BAZALT DOLGULU POLİMER KOMPOZİTLERİN AŞINMA DAVRANIŞLARI

WEAR PROPERTIES OF BASALT FILLED POLYMER COMPOSITES

Publication Year:

Abstract (2. Language): 
In this study, pin-on-disc wear tests of basalt filled, one of the volcanic rocks as a filler material, (10-70wt.%) LDPE polymer matrix composites were performed depending on various sliding speeds at 20 N loads under dry sliding conditions. Wear tests were carried out with configuration of a polymer pin on a rotating AISI 4140 steel disk in the atmospheric conditions under the loads of 20N and at the sliding speeds of 0.5 m/s and 1.5 m/s. The results showed that increase in basalt content of the basalt filled LDPE composites resulted in a decrease of the friction coefficient and wear rate. While the friction coefficient of LDPE composites was changing between 0.11 and 0.51 and basalt content of the polymer composites, and wear rates of the basalt filled LDPE composites ranged from 7.18x10 -4 mm 3 /m to 2.60x10 -2 mm 3 /m, depending on sliding speeds and basalt quantity
Abstract (Original Language): 
Bu çalışmada, volkanik kayaçlardan bazaltın takviye malzemesi olarak düşük yoğunluklu polietilen (DYPE) matrikse, %10-70 arasındaki değişen oranlarında ilave edilmesiyle elde edilen partikül dolgulu polimer matriksli kompozitlerin değişik sürtünme hızları ve sabit yük altında pin on disk aşınma davranışları incelenmiştir. Aşınma testleri, atmosferik ortamda, 20 N yük altında AISI 4140 çelik diskin 0.5 m/s ve 1.5 m/s dönme hızlarında gerçekleştirilmiştir. Aşınma hızı ve sürtünme katsayısının, bazalt takviyesi ile azaldığı görülmüştür. Bazalt takviyeli DYPE malzemenin kayma hızına ve bazalt miktarına bağlı olarak, sürtünme katsayısı 0.11 ve 0.51, aşınma oranı 7.18x10 -4 -2.60x10 -2 mm 3 /m’ arasında değişmektedir.
61-66