyon, kromitin soda kavurması için gerekli aktivasyon enerjisini düşürmüştür.