Bazik Çözeltilerde Molibdenin Anodik Oksidasyonu

Anodic oxidation of molybdenum in basic media

Journal Name:

  • Gazi Eğitim Fakültesi Dergisi

Publication Year:

  • 2002

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
The current potential curves of molybdenum were obtained in basic solutions at different potential ranges using the cyclic voltammetric method. The sodium hydroxide solutions of different concentrations were used as the working media. The anodic behaviours of molybdenum in stirred basic solutions were investigated. It was found that the stability of the passive film on molybdenum in basic solutions decreases due to formation of soluble species and the potentials of the transpassive dissolution depend on the concentration of solutions. In basic solutions a dissolution peak was observed before the transpassive dissolution’s peak, which was not found in acidic solutions.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada molibdenin bazik çözeltiler içinde değişik potansiyel aralıklarında geri dönüşümlü akım-potansiyel eğrileri (cyclic voltammogram) elde edilmiştir. Çalışma ortamıolarak sodyum hidroksitin farklıderişimlerdeki çözeltileri seçilmiştir. Molibden elektrotun sürekli hareket halinde olan ( karıştırılan ) sodyum hidroksit çözeltileri içindeki anodik davranışıincelenmiştir. Bu çözeltiler içinde molibdenin pasifliğinin bozulup transpasif çözünmenin başladığıpotansiyel değerinin derişime göre değiştiği saptanmışve asidik ortamlarda gözlenemeyen transpasif çözünme pikinden önce bir çözünme piki daha bulunmuştur.
FULL TEXT (PDF): 
PDF icon arastirmax-bazik-cozeltilerde-molibdenin-anodik-oksidasyonu.pdf
  • 2
177-122
  • Turkish

REFERENCES

References: 

Johnson, J.W., Chi, C.H., Chen, C.K., and James, W.J., 1970, Corr.-Nace., 26 (8), 238.
Goetz, R., and Landolt, D., 1982, Electrochim. Acta., 27 (8), 1061.
Goetz, R., and Landolt, D., 1984, Electrochim. Acta., 29 (5), 667.
Mischler, S., Vogel, A., Mathieu, H.J., and Landolt, D., 1991, Corr. Sci., 32 (9),
925.
Olefjord, I., Wegrelius, L., 1990, Corr. Sci., 31, 89.
Wikstrom, L.L. and Nobe, K., 1969, J.Electro.Chem. Soc., 116, 4, 525.
Lu, Y.C., Clayton, C.R., and Brooks, A.R., 1989, Corr. Sci., 29, 7, 863.
Mısırlıoğlu, Z. and Aksüt, A., 2002, J. of Sci. and Eng.Corr. (in press)
Lu, Y. C., Ives, M. B., 1992, Corr. Sci., 33 (2), 317.
Mısırlıoğlu, Z., 1994, Saf Demir ve Demir Molibden Alaşımlarının BazıSulu
Ortamlardaki Korozyonu, Ank.Üniv.Fen Bil.Ens., Ankara.
Badawy, W.A., and Al-Kharafi, F.M., 1998, Electrochim. Acta., 44, 693.
Kang, W., Ying-Sing, Li., He, P., 1998, Electrochim. Acta., 43 (16-17), 2459.
Pozdeeva, A.A., Antonowskaya, E.I., Sukhotin, A.M., 1966, Corr. Sci., 6, 149.
Lu, Y. C., and Clayton, C. R., 1989, Corr. Sc., 29, 8, 927.
El-Kharafi, F.M., Badawy, W.A., 1997, Electrochim. Acta., 42, 579.
Hull, M.N., 1971, J.Electroanal. Chem., 30, l.
Hull, M.N., 1972, J. Electroanal. Chem., 38, 143.
Povey, A.F., and Metcalfe, A.A., 1977, J. Electroanal. Chem., 84, 73.

Thank you for copying data from http://www.arastirmax.com