Nanokil Katkılı PVA/Kitosan Nanolif Sentezi ve Karakterizasyonu

Synthesis and Characterization of PVA/Chitosan Nanofiber Added Nanocla

Journal Name:

  • Süleyman Demirel Üniversitesi Fen Dergisi

Publication Year:

  • 2015

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, nanofibers have been prepared through the electrospinning method in which chitosan- a natural polymer- and polyvinyl alcohol (PVA) polymers were used. Gluteraldehide (GA) was added into the solution as cross-linker. A certain amount of nanoclay was added between the layers of the electrospun nanofibers to obtain PVA/Chitosan nanofiber and nanoclay layer. After that, the fiber morphology and fiber dimensions of the PVA/Chitosan nanofiber and nanoclay were examined by scanning electron microscope (SEM). As a result, it was determined that the diameter of the fiber was between 110 and 140 nm. By FT-IR analysis, the functional groups in the structure of the nanofiber-nanoclay layer and whether the cross-linkers formed were examined. Finally, the change of temperature and the weight loss in the sample were examined through TGA (thermal gravimetric analysis) and it was observed that two-stage degradation occurred.
Bookmark/Search this post with
Abstract (Original Language): 
Yapılan çalışmada, doğal bir polimer olan kitosan polimeri ile polivinil alkol (PVA) polimeri kullanılarak elektrostatik lif çekim (elektrospinning) yöntemi ile nananolif eldesi gerçekleştirilmiştir. Çapraz bağlayıcı olarak çözeltiye gluteraldehit (GA) ilave edilmiştir. Çekilen nanoliflerin arasına nanokil konularak PVA/Kitosan nanolif-nanokil yüzey elde edilmiştir. Elde edilen nanokil katkılı PVA/Kitosan nanolif yüzeyin taramalı elektron mikroskobu (SEM) görüntüleri alınarak lif morfolojisi ve lif boyutları incelenmiş ve lif çaplarının 110-140 nm arasında oluştuğu görülmüştür. FT-IR analizleri ile elde edilen yüzeyin yapısındaki fonksiyonel gruplar incelenmiş, çapraz bağların oluştuğu gözlenmiştir. TGA (termal gravimetrik analiz) yöntemi kullanılarak sıcaklık değişimi ile numunedeki ağırlık kaybı incelenmiş ve iki aşamalı bozunmanın gerçekleştiği görülmüştür.
FULL TEXT (PDF): 
PDF icon kitosan-nanolif-sentezi-karakterizasyonu.pdf
  • 1
118
128
  • Turkish

REFERENCES

References: 

[I]
Okutan N., 2013. Elektro yöndürme yöntemi ile elde edilen jelatin nanoliflerinin emülsiyonlarda
stabilize edici olarak kullanılması, Yüksek Lisans Tezi, Fen Bilimleri Enstitüsü, İstanbul Teknik
Üniversitesi, İstanbul, 139 s. [2] Kozanoğlu G., 2006. Elektrospinning yöntemi ile nanolif üretim teknolojisi, Yüksek Lisans Tezi, Fen
Bilimleri Enstitüsü, İstanbul Teknik Üniversitesi, İstanbul, 148 s. [3] Erem A.D., Özcan G., 2013. Polimer esaslı nanokompozitler ve tekstil uygulamaları. TMMOB Tekstil
Mühendisleri Odası, 20, 89. [4] Cengiz F., Jirsak O., Dayık M., 2009a. Ortam rutubetinin silindirli elektro lif çekim yöntemi ile nano
lif üretimi üzerine etkilerinin incelenmesi. Tekstil Teknolojileri Elektronik Dergisi, 3(3): 24-32. [5] Doğan G., Başal G., 2009. Elektrolif çekim yöntemine göre elde edilen biyopolimer nanoliflerin ilaç
salınım sistemleri yara örtüsü ve doku iskelesi olarak kullanımları, Tekstil Teknolojileri
Elektronik Dergisi 3, 2: 58-70. [6] İkiz Y., 2009. Elektro çekim yöntemi işlem parametrelerinin PVA nanolif morfolojisine etkileri,
Pamukkale Üniversitesi, Mühendislik Bilimleri Dergisi, Cilt 15, Sayı 3, Sayfa 363-369. [7] Bostan K., Aldemir T., Aydın A., 2007. Kitosan ve antimikrobiyal aktivitesi, İstanbul Üniversitesi
Veteriner Fakültesi Besin Hijyeni ve Teknolojisi Anabilim Dalı, İstanbul,TürkMikrobiyol Cem
Dergisi,
37 (2): 118-127.
[8] Koski K., Yim K., Shivkumar S. 2004. Effect of molecular weight on fibrous pva produced by
electrospinning, Materials Letters. 58: 493-497. [9] Son W. K., Youk J. H., Lee T. S., Park W. H. 2005. Effect of pH on electrospinning of poly vinyl
alcohol, Materials Letters., 59: 1571-1575. [10] Zhang Y., Huang X., Duan B., Wu L., Li S., Yuan X. 2007. Preparation of electrospun
chitosan/poly(vinyl
alcohol
) membranes, Colloid Polymer Science. 285: 855-863.
[II] Supaphol P., Chuangchote S. 2008. On the electrospinning of poly (vinyl alcohol) nanofiber Mats: A
Revisit, J. of Applied Polymer Science,. 108: 969-978. [12] Paipitak K., Porpra T., Mongkantalang P., Techitdheare W., Pecharapa W., 2010, Characterization of PVA-chitosan nanofibers prepared by electrospinning, 2nd International Science, Social Science, Engineering and Energy Conference 2010, Engineering Science and Management, Procedia Engineering 8: 101-105.
[13] Wanga X., Yang L., Zhang, J., Wanga C., Li O. 2014. Preparation and characterization of chitosan-poly(vinyl alcohol)/bentonite nanocomposites for adsorption of Hg(II) ions, Chemical Engineering Journal 251: 404-412.
[14] Haider S., Park S.Y. 2009. Preparation of the electrospun chitosan nanofibers and their applications to the adsorption of Cu(II) and Pb(II) ions from an aqueous solution, Journal of Membrane
Science 328: 90-96.
[15] Junior E. S. C., Edel F., Stancioli E. F. B., Mansur A. A. P.,Vasconcelos W. L., Mansur H. S. 2009. Preparation and characterization of chitosan/poly(vinyl alcohol) chemically crosslinked blends for biomedical applications Carbohydrate Polymers 76: 472-481.
[16] Hu H., Xin J. H., Hu H., Chan A., He L., 2013. Glutaraldehyde-chitosan and poly (vinyl alcohol) blends, and fluorescence of their nano-silica composite films, Carbohydrate Polymers 91: 305¬313.
[17] Toprakezer F., 2009.
Nanokompozi
t sentezinde kullanılacak na-bentonit kilinin saflaştırılması.
Yüksek Lisans Tezi, Fen Bilimleri Enstitüsü, Çukurova Üniversitesi, Adana, 68 s. [18] Zeng Q. H., Yu A. B., Lu G. Q., Paul D. R., 2005. Clay-based polymer nanocomposites: Research
and Commercial Development.
Journal of. Nanosc. Nanotech, 5 (10). [19] Elemen S., 2011. Nanokilin reaktif boyaları adsorplama özelliğinin incelenmesi, Yüksek Lisans Tezi,
Fen Bilimleri, Enstitüsü Ege Üniversitesi, İzmir, 69 s.
127
SDU Journal of Science (E-Journal), 2015, 10 (1): 118-128
[20] Guerra D.J.L., Mello I., Freitas L.R., Resende R., Silva R.A.R. 2014. Equilibrium, thermodynamic, and kinetic of Cr(VI) adsorption using amodified and unmodified bentonite clay, İnternational Journal of Mining Science and Technology. 24: 525-535.
[21]
Y
u Q., Song Y., Shi X., Xu C., Bin Y., 2011. Preparation and properties of chitosan derivative/poly(vinyl alcohol) blend film crosslinked with glutaraldehyde, Carbohydrate
Polymers 84: 465-470.
[22] Jia Y. T., Gong J., Gu X. H., Kim H. Y., Dong J., Shen X. Y., 2007. Fabrication and characterization
of poly (vinyl alcohol)/chitosan blend nanoWbers produced by electrospinning method,
Carbohydrate Polymers 67: 403-409. [23]
Kebapç
ı K., 2012. Kokulu mikrokapsüller, Yüksek Lisans Tezi, Fen Bilimleri Enstitüsü, Süleyman
Demirel Üniversitesi, Isparta,48 s. [24] Karaçay E., Alp E., Cabbar H.C., 2012. Sol-Jel yöntemiyle bor karbür üretimi ve karakterizasyonu,
Gazi Üniversitesi, Mühendislik-MimarlıkFakültesi Dergisi, 27(2): 417-428. [25] Turhan Y., Alp Z.,G., Alkan M., Doğan M., 2013. Preparation and characterization of
poly(vinylalcohol)/modifiedbentonite nanocomposites, Microporous and Mesoporous Materials
174: 144-153.

Thank you for copying data from http://www.arastirmax.com