ÇİFT FAZLI ÇELİKLERDE MARTENZİT MORFOLOJİSİNİN STATİK DEFORMASYON YAŞLANMA DAVRANIŞI ÜZERİNE ETKİSİ

THE EFFECT OF MARTENSİTE MORPHOLOGY ON STATIC STRAIN AGEING BEHAVIOUR OF DUAL PHASE STEELS

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2013

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, strain ageing behaviour of dual phase steel with different martensite morphology was investigated. Three different types (Intercritical annealing, intermediate quenching and step quenching) of heat treatment was applied in the critical temperature (775 oC). Ageing experiments after 4 % prestrain were carried out at 180 oC for different times ranging from 10 to 160 min. The microstructure after different heat treatments applied to the work pieces with the network, fiber, and the bulky martesite morphologies have been identified. It was found that the martensite morphology has no effect on the trend of ΔY (an increase in strength due to strain ageing), YS and UTS at different ageing times for 180 oC. However, at a given ageing time for 180 oC ΔY, YS, UTS and hardness values of fibrous martensite are higher than network or bulky martensite.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, farklı martenzit morfolojisine sahip çift fazlı bir çeliğin statik deformasyon yaşlanma davranışı incelenmiştir. Kritik sıcaklık bölgesinde (775 oC) üç farklı ısıl işlem türü (kritik çift faz, ara su verme ve kademeli su verme) uygulanmıştır. Yaşlanma deneyleri % 4 öndeformasyondan sonra 180 oC’de 10 dakika ile 160 dakika arasında bekletilerek gerçekleştirilmiştir. Uygulanan farklı ısıl işlemler sonrası yapılan mikroyapı çalışmaları ile ağ, fiber ve kütlesel martezit morfolojileri tespit edilmiştir. Martenzit morfolojisinin 180 oC’de farklı yaşlanma sürelerinde ΔY (yaşlanmadan dolayı dayanımda artış), akma dayanımı ve maksimum çekme değerlerinin eğilimini etkilemediği bulunmuştur. Belirli yaşlanma sürelerinde fiber martenzit morfolojisine sahip numuneler, ağ veya kütlesel martenzit morfolojisine sahip numunelere göre daha yüksek ΔY, akma dayanımı, maksimum çekme ve sertlik değerleri göstermiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-cift-fazli-celiklerde-martenzit-morfolojisinin-statik-deformasyon-yaslanma-davranisi-uzerine-etkisi.pdf
  • 2
353
362
  • Turkish

REFERENCES

References: 

1. Akay K. S., Otomotiv Endüstrisinde
Kullanılan Çift Fazlı Çeliklerin Fiziksel
Özelliklerinin Araştırılması, Doktora Tezi,
Uludağ Üniversitesi, Fen Bilimleri Enstitüsü,
2005.
2. Dehghani K. ve Jonas J.J., “Dynamic Bake
Hardening of IF Steels”, Metallurgical and
Materials Trans., 31A., 1375-1384, 2000.
3. Properties and Selection: Irons, Steels and High-
Performance Alloys, ASM Metals Handbook,
10th Edition, Vol. 1, 1996.
4. Kadkhodapour J., Butz A. ve Ziaei Rad S.,
“Mechanisms of void formation during tensile
testing in a commercial, dual-phase steel, Acta
Materialia, 2575–2588 (59), 2011.
5. Rashid, M. S., “A Unique High-Strength Sheet
Steel with Superior Formability”, SAE Technical
Paper 760206, Design Engineering and Styling,
938-949, 1976.
6. Coldren, A.P. ve Tither, G., “Development of a
Mn-Si-Cr-Mo as-rolled Dual Phase Steel”
Journal of Metals, vol.30, pp.6-9, 1978.
7. Erdogan. M, ''The effect of austenite dispersion
on phase transformation in dual phase steels'',
Scripta Materialia, 501-506 (48), 2003.
8. Davies RG. The mechanical properties of zerocarbon
ferrite-plus-martensite structures,
Metallurgical Transactions A; 9A: 451-455,
1978.
9. Dzupon M., Parilak L., Kollarova M. ve Sınaıova
I., “Dual phase ferrite-martensitic steel micro
alloyed with V-Nb”, Metalurgija, 46, 15-20,
2007.
10. Mustafa Türkmen ve Süleyman Gündüz,
"Martensite morphology and strain aging
behaviours in intercritically treated low carbon
steel ", Ironmaking & Steelmaking, Volume 38,
Number 5, 346-352, 2011.
11. Gündüz S., “Static strain ageing behaviour of
dual phase steels”, Materials Science and
Engineering A, 486/1-2: 63-71, 2008.
12. Turkoglu S., Kayalı E. S. ve Çimenoğlu H.
“Çelik Saclarda Deformasyon Yaşlanma
Davranışının İncelenmesi”, IV. Demir-Çelik
Sempozyumu, Karabük, 1-3 Kasım 2007.
13. De A.K., De Blauwe K., Vandeputte S. ve De
Cooman B.C.,. “Effect of Dislocation Density on
the Low Temperature Aging Behavior of an Ultra
Low Carbon Bake Hardening”, Journal of
Alloys and Compounds, 310, 405-410, 2000.
14. Andrews, K.W., “Empirical Formulae for the
Calculation of Some Transformation
Temperatures J. Iron Steel Inst., 203, 721-726,
1965.
15. TSE, Metalik malzemeler için çekme deneyleri,
TS EN ISO 6892 Ocak/2010.
16. Das D. ve Chattopadhyay P.P.,, “Influence of
Martensite Morphology on the Work-hardening
Behaviour of Highstrength Ferrite-martensite
Dual-Phase steel”, J Mater Sci., 44, 2957-2965,
2009.
17. Speich, G.R. ve Miller, R.L., “Mechanical
Properties of Ferrite-Martensite Steels”, AIME,
New Orleans, 145-182, 19-21 Şubat 1979.
18. Gündüz S., Demir B. ve Kaçar R., “Effect of
Aging Temperature and Martensite by Volume
on Strain Aging Behaviour of Dual Phase Steel”,
Ironmaking and Steel Making, Vol 35, 63-68,
2008.
19. Speich GR., “Physical metallurgy of dual-phase
steels”, AIME, Warrendale, 3-45,1981.
20. Rocha R.O., Melo T.M.F., Pereloma E.V. ve
Santos D.B. “Microstructural Evolution at the
Initial Stages of Continuous Annealing of Cold
Rolled Dual-phase Steel”. Materials Science
and Engineering A, 391, 296-304, 2005.
21. Mohan R. ve Marshall C., “Cracking Instabilities
in a Low-carbon Steel Susceptible to Dynamic
Strain Aging” Acta Mater., Vol.46, 1933-1948,
1998.
22. Davies R.G., “The Deformation Behavior of a
Vanadium-strengthened Dual Phase Steel”,
Metal. Trans. A, 9A, 41-52, 1978.
23. Bayram A., Uğuz A. ve Ula M., “Effects of
Microstructure and Notches on the Mechanical
Properties of Dual-Phase Steels”, Mater.
Charact., 43, 259-269, 1999.
24. Koo J.Y. ve Thomas G., “Formable HSLA and
Dual Phase Steels”, TMS-AIME, Chicago,
Illinois, 40-58, 1977.
25. Ekrami A., “High Temperature Mechanical
Properties of Dual Phase Steels”, Materials
Letters, 59, 2070-2074, 2005.
26. Abdalla A.J., Hein L.R.O., Pereira M.S. ve
Hashimoto T.M., “Mechanical Behaviour of
Strain Aged Dual Phase Steels”, Mater. Sci.
Technol., Vol.15, 1167-1170, 1999.
27. Besterci, M., Sulleıovu, K. ve Kvackaj, T.,
“Fracture Micromechanisms of Copper
Nanomaterials Prepared by ECAP”, Kovove
Mater., 46, 309-311, 2008.

Thank you for copying data from http://www.arastirmax.com