PERLİT AGREGASININ PESİMUM REAKTİF AGREGA ORANININ FARKLI YÖNTEMLERLE İNCELENMESİ

RESEARCH OF PESIMUM REACTIVE AGGREGATE RATIO OF THE PERLITE AGGREGATE WITH DIFFERENT METHODS

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2010

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, it is purposed to determine of reactive aggregate ratio of the perlite aggregate for given up the highest length change. For this purpose, properties of relate to alkali-silica reaction (ASR) of the perlite aggregate determined with non-reactive limestone aggregate. For the determination of ASR, according to ASTM C 1260 accelerated mortar bar method, for microstructure; Scanning Electron Microscope (SEM) and Energy Dispersive X-ray (EDX) analysis were carried out on the samples which are perlite, limestone and used both of them. Mixtures were prepared by weight at 0, 10, 20, 30, 40, 50 and 100% ratios with usage of perlite aggregate that obtained from Ankara Çubuk region instead of limestone aggregate that obtained from Ankara Hasanoğlan region. 21 pieces of mortar bars were produced for 7 different mixtures. The length change values of the samples were measured on the 3, 7, 10, 14, 21 and 28-day according to the accelerated mortar bar method. Morphology and chemical composition of highest length changed samples were determined with SEM and EDX. Increase of fracture density and Ca ratio was observed in parallel with the increase of length change. According to average of 14 days length change, 40% perlite aggregated samples underwent highest length change and these samples were determined as pesimum reactive aggregate ratio of the perlite aggregate.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, perlit agregasının en fazla boy değişimini veren reaktif agrega oranının tespiti amaçlanmıştır. Bu amaçla farklı oranlardaki perlit agregasının reaktif olmayan kireçtaşı agregası ile alkali-silika reaksiyonu (ASR)’na ilişkin özellikleri belirlenmektedir. Perlit, kireçtaşı ve her ikisinin birlikte kullanıldığı örnekler üzerinde ASR’nu belirlemek için ASTM C 1260’a göre hızlandırılmış harç çubuk deneyi, Scanning Electron Microscope (SEM) ve Energy Dispersive X-ray (EDX) ile mikro yapı incelemesi yapılmıştır. Karışımlar, Ankara Hasanoğlan bölgesinden temin edilen kireçtaşı agregasına Ankara Çubuk bölgesinden temin edilen perlit agregasının ağırlıkça %0, 10, 20, 30, 40, 50 ve 100 oranlarında yer değiştirilmesi ile hazırlanmıştır. 7 ayrı karışım için toplam 21 adet harç çubuğu üretilmiştir. Hızlandırılmış harç çubuk metoduna göre 3, 7, 10, 14, 21 ve 28 günlük boy değişim değerleri ölçülmüştür. En fazla boy değişimi veren örneklerin morfolojisi ve kimyasal kompozisyonu SEM ve EDX ile yapılmıştır. Boy değişiminin artması ile çatlak yoğunluğu ve Ca oranının arttığı gözlenmiştir. 14 günlük boy değişim ortalamalarına göre, içerisinde %40 oranında perlit agregası içeren örnekler en fazla boy değişimine uğramış ve perlit agregasının pesimum reaktif agrega oranı olarak belirlenmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-perlit-agregasinin-pesimum-reaktif-agrega-oraninin-farkli-yontemlerle-incelenmesi.pdf
  • 4
839
846
  • Turkish

REFERENCES

References: 

1. Struble, L.J., Diamond, S. “Swelling Properties of
Synthetic Alkali-Silica Gel”, Journal of the
American Ceramic Society, 64(11); 611-655
1981.
2. Swamy, R.N., “The Alkali-Silica Reaction in
Concrete”, Thomson Litho Ltd., Scotland, UK,
1990.
3. Ramachandran, V.S., “Concrete Admixture
Handbook”, Science and Technology, Second
Edition, USA, 1995.
4. Bektaş, F., Turanlı, L., Topal, T., Göncüoğlu,
M.C., “Alkali Reactivity of Mortars Containing
Chert and Incorporating Moderate-Calcium Fly
Ash”, Cement and Concrete Research, 34,
2209-2214, 2004.
5. Binal, A., “Pesimum Reaktif Agrega İçeriğinin
Alkali-Silika Reaksiyonuna Etkisinin Deneysel
Yöntemlerle Araştırılması”, İstanbul Üniv.
Müh. Fak. Yerbilimleri Dergisi, 17(2); 119-
128, 2004.
6. Turanlı, L., Mesut, A., Uzal, B., “Erzincan
Mollaköy Ham Perlit Agregasının ve Perlit
Tozunun Taşıyıcı Hafif Beton Üretiminde
Kullanılabilirliğinin Araştırılması”, Proje Kod
No: 2005-03-03-2-77, Ankara, 2006.
Analiz 1. 35 büyütmedeki EDX analizleri (The EDX analysis of 35 times enlarged)
H. S. Gökçe ve O. Şimşek Perlit Agregasının Pesimum Reaktif Agrega Oranının Farklı Yöntemlerle İncelenmesi
846 Gazi Üniv. Müh. Mim. Fak. Der. Cilt 25, No 4, 2010
7. ASTM C-1260-07, “Standard Test Method for
Potential Alkali Reactivity of Aggregates
(Mortar-Bar Method)”, Annual Book of ASTM
Standards, Concrete and Mineral Aggregates,
Philadelphia, PA, USA, American Society for
Testing and Materials, 2007.
8. Gökçe, H.S., Durmuş, G. ve Şimşek, O.,
“Alternatif Karışım Oranlarında Üretilen Doğal
Perlit Agregalı Hafif Betonların Su/Çimento
Üzerindeki Etkileri”, Politeknik Dergisi, 13(1);
55-63, 2010.
9. TS EN 1097-6, “Agregaların Mekanik ve Fiziksel
Özellikleri İçin Deneyler Bölüm 6: Özgül Ağırlık
ve Su Emme Oranı Tayini”, Türk Standartları
Enstitüsü, Ankara, 2002.
10. TS EN 197-1, “Çimento - Bölüm 1: Genel
Çimentolar - Bileşim, Özellikler ve Uygunluk
Kriterleri”, Türk Standartları Enstitüsü,
Ankara, 2002.
11. Gökçe, H.S., Taban, S., Şimşek, O., “Zeolitik Tüf
İkamesinin Farklı Agregalar Üzerinde Alkali-
Silika Reaksiyonu Etkilerinin Belirlenmesi”,
Gazi Üniv. Müh. Mim. Fak. Der., 25(4), 803-
809,2010.
12. Bektaş, F., Turanlı, L., Monterio, P.J.M., “Use of
Perlite Powder to Suppress the Alkali-Silica
Reaction”, Cement and Concrete Research, 35,
2014-2017, 2005.
13. Gökçe, H.S., Cemalgil, S. “Alkali-Silika
Reaksiyonunun Kontrol Altına Alınmasında
Endüstriyel Atıkların ve Doğal Kaynakların
Değerlendirilmesi”, Uluslararası Sürdürülebilir
Yapılar Sempozyumu (ISBS), Ankara, Türkiye,
30-34, 2010.
14. Demir, İ., “Alkali-Silika Reaksiyonu Etkisinde
Kalan Aynı Oranlardaki Silis Dumanı ve Uçucu
Kül İçeren Harçların Mekanik Özellikleri” Gazi
Üniv. Müh. Mim. Fak. Der., 25(4), 749-758,
2010.

Thank you for copying data from http://www.arastirmax.com