FABRICATION OF 2024 ALUMINIUM ALLOY METAL MATRIX COMPOSITES
REINFORCED WITH Al2O3 PARTICLES
Journal Name:
- Kahramanmaraş Sütçü İmam Üniversitesi Doğa Bilimleri Dergisi
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
In the present work, 2024Al alloy Metal Matrix Composites (MMCs) reinforced
with three different sizes and volume ratios of α- Al2O3 particles have been successfully
produced by using a vortex method and subsequently applied pressure. The density
measurements showed that the samples contained little porosity, and the amount of
porosity in the composites increased with increasing volume ratio and decreasing size of
particles. Scanning Electron Microscopic (SEM) observations of the microstructures
revealed that the dispersion of the coarser sizes of particles was more uniform while
finer particles led to agglomeration of the particles and porosity.
Bookmark/Search this post with
Abstract (Original Language):
Bu çalışmada, Vorteks metodu ve basınç ile üç farklı boyut ve hacim oranlarında
α-Al2O3 partikülleri ile takviye edilmiş 2024Al esaslı Metal Matriksli Kompozitler
(MMK) başarılı bir şekilde üretilmiştir. Yoğunluk ölçümleri, porozitenin çok düşük
olduğunu; partikül oranının artması ve boyutunun düşmesi ile porozite oranının arttığını
göstermiştir. Taramalı Elektron Mikroskobu (SEM) ile yapılan mikroyapı incelemeleri,
partikül boyutunun artmasıyla homojen bir dağılım sağlandığını göstermiş; düşük
boyutlu partiküllerin, partikül topaklanmasına ve porozite oluşumuna neden olduklarını
ortaya çıkarmıştır.