Effect of Different Ratio of Glass Fiber Reinforcement and Immersing Time in Sea Water on Fatigue Behavior of Polyester Resin Composite
Journal Name:
- Uludağ Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi
Keywords (Original Language):
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
Glass fiber reinforced composites that has an increasing using in marine industry must have some properties.
For the materials used for this aim, life time is one of the most important properties. In this study, the effect of
immersed time in sea water and different volume ratio of glass fiber reinforced polyester resin on fatigue behavior are
investigated. Four different volume ratio glass fiber, non-reinforced, %1, %3, % 6, respectively, reinforced polyester
resin are immersed in sea water and fatigued in 30 minutes and maximum extension and variation of extension are
obtained. Although, there is no effect of reinforcement ratio on extension, extension value decreases by increasing of
immersion time in sea water.
Bookmark/Search this post with
Abstract (Original Language):
Deniz sektöründe kullanımı gittikçe yaygınlaşan cam lifi takviyeli kompozit malzemelerin bir takım özelliklere
sahip olmaları gerekmektedir. Bu amaç doğrultusunda kullanılan malzemeler için ömür en önemli faktörlerden birisidir.
Bu çalışmada cam lifi takviyeli polyester kompozitlerde farklı lif oranlarının ve deniz suyunun yorulma davranışı
üzerinde etkisi incelenmiştir. Çalışmada, takviyesiz, %1 %3 ve %6 olmak üzere dört farklı oranlarda
takviyelendirilmiş polyester reçine numuneleri deniz suyunda bekletilerek 30 dakika süresince yorulma testine tabi
tutulmuş ve maksimum uzama ile uzama değişimi ölçülmüştür. Takviye oranına bağlı olarak uzamada anlamlı bir
değişim meydana gelmemişken; deniz suyunda bekletme süresi arttıkça uzama değeri düşmüştür.