LATERAL KONDANSASYON TEKNİĞİ SIRASINDA MEYDANA GELEN GERİLME DAĞILIMLARININ FOTOELASTİK YÖNTEMLE İNCELENMESİ

Journal Name:

  • İstanbul Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 1992

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
• İt is known thai the forces required for the condensation of gutta-percha during the lateral condensation technique may cause dentinal cracks of small magnitude and these may lead to fractures responsible of the failure in endodontic therapy. The purpose of this study is to examine the stress distribution during the application of lateral condensation technique by photoelastic models, and to determine the regions which are mostly subjected to the forces and which are the major causes of dentinal cracks and fractures. According to our results, the greatest amount of stress was observed in the lateral walls and the apical one-third portion of the canal. It was concluded that the stress characteristics varied with the applied force and the amount of stress increased with the amount offorce
Bookmark/Search this post with
Abstract (Original Language): 
Lateral kondansasyo n tekniği İle kök kanalım doldurma işlemi sırasında gütta-pcrkayı kondanse etmek için gerekli olan kuvvcüerin kanal duvarlarında ufak çatlaklara ve kırıklara yol açtığı bilinmektedir. Bu araştırma tekniğin uygulanışı sırasında meydana gelen gerilme dağılımlarını fotoelastik modellerden yararlanarak incelemek, kırık ve çatlaklara yol açan ve kuvvete en fazla maruz kalan bölgeleri tespit etmek amacıyla yapılmıştır. Elde edilen bulgulara göre en fazla gerilme apikal 1/3'te ve lateral duvarlarda oluşmaktadır. Gerilme karakteri uygulanan kuvvet ile değişmektedir. Kuvvet arttıkça gerilme artmaktadır.
FULL TEXT (PDF): 
PDF icon arastirmax-lateral-kondansasyon-teknigi-sirasinda-meydana-gelen-gerilme-dagilimlarinin-fotoelastik-yontemle-incelenmesi.pdf
  • 1
51
55
  • Turkish

REFERENCES

References: 

1.
Aköz
, A.Y.: Yüksekliği değişen kirişlerin hesabı için yeni bir metod ve deneysel gerçekleşme. İTÜ inşaat Fak. 1969 İstanbul.
2.
Aköz
, A.Y.: "Orlotropik Fotoelastisitc üzerine bir çalışma ve öneriler" Doçentlik Tezi, 1973.
3.
Aköz
, A.Y.: Deneysel mekanik. 5. Ulusal Mekanik Kongresi. 1987, Bursa.
4. Dally, J.W. and W.W. Riley: "Experimental Slrcss Analysis' McGraw Hill Inc.
Elasticity Photoclastic Constants of Unidirectional Composites" Exp. hitch. 1971; 5:345-346.
6. Frocht, M. M.: "Photoclasticity" Vol.1. New York: John Wiley & Sons Inc. 1941. Vol.2, 1948.
7. Gimlin, D.. Parr, C, Aquino-Ramirez, G.: A comparison of stresses produced by lateral and vertical condensation using engineering models. J.Endod. 1986,12: 235-241.
8. Harvey, T., White, J., Leeb, J.: Lateral condensation stress and root canals. J.Endod. 1981, 7: 151-155.
5. Dally, J.W. and Prabnakyan, R.: Photo-An isotropic-
9. llolcomb, J.. Pitts, D.. Nicholls. J.: Further investigation
Lateral Kondansasyon
Tekniği
Sırasında Meydana Gelen Gerilme Dağılımlarının Fotoelastik Yöntemle incelenmesi
55
• spreader loads required to cause vertical root fracture during la-condensation. J.Endod 1986,13: 277-284
10. Martin, II., Fischer, E.: Photoelastic stress comparison of a ami (Endotec) versus cold lateral condensation techniques. Oral
Surg Oral Med Oral Pathol. 1990; 70: 325 327.
11. Wiley, J. and Sons Inc. "Handbook of experimental stress analysis" 1950 829-880.

Thank you for copying data from http://www.arastirmax.com