BAKIR ESASLI BRONZ VE PİRİNÇ YATAKLARIN TRİBOLOJİK ÖZELLİKLERİNİN KARŞILAŞTIRILMASI

COMPARISON OF TRIBOLOGICAL PROPERTIES OF COPPER BASED BRONZE AND BRASS BEARINGS

Journal Name:

  • Dokuz Eylül Üniversitesi Mühendislik Fakültesi Fen ve Mühendislik Dergisi

Publication Year:

  • 2003

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
For copper based alloys brass and especially bronze are widely used as journal bearing material. These alloys ensure that expected properties for journal bearings. These materials that have tribological performance good conclusions give at journal bearings. In this study, CuSn10 bronze and CuZn30 brass that were manufactured journal bearings friction and wear properties has been determined and compared. SAE 1050 steel shaft has been used as counter abrader. Experiments have been carried out 20 N load, 1500 rpm and 2.5 h times by using radial journal bearing wear test rig. As a results, high friction coefficient and weigh loss have been obtained at dry condition more than lubricated condition.
Bookmark/Search this post with
Abstract (Original Language): 
Kaymalı yatak malzemesi olarak bakır esaslı alaşımlardan pirinç ve özellikle bronz yaygın bir şekilde kullanılmaktadır. Bu alaşımlar kaymalı yataklardan beklenen özellikleri sağlamaktadırlar. İyi bir tribolojik performansa sahip bu malzemeler, kaymalı yataklarda iyi sonuçlar vermektedir. Bu çalışmada; CuSn10 bronzu ile CuZn30 pirincinden üretilen kaymalı yatakların sürtünme ve aşınma özellikleri belirlenip, birbiriyle karşılaştırılmıştır. Karşı aşındırıcı olarak SAE 1050 çelik mil kullanılmıştır. Deneyler radyal kaymalı yatak aşınma test cihazında 20 N yük, 1500 d/dak ve 2.5 saatte yapılmıştır. Sonuç olarak, kuru ortamda yapılan deneylerde yüksek sürtünme katsayısı ve ağırlık kaybı, yağlı ortamda ise çok daha düşük elde edilmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-bakir-esasli-bronz-pirinc-yataklarin-tribolojik-ozelliklerinin-karsilastirilmasi.pdf
  • 2
103-108
  • Turkish

REFERENCES

References: 

Akkurt M., (1990): “Makine Elemanları Cilt I”, Birsen Yayınevi, İstanbul, s.440.
Atik E., Ünlü B.S., Meriç C. (2001): “Radyal Kaymalı Yatak Aşınması Deney Cihazı
Tasarımı”, Makine Malzemeleri ve Teknolojisi (MAMTEK) Sempozyumu, Manisa, 98-
103.
Backensto A.B. (1990): “Effects of Lubricants on the Properties of Copper-Tin Powders and
Compacts”, N. Jersey, Advences in P/M, Proc. of PM Conf., APMI, PP.303-314.
Coupard D., Castro M.C., Coleto J., Garcia A., Goni J., Palacios J.K. (1997): “Wear
Behaviour of Copper Matrix Composites”, Key Engineering Materials Vols. 127-131,
pp:1009-1016.
Meran C., Yüksel M., König R. (1999): “Pirinç Malzemelerin Kaynak Edilebilirliği ve Uygun
Kaynak Parametrelerinin Tesbiti”, MMO Bildiriler Kitabı Yayın No: 221, s. 206-214.
Niemann G. (1973): “Makine Elemanları”, Cilt-II, s.43.
Paulo Davim J. (2000): “An Experimental Study of the Tribological Behaviour of the
Brass/Steel Pair”, Materials Processing Technology, pp: 273-277.
Prasad B.K. (1997): “Dry Sliding Wear Response of Some Bearing Alloys as Influenced by
the Nature of Microconstituents and Sliding Conditions”, Metall Trans. (A-28), pp.809-
815.
Pratt, G.C. (1973): “Materials for Plain Bearings”, International Metallurgical Reviews, Vol.
18, Review 174, pp. 23-25.
Schatt W., Wieters K.P. (1997): “Powder Metallurgy”, Processing and Materials, EPMA,
Shrewsbury, U.K., pp.492.
Schmidt R. F., Schmidt D.G. (1993): “Selection and Application of Copper Alloy Castings”,
ASM Handbook (II), pp. 346-355.
Ünlü B.S., Atik E., Meriç C. (2002): “Kaymalı Yataklarda Aşınma Mekanizmaları”, Makine
Metal Teknolojisi, Sayı. 127, s. 45-50.
Varol R. (2001): “Cu ve Fe Esaslı T/M Yatak Malzemelerinin Aşınma Özellikleri”, DEÜ
Müh. Fak. Fen ve Müh. Dergisi Cilt 3, Sayı 1, S. 81-90.

Thank you for copying data from http://www.arastirmax.com