A360 alüminyum alaşımına Mg ilavesinin malzeme yapısındaki sertlik dağılmına etkisinin incelenmesi

Journal Name:

  • Dicle Üniversitesi Mühendislik Fakültesi Mühendislik Dergisi

Publication Year:

  • 2011

Key Words:

Keywords (Original Language):

Author NameUniversity of Author
Abstract (2. Language): 
Structural and mechanical properties of Al-Si-Mg cast alloys depend on Į-Al phase, eutectic-Si particles, iron-rich intermetallics and especially Mg2Si phase. These can be changed with various ways such as chemical modification, Mg addition. In this study, commercial A360 hypoeutectic Al-Si-Mg alloy with addition of 0.2% - 0.8% Mg, affecting of alteration in microstructure and hardness, was investigated. The alloys in different compositions were produced by gravity casting method. And the casting temperature was set at 650°C. Microstructures were examined and intermetallic compounds were shown in detail. The observations were carried out in MEIJI ML 7100 optical microscopy. According to microstructural results; Mg2Si phase, AlFeMnSi phase and eutectic phase occurred in the structure. In addition, the effect of Mg supplementation in rates of 0% - 0.2% - 0.4% - 0.8% have also examined. The hardness was measured in Brinell macro hardness tester. The results showed that the Mg addition increased the hardness. Micro hardness of intermetallic phases was measured. Thus, the effect of hardness of the phases may be identified. Micro hardness measurements were carried out under load 10 gf in Vickers micro hardness tester. As a result of this work, it was found that Mg2Si phase increased the hardness values. According to the specific hardness values, the hard phase was Mg2Si intermetallic phase which consist of Mg addition. Intermetallics and eutectic Si phase fined with increasing Mg addition. The addition of Mg increased the hardness of the material overall.
Bookmark/Search this post with
Abstract (Original Language): 
Al-Si-Mg döküm alaúÕmlarÕnÕn yapÕsal ve mekanik özellikleri Į-Al fazÕna, ötektik Si partiküllerine, demirce zengin intermetaliklere ve özellikle Mg2Si fazÕna ba÷lÕdÕr. Bu yapÕlar kimyasal modifikasyon, Mg ilavesi gibi çeúitli yollarla de÷iútirilebilmektedir. Bu çalÕúmada, özellikle otomotiv sanayinde geniú yer bulan A360 alaúÕmÕna %0.2 - 0.8 oranlarÕndaki Mg ilavesi ile mikroyapÕdaki ve sertlikteki de÷iúimin etkileri araútÕrÕlmÕútÕr. AraútÕrmalar esnasÕnda farklÕ oranlarda Mg ilave edilmiú mikroyapÕlar incelenmiú ve intermetalik bileúikler detaylÕ olarak gösterilmiútir. MikroyapÕ sonuçlarÕ incelendi÷inde Mg2Si fazÕnÕn oluútu÷u gözlenmiútir. AyrÕca %0 - %0.2 - 0.4 - 0.8 oranlarÕndaki Mg ilavesinin sertli÷e etkisi de incelenmiútir. Sonuçlar, Mg ilavesine ba÷lÕ olarak sertlikte artÕú meydana getirdi÷ini göstermiútir. Oluúan intermetalik fazlarÕn sertli÷e etkisini tespit etmek amacÕyla intermetalik fazlarÕn mikrosertlikleri ölçülmüútür. Ölçümler Vickers mikrosertlik cihazÕnda 10gf yük altÕnda yapÕlmÕútÕr.
FULL TEXT (PDF): 
PDF icon arastrmx_31878_2_pp_87-93.pdf
  • 2
87-93
  • Turkish

REFERENCES

References: 

Metals Handbook (1988). Casting, ASM, Ninth
Edition, Volume 15.
Terjesen, G., (2003). Effect of elevated temperature
on tensile properties and fracture toughness of an
AlSi10Mg alloy, Aluminium, 79, 9, 748-754.
Shah, B.K., Kumar S.D. ve Dwivedi D.K., (2003).
Aging temperature and abrasive wear behaviour
of cast Al–(4%, 12%, 20%)Si–0.3% Mg alloys,
Materials and Design, 28, 6, 1968-1974.
ayrÕk Si partikülü
Į-Al
AlFeSi
AlFeMnSi
Mg2
Si 93
Esmaeili S., Lloyd D.J. ve Poole W.J., (2003).
Modeling of precipitation hardening for the
naturally aged Al-Mg-Si-Cu alloy AA6111, Acta
Materialia, 51, 12, 3467-3481.
Esmaeili S. ve Lloyd D.J., (2005). Modeling of
precipitation hardening in pre-aged AlMgSi(Cu)
alloys, Acta Materialia, 53, 20, 5257-5271.
Wang Q.G. ve Davidson C.J., (2001). Solidification
and precipitation behaviour of Al-Si-Mg casting
alloys, Journal of Materials Science, 36, 3, 739-
750.
Tavitas-Medrano F.J., Gruzleski J.E., Samuel F.H.,
Valtierra S. ve Doty H.W., (2008). Effect of Mg
and Sr-modification on the mechanical properties
of 319-type aluminum cast alloys subjected to
artificial aging, Materials Science and
Engineering A, 480, 1-2, 356-364.
Hwang J.Y., Doty H.W. ve Kaufman M.J., (2008).
The effects of Mn additions on the microstructure
and mechanical properties of Al–Si–Cu casting
alloys, Materials Science and Engineering A,
488, 1-2, 496-504.
Hekmat-Ardakan A. ve Ajersch F., (2010). Effect of
isothermal ageing on the semi-solid
microstructure of rheoprocessed and partially
remelted of A390 alloy with 10% Mg addition,
Materials Characterization, 61, 8, 778-785.
Raghavan V., (2007), Al-Mg-Si (AluminumMagnesium-Silicon), Journal of Phase Equilibria
and Diffusion, Phase Diagram Evaluations:
Section II, 28, 189-191.
Voncina M., Kores S., Mrvar P. ve Medved J.,
(2011). Effect of Ce on solidification and
mechanical properties of A360 alloy, Journal of
Alloys and Compounds, 509, 27, 7349-7355.
Chakrabarti D.J. ve Laughlin D.E., (2004). Phase
relations and precipitation in Al-Mg-Si alloys
with Cu additions, Progress in Materials Science,
49, 3-4, 398-341.
Sun Y. ve Ahlatci H., (2011). Mechanical and wear
behaviors of Al-12Si-XMg composites reinforced
with in situ Mg2
Si particles, Materals and
Design, 32, 5, 2983-2987.

Thank you for copying data from http://www.arastirmax.com