BAZI GELENEKSEL İÇECEKLERİN MİKROHİBRİT KOMPOZİT REZİNDE MEYDANA GETİRDİĞİ RENK DEĞİŞİKLİKLERİNİN İNCELENMESİ

THE COLOR CHANGE OF A MICROHYBRID COMPOSITE IMMERSION IN DIFFERENT TRADITIONAL TURKISH DRINKS

Journal Name:

  • Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 2012

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
Purpose: The purpose of this study was to evaluate the color change of a microhybrid resin composite immersed in traditional Turkish beverages. Materials and Methods: A microhybrid resin composite was included within the study (Filtek Z250). Fifty resin composite specimens (6mm diameter, 2mm thickness) were prepared. Baseline color measurements were taken with a spectrophotometer and the specimens were immersed in four staining solutions (turnip juice, Turkish coffee, cranberry juice and black mulberry juice) and distilled water. (n=10) After a 24-hour, 72- hour and 1-week of immersion, the color values of each specimen were re-measured with a spectrophotometer and the color change values (ΔEab*) were calculated. Statistical analyses were evaluated by means of one-way ANOVA and post- hoc Tukey HSD test. (p=0,05). Results: The color change was higher than ΔEab*≥ 3.3 for all staining solutions except for in distilled water after 1-week of immersion. Among the all drinks tested, turnip juice showed the highest ΔEab* value for the composite samples. (p<0,05). Conclusion: Within the limitations of this study we can say that the resin composite tested was susceptible to staining by commonly used drinks in the Turkish populations, especially turnip juice and Turkish coffee.
Bookmark/Search this post with
Abstract (Original Language): 
Amaç: Bu çalışmanın amacı geleneksel Türk içecekleri içerisinde bekletilen bir mikrohibrit rezin kompozitin renk değişimini incelemektir. Gereç ve Yöntem: Çalışmamızda bir mikrohibrit rezin kompozit (Filtek Z250) kullanılmıştır. Toplam elli adet rezin kompozit örneği (6mm çapında 2 mm kalınlığında) hazırlanmıştır. Spektrofotometre ile yapılan ilk ölçümlerin ardından hazırlanan örnekler dört farklı içeceğe (şalgam suyu, Türk kahvesi, kızılcık suyu ve karadut suyu) ve saf suya konulmuştur. Her grup için 10 örnek hazırlanmış ve 24 saat, 72 saat ve 1 hafta sonunda her bir örneğin renk parametreleri spektrofotometre ile tekrar ölçülerek kaydedilmiştir. Örneklerin renk değişim değerleri (ΔEab*) hesaplanmıştır. İstatistiksel analizler tek yönlü varyans analizi (one-way ANOVA) ve Tukey HSD çoklu karşılaştırma testi ile yapılmıştır. (p=0,05). Bulgular: Saf su dışındaki diğer içeceklerde bekletilen örneklerde renk değişim miktarları ΔEab*≥ 3,3’den daha fazla bulunmuştur. Tüm içecekler içerisinde en çok renk değişikliğinin, şalgam suyunda bekletilen kompozit örneklerinde olduğu belirlenmiştir (p<0,05). Sonuç: Bu çalışmanın sınırları içerisinde, kullanılan rezin kompozitin özellikle şalgam suyu ve Türk kahvesi olmak üzere geleneksel Türk içecekleri karşısında renk değişimine karşı dayanıksız olduğu ortaya konmuştur.
FULL TEXT (PDF): 
PDF icon arastirmax-bazi-geleneksel-iceceklerin-mikrohibrit-kompozit-rezinde-meydana-getirdigi-renk-degisikliklerinin-incelenmesi.pdf
  • 2
115-120
  • Turkish

REFERENCES

References: 

1. Ülker M, Ertaş H, Ertaş E, Şişman Y. Erciyes
Üniversitesi Diş Hekimliği Fakültesi’nde
restorasyon yapılma ve yenilenme nedenleri. SÜ
Dişhek Fak Der 2008;(17):12-15.
2. Dogan A, Yuzugullu B. Renk seçiminde güncel
teknolojik gelişmeler. Atatürk Üniv. Diş Hek. Fak.
Derg. 2011(Suppl. 4):65-73.
3. Dayangaç GB. Kompozit rezin restorasyonlar.
Güneş Kitapevi Ltd. Şti., Ankara, 2000:1-20.
4. Fondriest J. Shade: Matching in Restorative
Dentistry. The Science and Strategies. Int J
periodontics Restorative Dent2003;23:467-479.
5. Joiner A. Tooth colour: a review of the literature.
J Dent 2004;32 (Suppl 1):3-12.
6. Turkun LS, Turkun M. Effect of bleaching and
repolishing procedures on coffee and tea stain
removal from three anterior composite veneering
materials. J Esthet Restor Dent 2004;16(5):290-
301.
7. Sarı ME, Koyutürk AE, Çankaya S. Çocukların
sıklıkla tükettiği yiyecek ve içeceklerin farklı dolgu
materyallerinin rengine etkisi. Turkiye Klinikleri J
Dental Sci 2010;117(2):140-146.
8. 8 Lee YK, Lim BS, Kim CW. Difference in
polymerization color changes of dental resin
composites by the measuring aperture size. J
Biomed Mater Res B Appl Biomater
2003;66(1):373-378
Atatürk Üniv. Diş Hek. Fak. Derg. BARUTCİGİL, HARORLI,
J Dent Fac Atatürk Uni SEVEN
Cilt:22, Sayı: 2, Yıl: 2012, Sayfa: 114-119
119
9. O'Brien WJ, Groh CL, Boenke KM. A new, smallcolor-
difference equation for dental shades. J
Dent Res 1990;69(11):1762-1764.
10. Seghi RR, Johnston WM, O'Brien WJ.
Performance assessment of colorimetric devices
on dental porcelains. J Dent Res
1989;68(12):1755-1759.
11. Ahmad I. Protocols for Predictable Aesthetic
Dental Restorations. Oxford, UK: Blackwell
Munksgaard; 2006.
12. Fay RM, Walker CS, Powers JM. Color stability of
hybrid ionomers after immersion in stains. Am J
Dent1998;11(2):71-72.
13. Abu-Bakr N, Han L, Okamoto A, Iwaku M. Color
stability of compomer after immersion in various
media. J Esthet Dent 2000;12(5):258-263.
14. Luiz BKM, Amboni RDMC, Prates LHM, Bertolino
JR, Pires ATN. Influence of drinks on resin
composite: Evaluation of degree of cure and
color change parameters. Polym Test
2007;26(4):438-444.
15. Arikawa H, Takahashi H, Kanie T, Ban S. Effect
of various visible light photoinitiators on the
polymerization and color of light-activated resins.
Dent Mater J 2009;28(4):454-460.
16. Bagheri R, Burrow MF, Tyas M. Influence of
food-simulating solutions and surface finish on
susceptibility to staining of aesthetic restorative
materials. J Dent 2005;33(5):389-398.
17. Mair LH. Staining of in vivo subsurface
degradation in dental composites with silver
nitrate. J Dent Res 1991;70(3):215-220.
18. Reis AF, Giannini M, Lovadino JR, Ambrosano
GM. Effects of various finishing systems on the
surface roughness and staining susceptibility of
packable composite resins. Dent Mater
2003;19(1):12-18.
19. Douglas WH, Craig RG. Resistance to extrinsic
strains by hydrophobic composite resin systems.
J Dent Res 1982;61(1):41-43.
20. Khokhar ZA, Razzoog ME, Yaman P. Color
stability of restorative resins. Quintessence Int
1991;22(9):733-737.
21. Pearson GJ, Longman CM. Water sorption and
solubility of resin-based materials following
inadequate polymerization by a visible-light
curing system. J Oral Rehabil 1989;16(1):57-61.
22. Kalachandra S, Turner DT. Water sorption of
polymethacrylate networks: bis-GMA/TEGDM
copolymers. J Biomed Mater Res B Appl Biomater
1987; 21(3):329-338.
23. Lu H, Roeder LB, Lei L, Powers JM. Effect of
surface roughness on stain resistance of dental
resin composites. J Esthet Restor Dent 2005;
17(2): 102-108; discussion 09.
24. Ertas E, Guler AU, Yucel AC, Koprulu H, Guler E.
Color stability of resin composites after
immersion in different drinks. Dent Mater J 2006;
25(2): 371-376.
25. Turssi CP, Ferracane JL, Serra MC. Abrasive wear
of resin composites as related to finishing and
polishing procedures. Dent Mater 2005;21(7):
641-648.
26. Omata Y, Uno S, Nakaoki Y, Tanaka T, Sano H,
Yoshida S, et al. Staining of hybrid composites
with coffee, oolong tea, or red wine. Dent Mater
J 2006;25(1):125-131.
27. Patel SB, Gordan VV, Barrett AA, Shen C. The
effect of surface finishing and storage solutions
on the color stability of resin-based composites. J
Am Dent Assoc 2004;135(5):587-594.
28. Doray PG, Eldiwany MS, Powers JM. Effect of
resin surface sealers on improvement of stain
resistance for a composite provisional material. J
Esthet Restor Dent 2003;15(4):244-249;
discussion 49-50.

Thank you for copying data from http://www.arastirmax.com