KOMPOZİT TABAKALARININ ART ARDA VE ZAMAN ARALIĞI İLE BAĞLAYICI KULLANILARAK YERLEŞTİRİLMESİNİN MAKAS DAYANIMI ÜZERİNE ETKİSİ (IN VITRO ARAŞTIRMA)

The Effect of Bonding Application Between Two Layers of Composite Placed Immediately or After 15 Minutes on the Shear Strength of the Material. (In Vitro Study)

Journal Name:

  • İstanbul Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 2012

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
Purpose:The aim of the comparative study is to evaluate the effect of bonding application between two layers of composite placed immediately or after 15 minutes composite on the shear strength of the material. Material and Methods: The composite (PrimeDent, USA) is placed into special prepared holes on acrylic blocks with standard dimensions. Ultradent (USA) application apparatus is applied to allow the standart placement of the second layer. Shear strengths between two composite layers were measured by the testing machine (Shimadzu Autograph AG-X) and the obtained data analysed statistically. Results: Shear strength of composite in group 2 (18.6 MPa) was the highest (p<0.001). Acid etching procedure had no significant effect on shear strength of placing 15 minutes delayed second layer of composite before applying a bonding agent (p>0.05). Conclusion: Application of bonding between two layers of composite increases shear strength.
Bookmark/Search this post with
Abstract (Original Language): 
Amaç: Kompozit restorasyon yapımında iki kompozit tabakasının yerleştirilmesi arasında zamanın uzadığı durumlarla karşılaşılmaktadır. Çalışmamızda kompozit tabakaları arasına asit ve bağlayıcı uygulaması ve tabakaların yerleştirilmesinde zaman aralığını değişken tutulmasının kompozitin makas kuvvetlerine dayanımı üzerine etkisi araştırılması amaçlanmıştır. Gereç ve Yöntem: Çalışmada standart ölçülerde hazırlanan silikon kalıplara dökülerek elde edilen akrilik bloklarda bulunan özel hazırlanmış kalıplara kompozit materyal (PrimeDent, USA) yerleştirildi. Diğer tabaka kompozitin yerleştirilmesinde Ultradent (USA) firmasının bağlantı aparatından yararlanılmıştır. Deney örneklerinin makas dayanımları, Instron test cihazında ölçüldü. Elde edilen veriler karşılaştırmalı olarak değerlendirildi Bulgular: Çalışmada makas kuvvetlerine dayananım en yüksek Grup 2'de bulunmuştur (18,6 MPa)(p<0.00l) ve en düşük değer Grup 3'te (6,8 MPa)(p<0.001)bulunmuştur. Grup 4 ile Grup l(kontrol) arasında ve Grup 5 arasında makas kuvvetlerine dayanım açısından anlamlı bir fark tespit edilememiştir (p>0.05). Sonuç: İki kompozit tabakasının art arda veya 15 dakika zaman aralığı ile yerleştirilmesinde bağlayıcı uygulanması dişin makas kuvvetlerine dayanımını arttırmaktadır.
FULL TEXT (PDF): 
PDF icon arastirmax-kompozit-tabakalarinin-art-arda-zaman-araligi-ile-baglayici-kullanilarak-yerlestirilmesinin-makas-dayanimi-uzerine-etkisi-vitro-arastirma.pdf
  • 1
17
23
  • Turkish

REFERENCES

References: 

1.
Leinfelde
r KF. Composite resins. Dent Clin North Am, 2000; 29: 359-71.
2.
Masud
i SM, Padtong EA. Effect of delayed light cured activation on bond strengths between composites and adhesives. Arch Orofac Sci, 2006; 1: 36-41.
3.
Rathk
e A, Tymina Y, Haller B. Effect of different surface treatments on the composite-composite repair bond strength. Clin Oral Invest, 2009; 13: 317-23.
4.
Rinastit
i M, Ozcan M Siswomihardjo W, BusscherHJ. Immediate repair bond strengths of microhybrid, nanohybrid and nanofilled composites after different surface treatments. J Dent, 2010; 38(1): 29-38.
5.
Truffier-Boutr
y D, Place E, Devaux J, Leloup G. Interfacial layer characterization in dental composite. J Oral Rehabil, 2003; 30: 74-7.
6.
Shawka
t E,Shortall A, Addison O,Palin W. Oxygen inhibition and incremental layer bond strengths of resin composites. Dent Mater, 2009; 2(5): 1338-46.
7.
Boye
r DB, Chan KC,Rreinhardt JW. Build-up and repair of light-cured
23
composites: bond strength. J Dent Res, 1984; 63(10): 1241-44.
8.
L
i J. Effects of surface properties on bond strength between layers of newly cured dental composites. J Oral Rehabil, 1997; 24:
358-60.
9.
Tezvergi
l A, Lassila LVJ, Vallittu. Composite-composite bond strength: effect of different adhesion primers. J Dent, 2003; 31: 521-25.
10.
Riberi
o JCR, GomesPN, Moyses MR, Dias SC, Pereira LJ, Reiberio JGR. Shear strength evaluation of composite-composite resin associations. J Dent, 2008;
36: 326-30.
11. Eren D, Bektaş ÖÖ, Siso ŞH, Hürmüzlü F. Posterior kompozit restorasyonların tamir bağlanma dayanımlarının mikromakaslama yöntemi ile değerlendirilmesi. SÜ Dişhek Fak Derg, 2007; 16: 18-22.
12.
Staxru
d F, Dahl JE. Role of bonding agents in the repair of composite resin restorations. Eur J Oral Sci, 2011; 119: 316-22.
13.
Lucena-Marti
n C, Gonzalez-Lopez S, Navas-Rodriguez de Mondelo JM. The effect of various surface treatments and bonding agents on the repaired strength of heat-treated composites. J Prosthet Dent, 2001; 86: 481-88.
14.
Tabatabae
i MH, Alizade Y, Taalim S. Effect of various surface treatment on repair strength of composite resin. J Dent TUMS, 2004; 1(4): 5-10.
15. Erdemir A, Eldeniz AÜ, Belli S. Kompozit rezinlerin tamirinde farklı bonding sistemlerin kullanılması. CÜ Dişhek Fak
Derg, 2004; 7(1): 7-10.
16.
Hagg
e MS, Lindemuth JS, Jones AG. Shear bond strength of bis-acryl composite provisional material repaired with flowable
M. TİRYAKİ, F. KORAY, A. GÜLER, A. UZUN
composite. J Esthet Restor Dent, 2002; 14: 47-52.
17.
Rawl
s HR, Esquivel-Upshaw J. Restorative resins. İçinde: Anusavice KJ, editör. Phillips' science of dental material. St. Louis: W.B. Saunders, 2003, p.419.
18.
Dauvillie
r BS, Feilzer AJ, DeGee AJ, Davidson CL. Visco-elastic parameters of dental restorative materials during setting. J Dent Res, 2000; 79(3): 818-23.
19. Bektaş ÖÖ, Siso ŞH, Eren D. Işık kaynakları, polimerizasyon ve klinik uygulamalar. EÜ Dişhek Fak Derg 2006; 27: 117-24.
20.
Crai
g RG. Direct esthetic restorative materials restorative dental materials. vol.10, Mosby, St Louis: Mosby, 1989, p. 255-71.
21. Ersoy M, Özel E, Gökçe K. Farklı uygulama yöntemlerinin kompozit rezinlerin mikrosertlikleri üzerine etkisi. Atatürk Üniv Diş Hek Fak Derg, 2007; 17(1): 28-31.
22. Nalçacı A, Salbaş M. Self-etch adezivin tek kat veya çok uygulamasının makaslama direnci üzerine etkisi. A.Ü. Diş Hek Fak Derg, 2005; 32(1): 19-23.
23. Albers H.
Tooth-colore
d restoratives: principles and techniques. 9th ed., Canada: BC Decker Publishing, 2002, p.149-50.

Thank you for copying data from http://www.arastirmax.com