DELİKLİ KARBON-EPOKSİ PLAKALARIN GERİLME ŞİDDETİ FAKTÖRLERİ ÜZERİNDE KARŞILAŞTIRMALI BİR ÇALIŞMA

A COMPARATIVE STUDY ON THE STRESS INTENSITY FACTOR OF CARBON EPOXY COMPOSITE PLATES HAVING CENTRAL HOLES

Journal Name:

  • Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi

Publication Year:

  • 2000

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this paper, a comparative study regarding the determination of stress intensity factors (SIF) for non-standard thin composite plates is presented. Carbon-Epoxy composite plates are considered for the study. Unnotched specimens and specimens containing either 4, 6, or 8 mm dia. holes are prepared and then tested. Based on the experimental data thus obtained, two analytical approaches and a finite element fracture analysis tool called FRANC have been used to compare the critical SIF values for this composite material.
Bookmark/Search this post with
Abstract (Original Language): 
Makalede standart olmayan ince kompozit levhaların gerilme şiddeti faktörlerinin (GŞF) hesaplanmasıyla ilgili karşılaştırmalı bir çalışma sunulmaktadır. Çalışmada Karbon-Epoksi kompozit levhalar kullanılmıştır. Çentiksiz ve üzerinde 4, 6 veya 8 mm çapında delik bulunan deney numuneleri hazırlanıp test edilmiştir. Elde edilen deney sonuçlarına dayanarak, iki analitik yaklaşım ve FRANC-sonlu elemanlar programı kullanılarak kompozitin kritik GŞF'leri hesaplanıp karşılaştırmalar yapılmıştır.
FULL TEXT (PDF): 
PDF icon arastirmax-delikli-karbon-epoksi-plakalarin-gerilme-siddeti-faktorleri-uzerinde-karsilastirmali-bir-calisma.pdf
  • 2
109
112
  • Turkish

REFERENCES

References: 

Fracture Toughness Testing and Its Applications. Published by American Society For Testing and Materials, Chicago. 1964.
Glyn, L. Lin, Y. Yui-Wing, M. 1997. Progressive Damage and Residual Strength of a Carbon Fibre Reinforced Metal Laminate. J. of Composite Materials 31 (31), 762-786.
Murti, V. Valliappan, S. Lee, I. K. 1984. Stress Intensity Factor Using Quarter Point Element. J. of Engineering Mechanics, (111), 203-217.
Usama, A. K. 1996. Notched and Pin Bearing Strengths of GFRP Composite Laminates. J. of Composite Materials, (30), 2042-2055.
Waddoups, M. E. Eisenmann, J. R., Kaminski, B. E. 1971. Macroscopic Fracture Mechanics of Advanced Composite Materials. J. of Composite Materials. (5),
446-454.
Wawrzynak, P. Ingraffea, A. R. 1987. Interactive Finite Element Analysis of Fracture Processes: An Integrated Approach. Theoretical and Applied Fracture Mechanics, (8), 137-150.
Whitney, J. M. Nuismer, R. J. 1974. Stress Fracture Criteria for Laminated Composites Containing stress Concentrations. J. of Composite Materials, (8),
253-265.

Thank you for copying data from http://www.arastirmax.com