MICRO LEAKAGE STUDY OF PORCELAIN FUSED TO METAL ALLOYS
Journal Name:
- İstanbul Üniversitesi Diş Hekimliği Fakültesi Dergisi
Key Words:
Keywords (Original Language):
Author Name | University of Author | Faculty of Author |
---|---|---|
Abstract (2. Language):
The present article reports a study ofmicroleakage in the interface
between various metal alloys and porcelain. In this
study chrome-nickel, chrome-cobalt and titanium alloys were
investigated. Microleakage specimen were prepared in
the shape $2.2 mm thick disks which were 1 cm in diameter.
Our findings showed similar microleakage in specimen stored
in water and those not stored in water.
The results indicated that microleakage at porcelain fused
to chrome-cobalt alloy was greater than that found for the other
two alloys.
No significant differences were found between the microleakage
at the intetface of porcelain fused to titanium and porcelain
fused to chrome nickel alloy.
Bookmark/Search this post with
Abstract (Original Language):
Çalışmada metal destekli porselen ara yüzeyinde mikrosızıntı
incelenmiştir. Bunun için krom-kobalf, kromnikel
ve titanyum alaşımlarından 1 cm çapında, lmm
metal kalınlığı ve 1.2 mm porselen kalınlığı olan 20'şer
adet örnek hazırlanmıştır. Sızıntı belirlemesinde oforadyografi
yöntemi kullanılmıştır. Her alaşım grubundaki
örnekler suda beklemiş ve beklememiş olmak
üzere ikiye ayrılmıştır.
Çalışmanın sonucunda suda beklemiş ve beklememiş
örneklerin sızıntıları arasında önemsiz fark olduğu bulunmuştur.
En fazla sızıntı krom-kobalt destekli porselen örneklerde
gözlenmiştir. Krom-nikel ve titanyum destekli
porselen örnekler arasında ise mikrosızıntı farkı
önemsiz bulunmuştur.