Al-SiCp MMK'LERDE PARTİKÜL TAKVİYE ORANININ MEKANİK ÖZELLİKLERE VE İŞLENEBİLİRLİĞİNE ETKİSİNİN ARAŞTIRILMASI

INVESTIGATION OF REINFORCEMENT RATE AFFECTING MECHANICAL PROPERTIES AND MACHINABILITY IN Al-SiCp MMCs

Journal Name:

  • Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi

Publication Year:

  • 2006

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
In this study, the effects of various rate of reinforcement materials (SiCp) addition to Al Si7 Mg2 metal matrix composite on mechanical properties and machinability were investigated. It was noticed that the mechanical properties increased with increasing added reinforcement materials rate in 5, 10 and 15 % SiCp reinforced metal matrix composite. The investigation of tool wear and surface roughness was carried out by using different cutting speeds (50, 100 and 150 m/min) and feed rate (0.1, 0.2 and 0.3 mm/rev) at constant depth of cut (1.5 mm) and reinforcement rates. It was observed that, tool wear and surface roughness increased when reinforcement material rate raised at using the same cutting speed and feed values. The tool life was a maximum when 15 % SiCp reinforced metal matrix composite was machined at 150 m/min of cutting speed. The highest surface roughness was also noticed at 15 % SiCp reinforced metal matrix composite machined at 50 m/min of cutting speed and 0.3 mm/rev of feed.
Bookmark/Search this post with
Abstract (Original Language): 
Bu çalışmada, Al Si7 Mg2 metal matriks kompozit malzeme içerisine farklı oranlarda takviye edilen SiCp'in mekanik özelliklere ve talaşlı işlenebilirliğine olan etkisi araştırılmıştır. % 5, 10 ve 15 SiCp takviyeli kompozit malzemenin mekanik özellikleri, takviye oranının artması ile iyileştiği görülmüştür. Farklı kesme hızları (50, 100 ve 150 m/dak) ve ilerleme (0.1, 0.2 ve 0.3 mm/dev) değerlerinde kesici takım aşınması ve yüzey pürüzlülüğü takviye oranına bağlı olarak araştırılmıştır. Sabit kesme hızı ve ilerleme değerlerinde takviye oranının artması ile kesici takım aşınmasının ve yüzey pürüzlülüğünün arttığı görülmüştür. En büyük takım aşınması % 15 SiCp takviyeli metal matriks kompozit malzemenin 150 m/dak kesme hızında işlenmesinde ve en fazla yüzey pürüzlülüğü ise % 15 SiCp takviyeli metal matriks kompozit malzemenin 50 m/dak kesme hızı ve 0.3 mm/dev ilerleme değerinde olduğu tespit edilmiştir.
FULL TEXT (PDF): 
PDF icon arastirmax-al-sicp-mmklerde-partikul-takviye-oraninin-mekanik-ozelliklere-islenebilirligine-etkisinin-arastirilmasi.pdf
  • 3
313
320
  • Turkish

REFERENCES

References: 

Akdoğan, A., Özben, T. 2001. "Sıkıştırma Döküm Yöntemi ile Üretilen SiCp Takviyeli Metal Matriksli Kompozit Malzemelerin Mekanik Özelliklerinin İncelenmesi", II. Makina Malzemesi ve İmalat Teknolojileri Sempozyumu, Manisa, 358-367.
Bedir, F., Ögel, B. 2004. "SiCp Katkılı Al Kompozitlerin Sertlik, Mikroyapı Özellikleri ve Aşınma Davranışlarının İncelenmesi", 11. International Conference on Machine Design and Production (UMTIK), Antalya.
4
Mühendislik Bilimleri Dergisi 2006 12 (3) 313-320
319
Journal of Engineering Sciences 2006 12 (3) 313-320
Al-SiCp MMK'lerde
Partikül
Takviye Oranının Mekanik Özelliklere ve İşlenebilirliğine Etkisinin..., E. Kılıçkap, T. Özben, O. Çakır
Bergman, F., Jacobson, S., Abdel Moneim, M.E. 1996. Comments on Tool Wear Mechanisms in Intermittent Cutting of Metal Matrix Composites, Wear, Vol. 1971-2, 295-296.
Cöcen, Ü., Önel, K. 1997. "Metal Matrisli Kompozitlerde Dayanım Artımı ve Düktilite", 7. Denizli Malzeme Sempozyumu, 138-145.
Ejiofor, J. U., Reddy, R. G. 1997. Developments in Thr Processing and Properties of Particulate Al-Si Composites, J. of the Materials Society, Vol. 79,
31-34.
El-Gallab, M., Sklad, M. 1998. Machining of Al/SiC Particulate Metal-Matrix Composites, Part II: Workpiece Surface Integrity, Journal of Materials Processing Technology, Vol.83, p.277-285.
El-Gallab, M., Sklad, M. 1998. Machining of Al/SiC Particulate Metal-Matrix Composites, Part I : Tool Performance, Journal of Materials Processing
Technology, Vol : 83, p.151-158.
El-Gallab, M., Sklad, M. 2000. Machining of Al/SiC Particulate Metal-matrix Composites, Part III: Comprehensive Tool Wear Models, Journal of Materials Processing Technology, Vol. 10, p.10-20.
Elsevier Materials
Selector
. 1997. Vol. 2, UK.
Embury, J. D.1985. Metal. Trans. A. 16, 2191-2200.
Guo, Z. X., Derby, B. 1995. Solid-state Fabrication and Interfaces of Fibre Reinforced Metal Matrix Composites, Progress in Materials Science, Vol. 39,
Issues 4-5, 411-495.
Kılıçkap, E. 2003. Doktora Tezi, Fırat Üniversitesi Fen Bilimleri Enstitüsü.
Kılıçkap E., Çakır O., Aksoy M., İnan A. 2004.
"% 5 SiC(p) Takviyeli Al Si7 Mg2 Metal Matriksli
Kompozitin Soğuk Talaşlı İşlenmesinde Takım Ömrü ve Yüzey Pürüzlülüğünün Araştırılması", 11. International Conference on Machine Design and
Production (UMTIK), Antalya, p. 891-902.
Kılıçkap E., Çakır O., İnan A.
2004
. "Investigation of Tool Wear and Surface Roughness in Turning of Metal Matrix Composites", 3rd International
Conference On Advanced Manufacturing
Technology (ICAMT), Malaysia.
Kılıçkap, E., Cakır O., Aksoy, M., İnan, A. 2005. Study of tool wear and Surface Roughness in Machining of Homogenized SiCp Reinforced Aluminium Metal Matrix Composites, Journal of Materials Processing Technology, 164-165, 862¬867.
Lewondowski, J. J., Altmışoglu, A. 1992. Effect of Casting Conditions and Deformation Processing on
A356 Aluminium and A356-Vol. % SiC
Composites, J. of Composite Materials, Vol. 26, 14.
Li, X., Seah, W. K. H. 2001. Tool Wear
Acceleration in Relation to Workpiece Reinforcement Percentage in Cutting of Metal Matrix Composites, Wear, Vol. 2472, 161-171.
Lin, J. T., Bhattacharyya, D., Ferguson, W.G. 1998. Chip Formation in The Machinability of SiC Particle- Reinforced Aluminium- Matrix Composites, Composites Science and Technology,
Vol. 58, 285-291.
Matthew, F. L., Rawlings, R. D. 1994. Composite Materials Engineering and Science, Charpman & Hall, Londan.
Özben,
T
. 2001. Yüksek Lisans Tezi, Yıldız Teknik Üniversitesi Fen Bilimleri Enstitüsü.
Slezenev, M. L., Slezenev, I. L., Cornie, J. A., Argon, A. S., Mason, P. R. 1998. "Effect of Composite Particle Size and Heat Treatment on The Mechanical Properties of Al-4.5wt. % Cu Based Alumina Particulate Reinforced Composites",
Presented At The International Congress and Exposition, Detroit, 23-26.
Taminger, K. M. B. 1999. Analysis of Creep Behavior and Parametric Modals for 2124 Al and 2124 Al + SiCw Composite, Master of Science in Materials and Engineering, Virginia Polytechnic Institute and State University.
Weinert, K. 1993. A Consideration of Tool Wear Mechanism When Machining Metal Matrix
Composites (MMC), Annals of the CIRP, Vol. 42 95-98.

Thank you for copying data from http://www.arastirmax.com