YUMUŞAK ASTAR MADDELERİNİN MİKRODALGA ENERJİSİ İLE POLİMERİZASYONUNA AİT BİR ÖN ÇALIŞMA

POLYMERIZATION OF RESILIENT DENTURE LINERS WITH MICROWAVE ENERGY : A PILOT STUDY

Journal Name:

  • İstanbul Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 1993

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
The purpose of this study is to realize the poluneriza-tion ofrelisient denture liners with microwave energy and to compare their certain physical properties. A plasticized acrylic co-polymer (Super-soft) and a silicone rubber (Molloplast-B) were selected and their Shore-A hardness and tensile strength properties were tested. Conventional water bath curing was accepted as the control group. Statistical analysis was made by using ANOVA and the differences were evaluated with Dunnett's test. Wattage and exposure time of microwave polymerization were effective on the hardness and the tensile strength of the materials. It was concluded that resilient denture liners could be polymerized by microwave energy, but additional studies should be conducted on physical properties and clinical applications.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmanın amacı yumuşak astar maddelerinin mikrodalga enerjisi ile polimerizasyonlarmın gerçekleştirilmesi ve bazı fiziksel özelliklerinin karşılaştınlmasıdır. Bu amaçla akrilİk esaslı Super-soft ve silikon esaslı Mol-loplast-B yumuşak astar maddeleri kullanıldı. Konvansİ-yonel polimerizasyon yöntemi ile elde edilen örnekler kontrol grubu olarak kabul edildi ve mikrodalga fırınında polimerize edilen örneklerle sertlik ve çekme dayanımları açısından karşılaştırıldı. İstatistiksel değerlendirme için tek yönlü varyans analizi kullanıldı ve karşılaştırmalar Dunnett testi ile yapıldı. Farklı güçte ve süreler/deki mikrodalga enerjisi uygulamalarının materyallerin sertlikleri ve çekme dayanımları üzerinde etkili olduğu bulundu. Sonuç olarak yumuşak astar maddelerinin mikrodalga enerjisi ile polimerizasyonlan konvansiyonel yönteme göre çok daha kısa sürede yapılabilmektedir. Ancak fiziksel özelliklerin daha kapsamlı incelenmesinin ve klinik uygulamaların yapılmasının gerekli olduğu kanısına varılmıştır.
FULL TEXT (PDF): 
PDF icon arastirmax-yumusak-astar-maddelerinin-mikrodalga-enerjisi-ile-polimerizasyonuna-ait-bir-calisma.pdf
  • 1
1
7
  • Turkish

REFERENCES

References: 

1. Bates, J.F. Smith, D.C.: Evaluation of Indirect Resilient Liners for Dentures. JAmDentAssoc., 1965; 70: 344-353.
2. Chaing, B.K.P.: Polymers in the Service of Prosthetic Dentistry. J Bent., 1984; 12: 203-214.
3. Craig, R.G., Gibbons, P.: Properties of Resilient Denture Liners. J Am Dent Assoc., 1961; 63: 382-390.
4.
Çalıkkocaoğlu
, S.: Tam Protezler, I. Baskı, II. Cilt, Doyuran Matbaası. İstanbul, 1988: 111-121.
5. Dootz, E.R., Koran, A., Craig, R.G.: Properties of Soft Denture Liners as a Function of Accelerated Aging. J Dent. Res., 1991; 70: 476, Abstract No.1679.
6. Eick, J.D., Craig, R.G., Peyton, F.A.: Properties of Resilient Denture Liners in Simulated Mouth Conditions. J.Prost-het.Dent., 1962; 12: 1043-1052.
7. Graham, B.S., Jones, D.W., Sutow, E.J.: Clinical Implications of Resilient Denture Lining Material Research. Part I: Flexibility and Elasticity. J.Prosthet. Dent., 1989; 62: 421-428.
8. Hernandez, M., Andres, C: Polymerization of RTV Silicone Using Microwave Energy. J.Dent.Res., 1991; 70: 539, Abstract No.2184.
9. Kawano, F., Dootz, E.R., Koran, A., Craig, R.G.: Effect of Accelerated Aging on Bond Strength of Denture Liners. J.Dent.Res., 1992; 71: 629, Abstract No.911.
10. Kutay,
Ö.
: Akrilik ve Metal Protez Kaide Maddelerine Molİopİast-B'nin Tutunması. İ.Ü. Diş Hek. Fak. Protetik Diş, Tedavisi A.B. Dalı, Doktora Tezi, 1989.
11. Luebke, R.J., Schneider, R.L.: Microwave Oven Drying of Artificial Stone. J.Prosthet.Dent., 1985; 53: 261-265.
12. McKinstry, R.E., Browning, S.: Microwave Processing of Cleft Palate Orthopedic Expansion Devices. J.Prosthet. Dent. 1992; 67: 882-886.
13. McKinstry, R.E., Zini, I., Beery, Q.C.: Microwave-cured
Tracheostoma Ven\s. J J>rosthetJ)ent.> 1992; 67: 385-389.
14. Nelson, M.W., Kotwal, K.R., Sevedge, S.R.: Changes in Vertical Dimension of Occlusion in Conventional and Microwave Processing of Complete Dentures./. Prosthet. Dent., 1991; 65: 306-308.
15. Phillips, R.W.: Skinner's Science of Dental Materials. 9th ed., Philadelphia, WB. Saunders Company, 1991; 204-206.
16. Reitz, P.V., Sanders, J.L., Levin, B.: The Curing of Denture Acrylic Resins by Microwave energy. Physical Properties. Quintlnt., 1985; 8: 547-551.
17. Rohrer, M.D., Bulard, R.A.: Microwave Sterilization. JAm.DentAssoc, 1985; 110: 194-198.
18. Seals, Jr., R.R., Cortes, A.L., Funk, J.J.: Microwave Techniques for Fabrication of Provisional Facial Prostheses. JProsthet.Dent., 1989; 62: 327-331.
19. Shotwell, J.L., Razzoog, M.E., Koran, A.: Color Stability of Long Term Soft Denture Unas. J.Prosthet.Dent., 1992; 68: 836-838.
20. Tuncer, N.,
Külekçi
, G., Tüfekçioğlu, H.B., Arat, E., İnanç, D., Balkanlı, O.: Alçı Modellerle Çapraz Bulaşmanın Önlenmesinde Mikrodalga Steril izasy onunun Etkinliği. Dİş Hek. Kli., 1990; 3: 45-47.
21. Tuncer, N., Tüfekçioğlu, H.B., Çalıkkocaoğlu, S.: An Investigation on the Compressive Strength of Several Gypsum Products Dried by Microwave Oven with Different Programs. J.Prosthet. Dent., (Baskıda).
22. Tuncer, N.,
Tüfekçioğlu
, H.B.: Mikrodalga Enerjisi ve Su İçinde Kaynatma Yöntemi ile Polimerize Edilen Değişik Akrilik Reçine Örneklerinin Porotize Açısından Karşılaştırılması, tst.Üni.Diş Hek. Fak. Derg., 1990; 24: 139-147.
23. Van Zyl, I.P., Wagner, W.C., Dootz, E.R., Koran, A.: Creep Compliance of Long-Term Soft Denture Liners. J.Dent. Res., 1991; 70: 476, Abstract No.1682.

Thank you for copying data from http://www.arastirmax.com