YÜKSEK KARBONLU ÇELİKLERE SU VERME İŞLEMİNİN MEKANİK ÖZELLİKLERE ETKİSİNİN İNCELENMESİ

Effect of Quenching Process on Mechanical Properties of High Carbon Steels

Journal Name:

  • Uludağ Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2015

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, quenching process was applied to high carbon steel and the effect of this process on mechanical properties was investigated. The specimens were placed in a box-type furnace held at the desired temperature and then quenched. According to the tensile test and hardness measurements, it was concluded that the material has become brittle and the tensile strength decreased. The reason for this was higher cooling rate occurred during quenching process.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, yüksek karbonlu çelik malzemeye su verme işlemi uygulanılarak, bu işlemin malzemenin dayanımı üzerindeki etkileri incelenmiştir. Malzeme fırında ısıtılarak belirli bir süre bekletilmiş ve fırından çıkarıldıktan sonra suda soğutulma işlemleri gerçekleştirilmiştir. Uygulanan çekme deneyleri ve sertlik ölçümleri sonucunda, malzemenin su verme işlemiyle gevrekleştiği ve dayanımının düştüğü sonucuna varılmıştır. Bu durumum sebebi olarak, su verme işlemi esnasındaki soğuma hızının yüksek olması düşünülmektedir.
FULL TEXT (PDF): 
PDF icon arastirmax-yuksek-karbonlu-celiklere-su-verme-isleminin-mekanik-ozelliklere-etkisinin-incelenmesi.pdf
  • 2
77
83
  • Turkish

REFERENCES

References: 

1. Acarer, M. (2005). Düşük Karbonlu Çelik Saclardan Çift-Fazlı Çelik Üretimi ve Mho’nın
Çekme Özellikleri Üzerine Etkisi, Teknoloji, 8 (3), 237-244.
2. Çalık, A. ve Özsoy, A. (2004). Isıl Çevrimli Borlama İşleminin SAE 1030 ve SAE1050
Çeliklerine Etkileri, II. Uluslararası Bor Sempozyumu, Eskişehir, 213-218.
3. Demirezen, M., Bayrak, M. ve Öztürk, F. (2006). DIN 41Cr4 Ve DIN42CrCo4 Çeliklerde
Isıl İşlemin Mekanik Özelliklere Etkisinin Araştırılması, Teknoloji, 9 (2), 145-152.
4. Güneş, İ., Ulu, S. ve Ayan, O. (2009). Su verilmiş çeliklerdeki temperleme kademelerinin
aşınma davranışına etkisinin araştırılması, 5. Uluslararası İleri Teknolojiler Sempozyumu
(IATS’09), Karabük.
5. Hwang, G. C., Lee, S., Yoo, J. Y. ve Choo W.Y. (1998). Effect of direct quenching on
microstructure and mechanical properties of copper-bearing high-strength alloy steels,
Materials Science and Engineering: A, 252 (2), 256–268.
6. Köksal, N. S., Uzkut, M., Ünlü, B. S. (2004). Farklı karbon içerikli çeliklerin mekanik
özelliklerinin ısıl işlemlerle değişimi, Deü Mühendislik Fakültesi Fen ve Mühendislik
Dergisi, 6 (2), 95-100.
7. Nayak, S.S., Anumolu, R., Misra, R.D.K., Kim, K.H. ve Lee, D.L. (2008). Microstructure–
hardness relationship in quenched and partitioned medium-carbon and high-carbon steels
containing silicon, Materials Science and Engineering: A,498 (1-2), 442-456.
8. Tavares, S.S.M, Pedroza, P.D, Teodósio, J.R ve Gurova, T. (1999). Mechanical properties of
a quenched and tempered dual phase steel, Scripta Materialia, 40 (8), 887–892.
9. Tomita, Y. (1989). Development of mechanical properties of structural high-carbon low-alloy
steels through modified heat treatment, Journal of Materials Science , 24 (4), 1357-1362.
10. Ulu, S. (2009). DIN17CrNiMo6 Çeliğinin Mikro yapı Özelliklerine Kritik Sıcaklıklar arası
Isıl İşlemlerin Etkisi, Makine Teknolojileri Elektronik Dergisi, 6 (3) , 79-88.
11. Uzkut, M. ve Özdemir, İ. (2001). Farklı Çeliklere Uygulanan Değişen Isıtma Hızlarının
Mekanik Özelliklere Etkisinin İncelenmesi, DEÜ Mühendislik Fakültesi Fen ve Mühendislik
Dergisi, 3(3), 65-73.
12. Yamanoğlu, O. ve Gül. F. (2012). Aşınmaya Dirençli Krom-Vanadyum Alaşımlı Soğuk İş
Takım Çeliklerinin Abrasif Aşınma Davranışı, International Iron & Steel Symposium,
Karabük.

Thank you for copying data from http://www.arastirmax.com