FARKLI KESİTE SAHİP FİLAMENTLERDEN OLUŞAN POLİESTER İPLİKLERDE BÜKÜMÜN MUKAVEMET ÖZELLİKLERİNE ETKİSİ

Effect of Twist on Strength for Polyester Yarns Produced from Filaments Having Different Cross Sectional Shapes

Journal Name:

  • Uludağ Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2011

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this research, 24 types polyester yarn were produced in six different twist levels from filaments which had four different cross-sectional shapes. Tensile strength and breaking elongation of these 24 yarns were evaluated according to six twist levels. Statistical evaluations of the results showed that yarn twists have statistically important effect on tenacity and breaking elongation of all yarns. Also high regression coefficients were obtained between yarn properties and yarn twists. As tenacity results of untwisted yarns were considered, it was observed that values of yarns which were produced from hollow filaments decreased at a lower extent than that of the yarns produced from full filaments. Breaking elongation of yarns which were produced from hollow filaments showed higher changes than that of yarns produced from full filaments when compared to untwisted form.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada; aynı üretim parametreleriyle elde edilmiş 4 farklı kesit tipindeki filamentlerden oluşan poliester ipliklere, 6 farklı seviyede büküm uygulanmış ve toplamda 24 farklı ipliğe ait kopma mukavemeti ve kopma uzaması değerleri ile büküm miktarı arasındaki ilişki incelenmiştir. Çalışmada elde edilen sonuçlardan; farklı kesite sahip filamentlerden oluşan ipliklerin tamamında, bükümün kopma mukavemeti ve kopma uzaması değerleri üzerinde istatistiki olarak anlamlı bir etkiye sahip olduğu görülmüş, incelenen iplik özellikleriyle büküm arasında güçlü bir regresyon katsayısına sahip ilişkiler elde edilmiştir. Bükümsüz haldeki kopma mukavemet değerleri dikkate alındığında, içi boş filamentlerden oluşan iplik yapılarındaki kopma mukavemeti kaybı değerlerinin, içi dolu filamentlerden oluşan iplik yapılarındakine göre daha düşük olduğu gözlenmiştir. Kopma uzaması değerlerinde ise; içi boş filamentlerden oluşan iplik yapılarında gerek bükümsüz haldeki kopma uzaması değerlerine göre, gerekse uygulanan büküm miktarına göre daha yüksek değişimler görülmüştür.
FULL TEXT (PDF): 
PDF icon arastirmax-farkli-kesite-sahip-filamentlerden-olusan-poliester-ipliklerde-bukumun-mukavemet-ozelliklerine-etkisi.pdf
  • 2
45-53
  • Turkish

REFERENCES

References: 

1. Hearle, J. W. S., Grosberg, P. and Backer, S. (1969). Structural Mechanics of Fibers, Yarns, and
Fabrics, Wiley-Interscience, New York.
2. Lee, M. S., Oh, T. H., Kim, S. Y. and Shim, H. J. (1999). Deformation kinetics of polypropylene
hollow fibers in a continuous in a process, J Appl Polym Sci, 74, 1836-1845.
3. Lord, P. R. (2003). Handbook of Yarn Production: Technology, Science and Economics,
Woodhead Publishing Ltd., Philadelphia.
4. Nakajima, T. (1994). Advanced Fiber Spinning Technology, Woodhead Publishing Ltd.,
Philadelphia.
5. Omeroglu, S., Karaca, E. and Becerir, B. (2010). Comparison of bending, drapability and crease
recovery behaviors of woven fabrics produced from polyester fibers having different crosssectional
shapes, Text Res J, 80(12), 1180–1190.
6. Pan, N. (1993). Prediction of statistical strengths of twisted fibre structures, J Mater Sci, 28, 6107-
6114.
7. Petrulis, D. (2004). Fundamental study of the effect of the fiber wall thickness and inner diameter
on the structure of polyamide and polypropylene hollow fibers, Appl Polym Sci, 92, 2017-2022.
8. Rovere, A. D. and Shambaugh, R. L. (2001). Melt spun hollow fibers: Modelling and experiments,
Polym Eng Sci, 41, 1206-1219.
9. Rwei, S. P. (2001). Formation of hollow fibers in melt spinning process, J Appl Polym Sci, 82,
2896-2902.10. Saville, B. P. (2000). Physical Testing of Textiles, Woodhead Publishing Ltd., Cambridge.
11. Takarada, W., Ito, H., Kikutani, T. and Okuin, N. (2001). Studies on high speed melt spinning of
noncicurlar cross-section fibers. I. Structure analysis of as-spun fibers, J Appl Polym Sci, 80,
1575-1581.

Thank you for copying data from http://www.arastirmax.com