ALKALİ-SİLİKA REAKSİYONU ETKİSİNE MARUZ AYNI ORANDA SİLİS DUMANI VE UÇUCU KÜL İÇEREN HARÇLARIN MEKANİK ÖZELLİKLERİ

THE MECHANICAL PROPERTIES OF ALKALI-SILICA REACTIVE MORTARS CONTAINING SAME AMOUNTS OF SILICA FUME AND FLY ASH

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2010

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the Alkali silica reaction (ASR) effects on the mortars containing the same proportions of silica fume (SF) and fly ash (FA) instead of cement were investigated. SF and FA, used to control the expansion caused by ASR, were seen to have effects on the expansion and mechanical properties. In the study, SF and FA were substituted for cement in the proportions of 0.5.0%, 10.0%, 15.0% and 20.0%. ASTM C 1260 standard was used to determine the reactivity of aggregates and cement mixtures. In this experimental study, the morphology and chemical composition of the samples exposed to the effects of ASR were analyzed by using a scanning electron microscope (SEM) and Energy Dispersive X-ray (EDX). The results of 14-day experimental measurement showed that the average maximum length of extended control mortar bars was observed to be 0.34% while the lowest average 20% increase of the length SF replace was seen to be 0.04% in the mortar bar. The least strength loss in the mortars exposed to ASR was in those which had 20% SF substitution. Exposed to the effects of ASR, the mortars with 0%-20% SF substitution had a 18% better flexural strength and compressive strength compared to the mortars with FA. As observed on the SEM images, EDX done on the dense and wide ASR cracked areas showed high calcium and low silica percentage.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, çimento yerine aynı oranlarda silis dumanı (SD) ve Uçucu kül (UK) içeren karışımların Alkalisilika reaksiyonu (ASR) etkisi araştırılmıştır. ASR nedeniyle oluşan genleşmenin kontrol altına alınması için kullanılan SD ve UK’nın genleşme ve mekanik özellikleri üzerine etkisi belirlenmiştir. Araştırmada, SD ve UK % 0, 5,0, 10,0, 15,0 ve 20,0 oranlarında çimento yerine ikame edilmiştir. Agrega ve çimento karışımlarının reaktifliğini belirlemek için ASTM C 1260 deney standardı kullanılmıştır. Deneysel çalışmada, ASR etkisinde bırakılan örneklerin morfolojisi ve kimyasal kompozisyonu taramalı elektron mikroskobu (SEM) ve Enerji yayıcı X-ışını analizörü (EDX) kullanılarak incelenmiştir. Deney sonuçlarına göre, 14 günlük ölçümler sonucunda, ortalama en yüksek boy uzamasının kontrol harç çubuklarında %0,34, ortalama olarak en düşük boy uzamasının ise %20 SD ikamesi yapılan harç çubuklarında %0,04 olduğu gözlenmiştir. ASR etkisine maruz kalan harçlarda en az dayanım kaybı %20 SD ikamesi yapılan harçlarda olmuştur. ASR etkisinde bırakılan % 0–20 ikameli SD’li harçlar UK’lı harçlara göre %18 daha iyi eğilme dayanımına ve basınç dayanımına sahip olduğu görülmüştür. SEM görüntüsünde ASR çatlaklarının yoğun ve geniş çatlaklı olduğu bölgelerde yapılan EDX’larda kalsiyum oranı yüksek silis oranı düşük oluşmuştur.
FULL TEXT (PDF): 
PDF icon arastirmax-alkali-silika-reaksiyonu-etkisine-maruz-ayni-oranda-silis-dumani-ucucu-kul-iceren-harclarin-mekanik-ozellikleri.pdf
  • 4
749
758
  • Turkish

REFERENCES

References: 

1. Ramyar, K., Dönmez, H. Andiç, Ö., Araştırma
Raporu, “Alkali-Silis Reaksiyonunun Mineral ve
Kimyasal Katkılar Yardımı İle Kontrol Altına
Alınması”, Türkiye Çimento Müstahsilleri
Birliği, Çimento Endüstrisi-Üniversite İşbirliği
Araştırma Projesi Raporları, Rapor No:9,Ege
Üniversitesi, İzmir, Türkiye, 2002.
2. Malvar, L.J., Cline, G.D., Burke, D.F., Rollings,
R., Sherman, T.W. and Grene, J., “Alkali-Silica
Reaction Mitigation” State-Of-The-Art and
Recommendations, ACI Materials Journal, Vol.
99, No. 5, pp.480–489, Sept-Oct, 2002.
3. Neville, A.M., “Properties of Concrete”, John
Wiley & Sons Inc., New York, U.S.A, 1997.
4. Bagel, L., “Strength and pore structure of ternary
blended cement mortars containing blast furnace
slag and silica fume”, Cement and Concrete
Research, 28 (7):1011–1022, 1998.
5. Taban, S., Şimşek, O., “Zeolitik Tüf Katkı Oranı
ve Deniz Suyunun Çimentonun Fiziksel ve
Mekaniksel Özelliklerine Etkisi”, Gazi Üniv.
Müh. Mim. Fak. Der., Cilt 24, No 1, 145-153,
2009.
6. Dongxue, L., Xinhua, F., Xuequan, W. and
Mingshu, T., “Durability study of steel slag
cement”, Cement and Concrete Research, 27
(7): 983–987, 1997.
7. Monterio, P.J.M. Wang, K., Sposito G., Dos
Santos, M.C., de Andrade W.P., “Influence of
Mineral Admixtures on the Alkali-Aggregate
Reaction”, Cement and Concrete Research,
Vol.27, No.12, pp. 1989-1909, 1997.
8. Ramlochan, T., Thomas, M.,Gruber K.A., “The
Effect of Metakaolin on Alkali-Silica Reaction ‘n
Concrete”, Cement and Concrete Research, 30,
pp. 1139-1150, 2000.
9. Massazza, F., “Evaluation of cements and
cementations systems: history and prospects”,
Proceedings of the second international
symposium on cement and concrete technology
in the 2000s. Istanbul; p. 3–28, 2000.
10. Cyr, M., Carles-Gibergues, A., Moisson, M.,
Ringot, E., “mechanism of ASR reduction by
reactive aggregate powders’”, Advances in
Cement Research, 21, pp 147 –158, 2009.
11. Giaccio, G., Zerbino, R., Ponce, J.M., Batic,
O.R., “Mechanical behavior of concretes
damaged by alkali-silica reaction”, Cement and
Concrete Research, 38: pp. 993–1004, 2008.
12. ASTM C1260-07,. “Standard Test Method for
Potential Alkali Reactivity of Aggregates
(Mortar-bar method)”, Annual book of ASTM
standards, Philadelphia, USA, 2007.
13. Bektas, F., Turanli, L., Topal,T., Goncuoğlu.
M.C., “Alkali reactivity of mortars containing
chert and incorporating moderate-calcium fly
ash”, Cement and Concrete Research, 34,,pp.
2209–2214, 2004.
İ. Demir Alkali-Silika Reaksiyonu Etkisine Maruz Aynı Oranda Silis Dumanı ve Uçucu Kül…
758 Gazi Üniv. Müh. Mim. Fak. Der. Cilt 25, No 4, 2010
14. Fernandez-Jimenez, A., Garcia-Lodeiro, I.,
Palomo, A., “Durability of alkali-activated fly ash
cementations materials” Advances In
Geopolymer Science & Technology, 42: pp.
3055–3065, 2007.
15. Yazıcı, H., Tosun., K., Baradan, B., “Mineral
Katkıların Birlikte Kullanımının ASR
Genleşmesine Etkisi”, Çimento ve Beton
Dünyası, 54, say.60-69, 2005.

Thank you for copying data from http://www.arastirmax.com