INVESTIGATION INTO THE EFFECTS OF SILISIUM IN ALUMINIUM ALLOYS ONTO THE MECHANICAL PROPERTIES OF WELDING JOINT
Journal Name:
- Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi
Key Words:
Keywords (Original Language):
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
Since aluminium is a good heat and electric conductor, opaque and especially has high strength per unit weight when alloyed, it has widespread using areas in industry. The weldeability of aluminium and aluminium alloys and improvement of mechanical properties of welded parts will extend the usage area. In this study, the parts manufactured by adding Cu 1 % and Si 2, 3, 4, 5 % to Etial 7 aluminium material has been welded using Metal Inert Gas (MIG) technique. Mechanical properties of welding joint have been examined by hardness, tension and impact tests.
Bookmark/Search this post with
Abstract (Original Language):
Alüminyum birim ağırlık başına yüksek mukavemet özelliği, güvenirliği, uzun ömürlü oluşu, tasarım esnekliği, ısıl performansı, yüksek geri kazanım oranı gibi özellikleri nedeniyle kullanım alanları her geçen gün artmaktadır. Alüminyum ve alaşımlarının kaynak edilebilme özelliklerinin ve kaynaklı parçaların mekanik özelliklerindeki iyileşme kullanım alanını daha da genişletecektir. Bu çalışmada, seçilen Etial 7 alüminyum malzemesine % 1 bakır ve % 2, 3, 4, 5 silisyum ilavesi yapılarak elde edilen parçalar Metal İnert Gaz (MİG) kaynağı ile kaynatıldı. Kaynaklı parçalardan standartlara uygun numuneler hazırlandı. Bu numuneler üzerinde yapılan sertlik, çekme ve çentik darbe deneyleri ile kaynak dikişinin mekanik özellikleri incelendi.
FULL TEXT (PDF):
- 3