EFFECT OF MECHANICAL ACTIVATION AND IRON POWDER ADDITION ON ACIDIC LEACHING OF PSEUDORUTILE
Keywords (Original Language):
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
This study presents the effect of mechanical activation on iron removal from pseudorutile to obtain synthetic rutile by
hydrochloric acid leaching with or without iron addition as a reducing agent. Iron and titanium extraction efficiencies in
leaching for 3 h without iron addition are 64% and 49%, respectively. After mechanical activation of pseudorutile for
30 min, iron and titanium extraction efficiencies increased to 82% and 62%, respectively. In case of iron addition to
leaching step, mechanical activation has no prominent effect on the iron and titanium extractions. On the contrary, most
of iron content in pseudorutile dissolved but titanium oxide remains at the solid part. Effect of iron addition to the
leaching step was investigated with x-ray diffraction analysis of solid part.
Bookmark/Search this post with
Abstract (Original Language):
Bu çalışma, sentetik rutil elde etmek için, redükleyici olarak demir ilaveli veya ilavesiz sülfürik asit liçiyle
pseudorutilden demirin giderilmesi üzerine mekanik aktivasyonun etkisini sunmaktadır. Demir ilave edilmeksizin 3
saatlik liç işlemlerinde demir ve titanyum ekstraksiyon verimleri sırasıyla %64 ve %49 dur. Pseudorutilin 30 dakikalık
mekanik aktivasyonundan sonra demir ve titanyum ekstraksiyon verimleri sırasıyla %82 ve %62 ye çıkmıştır. Liç
kademesine demir ilave edilmesi durumunda, mekanik aktivasyonun demir ve titanyumun ekstraksiyonlarına belirgin
bir etkisi olmamıştır. Aksine pseudorutildeki demir içeriğinin çoğu çözünmüş ancak titanyum katı kısımda kalmıştır.
Demir ilavesinin liç kademesine etkisi, katı kısmın x-ışını difraksiyon analizi ile incelenmiştir.
FULL TEXT (PDF):
- 1
18-21