ANADOLUDA BİZANS DÖNEMİ KALE YAPILARINDA KULLANILAN TUĞLALARIN FİZİKSEL, KİMYASAL ve MEKANİK ÖZELLİKLERİNİN DEĞERLENDİRİLMESİ

EVALUATION OF PHYSICAL, CHEMICAL AND MECHANICAL CHARACTERISTICS OF BRICKS USED IN CASTLE STRUCTURES OF BYZANTINE PERIOD

Journal Name:

  • Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi

Publication Year:

  • 2010

Key Words:

Keywords (Original Language):

Author NameFaculty of Author
Abstract (2. Language): 
In this study, physical, chemical and mechanical characteristics of brick material used in castle structures of Byzantine period constructed in different cities and different climatic conditions of Turkey shall be analyzed. In this scope, brick samples analyzed in this study are provided from castle structures of Byzantine period constructed in Trabzon, Kütahya, Amasra and İstanbul. Chemical composition of bricks is identified by means of ICP-ES, their mineralogical structure is determined by XRD analysis, whereas mechanical tests are applied to observe their resistance and pozzolanic activity experiments are made on ground bricks having dimension of powder. According to results of XRD and pozzolanic activity analysis, entire bricks having kilned under low temperatures carry pozzolanic characteristics. Bricks of Kütahya castle have low unit weights and high porosity and their mechanical characteristic is lower than that of bricks of other castles. Samples taken from Trabzon Castle have superior characteristics when compared to other samples in terms of physical and mechanical properties. As for bricks of Yoros and Amasra Castle, they represent similar features. As a result of ultrasound speed measurements, it is analyzed that mechanical characteristics of historical castles can be estimated by means of nondestructive methods.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada Türkiye’nin farklı illerinde farklı iklim koşullarında yer alan, Bizanslılar döneminde inşa edilmiş olan kale yapılarında kullanılan tuğla malzemenin fiziksel, kimyasal ve mekanik özellikleri araştırılmaktadır. Bu amaçla; araştırmada kullanılan olan tuğla örnekleri Trabzon, Kütahya, Amasra ve İstanbul’da yer alan Bizans dönemi kale yapılarından temin edilmiştir. Tuğlaların kimyasal kompozisyonu ICP-ES, mineralojik yapısı da XRD analizleriyle, mukavemet özellikleri ise mekanik testlerle tespit edilmiş, tuğlaların öğütülmüş toz boyutlu örnekleri üzerinde de puzolanik aktivite deneyleri yapılmıştır. XRD ve puzolanik aktivite analiz sonuçlarına göre, tüm tuğlaların düşük sıcaklıklarda pişirilmiş olup puzolanik özellik taşıdıkları görülmüştür. Kütahya kalesi tuğlaları düşük birim ağırlıklarına ve yüksek poroziteye sahip olup, mekanik özellikleri de diğer Kale tuğlalarına göre daha düşüktür. Trabzon Kalesinden alınan örnekler fiziksel ve mekanik özellikler açısından diğer örneklere göre üstün özelliklere sahiptirler. Yoros ve Amasra Kalesi tuğlalarının ise genel olarak birbirlerine yakın özellikler taşımaktadır. Yapılan ultrases hızı ölçümleri sonucunda, tarihi tuğlaların mekanik özelliklerinin tahribatsız yöntemlerle de tahmin edilebileceği belirlenmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-anadoluda-bizans-donemi-kale-yapilarinda-kullanilan-tuglalarin-fiziksel-kimyasal-mekanik-ozelliklerinin-degerlendirilmesi.pdf
  • 4
767
777
  • Turkish

REFERENCES

References: 

1. Eyice, S. Bizans Devrinde Boğaziçi, İÜ, Edebiyat
Fak. Yay., No:2236. İstanbul, 1976.
2. Sakaoğlu, N. Çeşm-i Cihan AMASRA. Kültür
Bakanlığı Tarih Vakfı Yay., İstanbul, 1999.
3. Türk Standardı TS EN 14579, Doğal Taşlar-Deney
Metotları-Ses Hızı İlerlemesinin Tayini. Türk
Standardları Enstitüsü, Şubat 2006, Ankara.
4. Türk Standardı TS EN 772-1 Kagir Birimler-
Deney Metodları- Bölüm 1: Basınç
Dayanımının Tayini. Türk Standardları Enstitüsü,
Ankara, Nisan 2002.
5. Türk Standardı TS EN 12390-6 Betonda Yarma
Çekme Dayanımı Saptama Deneyi. Türk
Standardları Enstitüsü, Ankara, Nisan 2002.
6. Türk Standardı TS EN 771-1 Kagir Birimler –
Özellikler- Bölüm 1: Kil Kagir Birimler
(Tuğlalar). Türk Standardları Enstitüsü, Nisan
2005, Ankara.
7. EN 1936, European Standard Naturel Stone Test
Methods. Determination of Real Density and
Apparent Density, and of total and open
Porosity. Brussels, December 2006.
8. ASTMC 618-03 Standart Specification for Coal
Fly Ash and Raw or Calcined Natural Pozzolan
for Use in Concrete.
9. Türk Standardı TS 25, Doğal Puzolan (TRAS) –
Çimento ve Betonda Kullanılan – Tarifler,
Gerekler ve Uygunluk Kriterleri, Ankara,
Aralık 2008.
10. ASTM C 593-95 Standard Specification for Fly
Ash and Other Pozzolans for Use With Lime,
Reapproved 2000.
11. Radivojevic,A. Investigation of late Antique
Bricks from Archaeological Sites of
Contemporary Serbia as a Basis of
Conservation Works. Facta Universitatis,
Architecture and civil Engineering, 3, No:2, pp.
185-193, 2005.
12. Özkaya, A.Ö. Properties of Roman Bricks and
Mortars Used in Serapis Temple in Bergama.
Master of Science in Architectural Restoration, A
Thesis submitted to the Graduate School of
Engineering and Sciences of İzmir Institute of
Technology., İzmir, 2005.
13. Lopez-Arce, P., Garcia-Guinea, J., Garcia, M.,
Obis, J. Bricks in historical buildingis of Toledo
City: characterisation and restoration.
Materials Characterization, 50, 59-68, 2003.
14. Özgen, S. Bizans Tuğlaları Üzerine Bir
İnceleme. Mimar Sinan Üniv. MYO, Restorasyon
Bölümü, Yayınlanmamış teknik rapor, İstanbul,
1994
15. Böke, H., Akkurt, S., İpekoğlu, B. Uğurlu, E.
Characteristics of brick used as aggregate in
historic brick-lime mortars and plasters.
Cement and Concrete Research, 36, 1115–1122.
2006
16. 34. Wild, S., Khatib, J.M., O'Farrell, M. Sulphate
resistance of mortar containing ground brick
calcined at different temperatures. Cement and
Concrete Research 27 (5), 697–709.1997.
17. C.J. McConville, E.W. Lee. Micro-structural
development on firing illite and smectite clayc
compared with that in kaolinite. J.Am.Ceram
Soc. 88, 2267-2277. 2005.
18. Lopez-Arce, P., Garcia-Guinea, J. Weathering
traces in ancient bricks from historic buildings.
Building and Environment, 40, 929-941. 2005.
19. Maritan, L., Nodari, L., Mazzoli, C., Milano, A.,
Russo. Maritan. Influence of firing conditions on
ceramic products: Experimental study on clay
rich in organic matter. Applied Clay Science 31,
1-15, 2006.
20. Trindate, M.J., Dias, M.I., Coroado, J., Rocha, F.
Mineralogical transformations of calcareous
rich clays with firing: A comparative study
between calcite and dolomite rich clays from
Algarve, Portugal. Applied Clay Science 42
(2009) 345-355. 2009.
21. Aardt, J.H.P.; Visser, S. Calcium Hydroxide
Attack on Feldspars and Clays: Possible
Relevance to Cement-Aggregate Reactions,
Cement and Concrete Research, 7, s.643-648,
1997.
22. Mitchell, R.S., Hart,. S.C. Heated mineral
mixture related to ancient ceramic pabteb: XRay
diffraction study. In: Allen R.O, editor,
Archeological chemistry Iv. Washington, DC:
American Chemical Society, 145-55. 1989.
23. Lopez-Arce, P., Garcia-Guinea, J. Weathering
traces in ancient bricks from historic buildings.
Building and Environment 40, 929-941.2000.
24. Akıncı, Ö. Seramik Killeri ve Jeolojisi. Maden
Tetkik ve Arama Enstitüsü Dergisi, s.64, Ankara.
25. Lee, S.; Youn, J.K.; Moon, H.S.; “Phase
Transformation Sequence from Kaolinite to
Mullite Investigated by an Energy-Filtering
Transmission Electron Microscope”, Journal of
American Ceramic Society, 82, (10) 5, s.2841-
2848, 1999.
26. Böke, H., Akkurt, S., İpekoğlu, B. (2006).
Investigation of the Pozzolanic Properties of
Bricks Used in Horasan Mortars and Plasters
in Historic Buildings. Cement and Concrete, 36,
1115-1122
27. Ambroise, J.; Murat, M.; Pera, J.; Hydration
Reaction and Hardening of Calcined Clays and
Related Minerals. V. Extension of the Research
and General Conclusions, Cement and Concrete
Research, 15, s.261-268, 1985.

Thank you for copying data from http://www.arastirmax.com