FARKLI YÖNTEMLERLE POLİMERİZE EDİLEN AKRİLİK REZİNLERİN POROZİTE AÇISINDAN KARŞILAŞTIRILMASI

THE COMPARISON IN POJNT OF THE POROSITY OF ACRYLIC RESINS POLIMERISED BY USING DIFFERENT METHODS

Journal Name:

  • Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 2002

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
This study was realised to compare m point of the porosity of acrylic resins which are prepared in various thickness and polimerised by using different methods. 45 samples from each ol" three different acrylic resins were prepared. Total 135 acrylic resin sampler, having the dimensions of 20x20x2 mm, 20x20x4 mm and 20x20s.6 mm were prepared with various polimeri.sation methods. After the finishing and polishing procedures, they were immersed m Indian ink. They were evaluated in point of external porosity by using optic microscope. Than hall of the thickness of each sample were abrused. These samples were evaluated in view of internal porosity after they were painted with the same method. Datas obtained were evaluated with Kruskal-Wallis variant of analysis methods. It is statistically found that polimcrisalion method and the thickncsi are very important and the type of acrylic resin is not important
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışma, farklı yöntemlerle polimerice edilen değişik kaİ!îi!ıklafd?.ki akriiik reziillerin pomy.ite atçısından karşılaştırılması amacıyla yapıldı. Üç farklı akriiik recinin herbirinden, 45 adet olacak şekilde toplam 135 akrilîk rezin örnek, çeşitli polime-rizasyoıı yöntemleriyle 20x20x2 mm,, 20x20x4 mın. ve 20x20x6 mm. boyutlarında hazırlandı. Tesviye ve cilalama işlemlerini takiben, çini mürekkebine atılarak bekletildi. Tşık mikroskobunda, ekstcrnal porozite açısından değerlendirildi. Daha sonra yarıya kadar ağındırılıp, İnim, 2mm ve 3 mm. kalınlığa getirilen örnekler, aynı şekilde boyandıktan sonra internal porozite açısından değerlendirildi. Hide edile n verilerin değerlendirilmesinde, Kruskal-Wallis varyans analiz yöntemi kullanıldı. Akriiik tipinin önemli almadığı, polimeri/asyon tekniği (internal porozitede p<O.0OI, ekstcmal porozitede p< 0-01) ve kalınlığın (p<0.00l) ise çok önemli oldngıı istatistiksel olarak tespit edildi.
FULL TEXT (PDF): 
PDF icon arastirmax-farkli-yontemlerle-polimerize-edilen-akrilik-rezinlerin-porozite-acisindan-karsilastirilmasi.pdf
  • 2
25-30
  • Turkish

REFERENCES

References: 

1.
Tunue
r N, Tüfekçiliğin B. Mikrodalga enerjisi ve su içinde kaynatma yöntemi ile pof i ıncri/.e edilen değişik akriiik reçine örneklerinin poruzite açısından karçjlagtınlması. î Üniv Diş Hek Fak Derg 1990; 24 (3): 139-47.
2. Smith Ul\ Powers .İM, Ladd D. MedifinicJ properties of new denture resins polymerized by visible: li«ht, heal and microwave energy. İni i Prostlındom 1992; 3(4): 315-20.
3. Çahkkocaoğlu S. Tarn Protezler. Istanbul. ! 998: 532-562.4. De Clerk. JP. Microwawe polymerization of acrylic resins used in dental prostheses. .1 Prosthct Dent.
1987-57 (5): 650-4.
5. Dixon DL, Ekstrand KG, Breeding LC The transverse strengths of three denture base resins. J Prosthct Dent 1991; 66 (4): 510-3.
6. Füriy SA, and Ellis B, The effect of processing temperatures on the exotherm, porosity and properties uf acrylic denture base. Bnt Dent J 1979: 147 (S): 209-12.
7. Gay WD, and King GH. An evaluation of the cure of acrylic resin by three methods. J Prosthel Dent 1979; 42 (4): 437-40.
8. Phillips RW, Skinner's Science of Dental Materials. 7 in cd WB. Saunders Company, Philadelphia, London, Toronto, 1991:195-197.
9.
Zaimoğl
u A, Can G, Ersoy F,. Aksu 1,. Diş Hekimliğinde Maddeler Bilgisi. Ankara, 1993: 183-94. 208-9.
10. Sanders JL, Levin H, Reitî PV. Porosity in denture acrylic resins cured by microwave energy. Quintessence Int. 1987: 18 (8): 453-6.
1 I. Wolfoaardt JF, Clcaton- Jones P, Fatti P. The occurence of porosity in a heat cured poly{meLhyl mctacrylaLe) denture base resin. J Prosthct Dent 1986; 55 0): 393^00.
12. Keller JC, L.autcnschlager KP. Porosity reduction and its associated effect on the diametral tensile strength of activated acrylic resins. J Prosthct Dent 1985; 53 (3): 374-9.
13. Winkler LR. Complete Denture IVosthodontics, Littleton, Massachusetts: PSC l*ubhsliing Co İne, 198S: 329.
14. Bafile M, Grascr GN, Myers ML, Li HKH. Porosity of denture resin cured by nnerovawe energy. J Prosthct Dent 1991; 66 (2): 269-74.
15. The Academy of Denture Prosthetics. The final report of the workshop on the clinical rcquimenls of ideal denture base materials. J Prosthct Dent 1968; 20 (!): 101¬105.
16. Davenport JC. The oral distribution of Candida in denture stomatitis. KritDentJ 1970; 129(4}: 151-6.
17.
Keski
n Y, Afcoren AC. Farklı yöntemlerle polimerize edilen akriiik rezinlerin porozite açısından karşılaştırılması. Ankara Üniv Diş Hek Pak Derg 1998; 25 (3): 299-305.
18.
Karta
l M. Bilimsel Araştırmada Hipotez Testleri. Şafak Yayınevi, Erzurum, 1998: 210.
19. Anderson JN. Applied Dental Materials. 5 th cd. Blackwcll Scientific Publication .London, 1976: 200-2.
20- Combe EC Notes on Dental Materials. Edinburgh: Churchill/ Livingstone Inc, 1986; 50-52, 258-263.
21. Firtell DN, Harman LL. Porosity in boilablc acrylic resin. J Prosthct Dent 1983; 49 (I): 1 33-134.
22. .lagger RG, Htıggct R. The effect of cross linking on Idcntation resistance, creep and recovery of an acrylic resin denture base material. J Dent 1975; 3(1): 15-18¬23. Harrison A, Hugget R. Effect of the curing cycle
on residual monomer levels of acrylic resin denture base polymers. .1 Dent 1992; 20 (6): 370-374.

Thank you for copying data from http://www.arastirmax.com