PLAZMA NİTRÜRLENMİŞ X40CRMOV5-1 YÜKSEK ALAŞIMLI ÇELİĞİN AŞINMA DAVRANIŞININ İNCELENMESİ

INVESTIGATION OF WEAR BEHAVIOUR OF PLASMA NITRIDED X40CrMoV5-1 HIGH ALLOY STEEL

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2013

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
X40CrMoV5-1 high-alloyed steel was plasma nitrided for different treatment times (3h, 5h and 7h) and temperatures (450, 500 and 550 oC) under at a constant gas mixture (75% H2+25% N2). The plasma nitriding properties of X40CrMoV5-1 high-alloyed steel have been examined by evaluating phase composition, hardness profile, compound layer thickness, case depth and wear strength. It was found that double layers (compound and diffusion) formed on the surface of the samples and increasing of treatment time and temperature has increased the layers thicknesses. It was found that plasma nitriding improves the wear strength, which depends on thicknesses and hardness of the diffusion layer, but the compound layer reduces the wear resistance by breaking off and forming abrasive particles because of the high hardness.
Bookmark/Search this post with
Abstract (Original Language): 
X40CrMoV5-1 yüksek alaşımlı çeliği farklı işlem süreleri (3h, 5h ve 7h), farklı işlem sıcaklıkları (450, 500 ve 550 oC) ve sabit gaz karışımı (%75 H2 + %25 N2) altında plazma nitrürlenmiştir. Plazma nitrürlenmiş X40CrMoV5-1 yüksek alaşımlı çeliğin plazma nitrürleme özellikleri faz bileşimi, sertlik profili, bileşik tabaka kalınlığı, difüzyon tabakasının derinliği ve aşınma direnci ele alınarak incelenmiştir. İncelemeler sonucunda X40CrMoV5-1 yüksek alaşımlı çeliğin yüzeyinde ikili nitrür tabakasının oluştuğu ve bu tabakaların (hem beyaz ve hem de difüzyon tabakasının) kalınlıklarının sıcaklık ve zamanın artışına bağlı olarak arttığı tespit edilmiştir. Plazma nitrürleme yüzeyde oluşan difüzyon tabakasının kalınlıklarına ve sertliklerine bağlı olarak aşınma direncini arttırdığı, fakat bileşik tabakanın yüksek sertliğinden dolayı kırılarak abrasif aşınmaya neden olarak aşınma direncini azalttığı tespit edilmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-plazma-nitrurlenmis-x40crmov5-1-yuksek-alasimli-celigin-asinma-davranisinin-incelenmesi.pdf
  • 1
7
14
  • Turkish

REFERENCES

References: 

1. Biermann, D., Weinert, K., Jansen, T., Noyen, M.,
“Profile and shape grinding of high alloyed
steels”, International Journal of Microstructure
and Materials Properties, Vol. 3, No 2/3, 413 –
423, 2008.
2. Novak, P., Vojtech, D., Serak, J., “Pulsed-plasma
nitriding of a niobium–alloyed PM tool steel”,
Materials Science and Engineering, A 393, 286–
293, 2005.
3. Schaaff, P., “Laser Nitriding of Metals”, Progress
in Materials Science, 47, 1-161, 2002.
4. Rajasekaran, B., Mauer, G., Vaßen, R., Röttger,
A., Weber, S., Theisen, W., “Thick tool steel
coatings using HVOF spraying for wear resistance
applications”, Surface & Coatings Technology,
205, 2449–2454, 2010.
5. Neto, V.F., Vaz, R., Oliveira, M.S.A., Grácio, J.,
“CVD diamond-coated steel inserts for
thermoplastic mould tools - Characterization and
preliminary performance evaluation”, Journal of
Materials Processing Technology, Vol. 209,
Issue 2, 1085-1091, 2009.
6. Sokovi, M., Bahor, M., “On the inter-relationships
of some machinability parameters in finish
machining with cermet TiN (PVD) coated tools”,
Journal of Materials Processing Technology,
Vol. 78, Issues 1-3, 163-170, 1998.
7. Kowacs, W., Russell, W., “An Introduction To Ion
Nitriding, What Is It?, Why Is It Used?, Ion
Nitriding”, Proceeding of an International
Conference on Ion Nitriding, Cleveland/Ohio,
9–17, 1986.
8. Karamış, M. B. “İyon Nitrürleme Esasları ve
Çeliklere Uygulanması”, 4.Ulusal Makina
Tasarım ve İmalat Kongresi, ODTÜ, Ankara,
1990.
9. Duh, J. G., Lin, S. C. 1993. Nitriding Behaviour in
Fe-Al-Mn-Cr-C Alloys at 1000-1100 Degree C,
Journal of Materials Science, 28 (22), 5975-
5980.
10. Karamış, M. B. “An investigation of the properties
and wear behavior of plasma-nitrided hot-working
steel (H13), Wear, 150, 331-342, 1991.
11. Karadeniz, S., Plazma Tekniği, TMMOB
yayınları, Ankara, Türkiye, 1990.
12. Karakan, M., Alsaran, A., Çelik, A., “Effects of
Various Gas Mixtures on Plasma Nitriding
Behavior of AISI 5140 Steel”, Materials
Characterization, 49, 241– 246, 2003.
13. M. Van Stappen, B. Malliet, L. Stals, L. De
Schepper, J.R. Roos, J.P. Celis “Characterization
of TiN coatings deposited on plasma nitrided tool
steel surfaces” Materials Science and Engineering:
A, 140, 554-562, 1991
14. Baycık H., “İyon Nitrürleme Ve Çeliğin
Özelliklerine Etkisi” Pamukkale Üniversitesi
Mühendislik Fakültesi Mühendislik Bilimleri
Dergisi, 8 (1), 19-25, 2002.
15. Karaoğlu S., Karadeniz S., Karaoğlu Ç., “Plazma
Nitrürlenmiş Az Alaşımlı Bir Çeliğin Aşınma
Davranışının İncelenmesi” Deü Mühendislik
Fakültesi Fen Ve Mühendislik Dergisi, 3 (3),
85-92, Ekim 2001.
16. Kahraman F., Karadeniz S., “Characterization and
Wear Behavior of Plasma Nitrided Nickel Based
Dental Alloy” Plasma Chemistry and Plasma
Processing, 31, 595–604, 2011.
17. Polat Ş., Atapek Ş. H., Topaç H., “Gaz Nitrasyon
ile Yüzeyleri Sertleştirilmiş AISI 4140 ve DIN
1.2344 Çeliklerinde Mikroyapısal
Karakterizasyon” 6th International Advanced
Technologies Symposium (IATS’11), Elazığ, 16-
18 May 2011.

Thank you for copying data from http://www.arastirmax.com