TİTANYUM ALAŞIMININ BİYOMİMETİK YÖNTEMLE KALSİYUM FOSFAT KAPLANMASI

BIOMIMETIC CALCIUM PHOSPHATE COATING OF TITANIUM ALLOY

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2014

Key Words:

Keywords (Original Language):

Author NameUniversity of Author
Abstract (2. Language): 
In this study, hydroxyapatite (HA) was coated on Ti6Al4V, which is a widely used titanium alloy in biomedical applications, via biomimetic method. For the coating process, Ti6Al4V plates were immersed into simulated body fluid (SBF) with an ionic concentration of 1.5 times that of conventional SBF at 37°C. In 1.5×SBF, the entire surface was successfully coated with a calcium phosphate (CaP) layer after 2 weeks. The surface morphology of the coated plates was studied by field emission scanning electron microscopy (FE-SEM) and it was shown that the CaP coating was initiated in the form of half spheres and grew up continuously. The molecular structure of the coatings was determined by Fourier transform infrared spectroscopy (FTIR) and the coatings showed the IR spectrum of carbonated hydroxyapatite regardless of the soaking time.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, biyomedikal alanda sıklıkla kullanılan bir titanium alaşımı olan Ti6Al4V üzerine biyomimetik yöntemle hidroksiapatit kaplanmıştır. Kaplama işlemi için, Ti6Al4V plakalar, sıcaklığı 37°C’de tutulan ve normal iyonik konsantrasyonundan 1,5 kat daha yoğun olarak hazırlanan yapay vücut sıvısı (1,5×SBF) içerisinde bekletilmiştir. Tüm yüzeyin 2 hafta sonrasında kalsiyum fosfat tabakası ile kaplanmış olduğu gözlemlenmiştir. Kaplamanın yüzey morfolojisi alan emisyon taramalı elektron mikroskobu (FE-SEM) ile incelenmiş ve yüzeydeki kalsiyum fosfat birikiminin ilk olarak yarım kürecikler şeklinde başladığı ve 1,5×SBF içerisinde geçen süre arttıkça bu küreciklerin büyüdüğü görülmüştür. Kaplamanın moleküler yapısı Fourier dönüşümlü kızıl ötesi spektrometresi (FTIR) ile incelenmiştir. FTIR sonuçlarına göre, 1,5×SBF içerisinde bekleme süresi farklı olan plakaların üzerinde oluşan kaplamaların hepsi karbonatlı hidroksiapatit spektrumu vermiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-titanyum-alasiminin-biyomimetik-yontemle-kalsiyum-fosfat-kaplanmasi.pdf
  • 1
105
109
  • Turkish

REFERENCES

References: 

1. Mavis, B. ve Taş, A.C., “Dip-Coating of Calcium
Hydroxyapatite on Ti-6Al-4V Substrates”,
Journal of The American Ceramic Society, Cilt
83, No 4, 989–991, 2000.
2. Wang, D., Chen, C., He, T. ve Lei, T.,
“Hydroxyapatite Coating on Ti6Al4 V Alloy by a
Sol-Gel Method”, Journal of Materials Science:
Materials in Medicine, Cilt 19, 2281–2286, 2008.
3. Evis, Z., “Cu2+ Eklenmiş Hidroksiapatitlerin
Yüksek Sıcaklıkta Sinterlenmesi ve İç Yapı
İncelemesi”, Gazi Üniversitesi Mühendislik
Titanyum Alaşımının Biyomimetik Yöntemle Kalsiyum Fosfat Kaplanması B. Yılmaz ve ark.
Gazi Üniv. Müh. Mim. Fak. Der. Cilt 29, No 1, 2014 109
Mimarlık Fakültesi Dergisi, Cilt 24, No 4, 569–
573, 2009.
4. You, C., Oh, S. ve Kim, S., “Influences of Heating
Condition and Substrate-Surface Roughness on
the Characteristics of Sol-Gel-Derived
Hydroxyapatite Coatings”, Journal of Sol-Gel
Science and Technology, Cilt 21, 49–54, 2001.
5. Yang, Y., Kim, K.H. ve Ong, J.L., “A Review on
Calcium Phosphate Coatings Produced Using a
Sputtering Process–An Alternative to Plasma
Spraying”, Biomaterials, Cilt 26, 327–337, 2005.
6. Hoppe, A., Will, J., Detsch, R., Boccaccini, A.R.
ve Greil P., “Formation and In Vitro
Biocompatibility of Biomimetic Hydroxyapatite
Coatings on Chemically Treated Carbon
Substrates”, Journal of Biomedical Materials
Research Part A, Çevrimiçi Yayın: 7 Mayıs
2013. DOI: 10.1002/jbm.a.34685.
7. Cai, Q., Feng, Q., Liu, H. ve Yang, X.,
“Preparation of Biomimetic Hydroxyapatite by
Biomineralization and Calcination Using Poly(llactide)/
Gelatin Composite Fibrous Mat as
Template”, Journal of Biomedical Materials
Research Part B: Applied Biomaterials, Cilt
101B, No 1, 173–186, 2013.
8. Bigi, A., Boanini, E., Panzavolta, S. ve Roveri, N.,
“Biomimetic Growth of Hydroxyapatite on
Gelatin Films Doped with Sodium Polyacrylate”,
Biomacromolecules, Cilt 1, No 4, 752–756, 2000.
9. Nishiguchi, S., Kato, H., Fujita, H., Kim, H.M.,
Miyaji, F., Kokubo, T. ve Nakamura, T.,
“Enhancement of bone-bonding strengths of
titanium alloy implants by alkali and heat
treatments”, Journal of Biomedical Materials
Research, Cilt 48, 689–696,1999.
10. Kim., H.M., Miyaji, F. ve Kokubo, T. “Effect of
Heat Treatment on Apatite-Forming Ability of Ti
Metal Induced by Alkali Treatment”, Journal of
Materials Science: Materials in Medicine, Cilt
8, 341–347, 1997.
11. Silva, C.C., Pinheiro, A.G., Miranda, M.A.R.,
Góes, J.C. ve Sombra, A.S.B., “Structural
Properties of Hydroxyapatite Obtained by
Mechanosynthesis”, Solid State Sciences, Cilt 5,
553–558, 2003.
12. Suchanek, W.L., Shuk, P., Byrappa, K., Riman,
R.E., TenHuisen, K.S. ve Janas, VF.,
“Mechanochemical-Hydrothermal Synthesis of
Carbonated Apatite Powders at Room
Temperature”, Biomaterials, Cilt 23, No 3, 699–
710, 2002.

Thank you for copying data from http://www.arastirmax.com