EFFECT OF EMBEDDED DELAMINATIONS ON IMPACT BEHAVIOR OF LAMINATED COMPOSITES

Journal Name:

  • Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi

Publication Year:

  • 2013
DOI: 
10.5505/pajes.2013.95967

Key Words:

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the influence of size and location of embedded delamination on impact behavior of laminated composite was investigated, experimentally. The specimens were produced as for with and without delamination by vacuum assisted resin infusion molding method (VARIM). CEAST-Fractovis plus impact test machine was used in the experiments. As a result of the experiments, the location of delamination on the impact behavior was seen to be more effective than the size of delamination.
Bookmark/Search this post with
FULL TEXT (PDF): 
PDF icon arastirmax-effect-embedded-delaminations-impact-behavior-laminated-composites.pdf
  • 7
303
309
  • English

REFERENCES

References: 

[1] Abrate, S., Impact on Composite Structures, Cambridge University Press, Cambridge, 1-5, 1998.
[2] Hosur, M. V., Adbullah, M. and Jeelani, S., "Studies on the low-velocity impact response of woven hybrid composites", Composite Structures, 67, 253-262, 2005.
[3] Zheng, D. and Binienda, W. K., "Effect of permanent indentation on the delamination threshold for small mass impact on plates", International Journal of Solids and Structures, 44, 8143-8158, 2007.
[4] Symons, D. D., "Characterization of indentation damage in 0/90 lay-up T300/914 CFRP", Composites Science and Technology, 60, 391-401, 2000.
[5] Datta, S., Krishna, A. V. and Rao, R. M. V. G. K., "Low velocity impact damage tolerance studies on glass/epoxy laminates-effects of material, process and test parameters", Journal of Reinforced Plastics and Composites, 23(3), 327-345, 2004.
[6] Baucom, J. N. and Zikry, M. A., "Low-velocity impact damage progression in woven E-glass composite systems", Composite: Part A, 36, 658-664, 2005.
[7] Evci, C. and Gulgec, M., "An experimental investigation on the impact response of composite materials", İnternational Journal of İmpact Engineering, 43, 40-51,
2012.
[8] Freitas, M., Silva A. and Reis L., "Numerical evaluation of failure mechanisms on composite specimens subjected to impact loading", Composite: Part B, 31(3), 199-207, 2000.
[9] Karakuzu, R., Erbil, E., Aktas, M., "Impact characterization of glass/epoxy composite plates: An experimental and numerical study", Composite: Part B, 41, 388-395, 2010.
[10] Aslan, Z., Karakuzu R., Okutan B., "The response of laminated composite plates under low velocity impact loading", Composite Structures, 59, 119-127, 2003.
[11] Aslan, Z., Karakuzu R. and Sayman O., "Dynamic characteristics of laminated woven E-glass-epoxy composite plates subjected to low velocity heavy mass impact", Journal of Composite Materials, 36, 2421-2442,
2002.
[12] Sabancı, E. and Karakuzu, R., "Impact behavior of laminated composites with embedded delaminations", 14th International Materials Symposium, 2012, 606-613.

Thank you for copying data from http://www.arastirmax.com