INVESTIGATION OF WEAR CHARACTERISTICS OF DISCS MANUFACTURED FROM 16MnCr5 UNDER SLIDING-ROLLING CONDITIONS
Journal Name:
- Dokuz Eylül Üniversitesi Mühendislik Fakültesi Fen ve Mühendislik Dergisi
Keywords (Original Language):
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
In this study, the wear behaviour of untreated and carburized discs manufactured from
16MnCr5 steel has been investigated under dry and lubricated sliding-rolling contact
conditions. Wear tests with various sliding- rolling ratios and under various loads were
carried out using a roller on roller test ring. It has been observed from the tests that wear has
become gradually so were in carburized discs by the increase in sliding-ratio. In addition, it
has been detected that carburized discs exhibited much lower wear than untreated discs.
Another observation was that carburization proved to be an effective method for the
improvement of wear resistant. Under lubricated sliding-rolling contact conditions, it has
determined that wear was much lower compared to dry sliding-rolling contact conditions.
Bookmark/Search this post with
Abstract (Original Language):
Bu çalışmada 16MnCr5 çelikten yapılmış yüzeyi işlem görmemiş ve yüzeyi sementasyonla
sertleştirilmiş disklerin, kuru ve yağlı kayma-yuvarlanma koşulları altında aşınma davranışı
araştırılmıştır. Aşınma deneyleri farklı kayma-yuvarlanma oranlarıyla ve farklı yükler altında
disk/disk test cihazıyla yapılmıştır. Yapılan deneyler sonucunda yüzeyi sertleştirilmiş
disklerde kayma oranının artmasıyla aşınmanın kademeli olarak şiddetlendiği görülmüştür.
Ayrıca yüzeyi sertleştirilmiş disklerin sertleştirilmemiş disklere göre çok daha az aşındığı
gözlenmiştir. Yüzey sertleştirmenin aşınma direncini arttırmada etkili bir yöntem olduğu
görülmüştür. Yağlı kayma-yuvarlanma temas koşullarında ise, kuru kayma-yuvarlanma
koşullarına göre aşınmanın çok daha az olduğu saptanmıştır.