PLAZMA İŞLEMİNİN REJENERE SELÜLOZ ESASLI LİFLERİN MEKANİK VE YÜZEY ÖZELLİKLERİNE ETKİSİNİN İNCELENMESİ

Investigation of Plasma Treatment Effects on Regenerated Cellulose Fibers’ Mechanical and Surface Properties

Journal Name:

  • Uludağ Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2008

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, Argon plasma treatment effects on regenerated cellulosic fibers’ surfaces and changing of the materials’ mechanical properties after plasma treatment were evaluated. Viscose rayon fibers and modal fibers were preferred for this study. Treatment time (min.) and RF discharge power (W) values were chosen as system modification parameters at fibers RF plasma treatment operation. For this purpose, separately nine studying was realized for every sample with 20W, 40W and 60W discharge power values and 10 min., 30 min. and 60 min. treatment times. The results of this study were discussed by scanning electron microscope (SEM) and Instron material strength test system. Finally, it’s observed that fibers’ surface roughness is increased and samples’ strength is decreased with increasing treatment time and RF discharge power values.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalısmada, Ar plazmanın selülozik esaslı liflerin yüzeylerine etkileri ve islem sonucu malzemelerin mekanik özelliklerinde meydana gelen değisimler incelenmistir. Selülozik esaslı malzemeler olarak viskoz rayonu ve modal lifleri tercih edilmistir. Liflerin RF Plazma sistemi ile muamelesi esnasında modifikasyon parametreleri olarak süre (dak.) ve bosalım gücü (W) değerleri seçilmistir. Bu amaçla; 20W, 40W ve 60W’lık bosalım gücü değerleri ve 10 dak., 30 dak. ve 60 dak.’lık islem süreleri ile kombine olarak her bir numune için dokuz farklı çalısma gerçeklestirilmistir. Sonuçlar, taramalı elektron mikroskobu (SEM) ve Instron mukavemet test cihazı kullanılarak değerlendirilmistir. Çalısma sonunda artan süre ve bosalım gücü değerleri ile liflerin yüzey pürüzlülüğünün farklı sekillerde artıs gösterdiği ve aynı zamanda numunelerin mukavemet değerlerinde ise genel bir düsmenin meydana geldiği gözlemlenmistir.
FULL TEXT (PDF): 
PDF icon arastirmax-plazma-isleminin-rejenere-seluloz-esasli-liflerin-mekanik-yuzey-ozelliklerine-etkisinin-incelenmesi.pdf
  • 2
139-150
  • Turkish

REFERENCES

References: 

1. Bae, B., Chun, B.-H., Kim, D. (2001) Surface Characterization of Microporous Polypropylene Membranes
Modified by Plasma Treatment, Polymer, 42, 7879-7885.
2. Chan C. M. (1994) Polymer Surface Modification and Characterisation, Hanser Publishers, Munich Vienna
New York
3. Eichhorn, S. J., Young, R. J., Yeh, W. Y. (2001) Deformation Processes in Regenerated Cellulose Fibers,
Textile Research Journal, 71(2):121-129
4. Güler, N. (2005) Farklı Rayon Tiplerinin Yorulma Davranıslarının Đncelenmesi, Uludağ Üniversitesi Mühendislik-
Mimarlık Fakültesi Tekstil Mühendisliği Bölümü, Bitirme Tezi
5. Inagaki, N., Tasoka, S., Shımada, S. (2001) Comparative Studies on Surface Modification of Poly(ethylene
terephthalate) by Remote and Direct Argon Plasmas, Journal of Applied Polymer Science, Vol. 79, 808-815
(2001)
6. Karahan, H. A., Demir, A., Özdoğan, E., Öktem, T., Seventekin, N. (2007) Plazma Teknolojisi ve Temel
Özellikleri, Ege Üniversitesi Tekstil Mühendisliği Bölümü, Tekstil Teknoloji Dergisi, Subat 2007-1, s.
102,104-106
7. Pastore, C.M., Kıekens P., 2001, Surface Characteristics of Fibers and Textiles, Marcel Dekker, Inc., New
York
8. www.tubitaktam.ege.edu.tr/index.php?lid=1&sid=0035

Thank you for copying data from http://www.arastirmax.com