Farklı Oranda Nano Silika İçeren Kür Uygulamalarının Çimento Bağlayıcılı Kompozitlerin Dayanımına Etkisinin İncelenmesi

Investigation of the Effect of Curing Applications Containing Different Nano Silica on the Strength of Cementitious Composites

Journal Name:

  • Bilge International Journal of Science And Technology Research

Publication Year:

  • 2017

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the difference between the increase rate of compressive strengths of cement-bonded composites at various ages cured in water and solutions containing different amount of nano-slica has been investigated. In the new generation curing solution developed, 0.5%, 1%, 2% and 3% of nano silica were used. A series of samples were cured in water only for control purposes. In the production of cement-bonded composites, fly ashes which are classified by ASTM standards as class F and C were used. In this way, the increase in strength of cementitious composites containing fly ash in different properties are cured in water and solution with different nano silica amount has been revealed. According to the results obtained from the experimental studies, the highest strength values were obtained from the samples cured in the solution with the 2% ratio of nano silica.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışma ile farklı oranlarda nano silika içeren solüsyonlarda kür edilen çimento bağlayıcılı kompozitlerin farklı yaşlarda basınç dayanımına tabi tutulması sonucu su içerisinde kür edilen numunelere göre dayanım artışının ne oranda olduğu test edilmiştir. Geliştirilen yeni nesil kür solüsyonunda %0,5, %1, %2 ve %3 oranlarında nano silika kullanılmıştır. Üretilen bir seri numune kontrol amacıyla sadece su içerisinde kür edilmiştir. Çimento bağlayıcılı kompozitlerin üretiminde ASTM standartlarına göre F ve C sınıfı özellikler gösteren uçucu küller kullanılmıştır. Buna göre farklı özellikte uçucu kül içeren çimento bağlayıcılı kompozitlerin farklı oranlarda nano silika solüsyonu içerisinde kür edilmesi ve su içerisinde kür edilmesi sonucu gelişen dayanım artışları ortaya konmuştur. Deneysel çalışmalardan elde dilen sonuçlara göre en yüksek dayanım değerleri %2’ lik orana sahip solüsyon içerisinde kür edilen numunelerden elde edilmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-farkli-oranda-nano-silika-iceren-kur-uygulamalarinin-cimento-baglayicili-kompozitlerin-dayanimina-etkisinin-incelenmesi.pdf
  • 1
47
51
  • Turkish

REFERENCES

References: 

Collepardi, M., Collepardi, S., Skarp, U., Troli, R. (2004). Optimization of silica fume, fly ash and amorphous nano-silica in superplasticized high-performance concrete. ACI Spec. Publ., vol. 221, pp. 495–505. Gaitero, J. J., Campillo, I., Guerrero, A. (2008). Reduction of the calcium leaching rate of cement paste by addition of silica nanoparticles. Cem. Concr. Res., vol. 38, no. 8–9, pp. 1112–1118. Hou, P., Qian, J., Cheng, X., Shah, S. P. (2015). Effects of the pozzolanic reactivity of nanoSiO2 on cement-based materials. Cem. Concr. Compos., vol. 55. Jalal, M., Fathi, M., Farzad, M. (2013). Effects of fly ash and TiO2 nanoparticles on rheological, mechanical, microstructural and thermal properties of high strength self compacting concrete. Mech. Mater., vol. 61, pp. 11–27. Kawashima, S., Kim, J. H., Corr, D. J., Shah, S. P. (2012). Study of the mechanisms underlying the fresh-state response of cementitious materials modified with nanoclays. Constr. Build. Mater., vol. 36, pp. 749–757. Keskinateş, M., Felekoğlu, K. T., Felekoğlu, B., Gödek, E. (2016). Çimento Esaslı Lifli Kompozitlerde Su/Çimento Oranı ve Mineral Katkı Türünün Çoklu Çatlak Davranışına Etkisi. Deu Muhendis. Fak. Fen ve Muhendis., vol. 18, no. 54, pp. 440–440, Jan. Li, V. C. (2002). Reflections on the Research and Development of Engineered Cementitious Composites (ECC). Proceedings of the JCI International Workshop on Ductile Fiber Reinforced Cementitious Composites (DFRCC)- Aplication and Evaluation- October. Madandoust, R., Mohseni, E., Mousavi, S. Y., Namnevis, M. (2015). An experimental investigation on the durability of self-compacting mortar containing nano-SiO2, nano-Fe2O3 and nano-CuO. Constr. Build. Mater., vol. 86, pp. 44–50. Nazari, A., Riahi, S. (2011). The effects of SiO2 nanoparticles on physical and mechanical properties of high strength compacting concrete. Compos. Part B Eng., vol. 42, no. 3, pp. 570–578. Sahmaran, M., Yildirim, G., Erdem, T. K. (2013). Self-healing capability of cementitious composites incorporating different supplementary cementitious materials. Cem. Concr. Compos., vol. 35, no. 1, pp. 89–101.

Thank you for copying data from http://www.arastirmax.com