EFFECTS OF MECHANICAL ACTIVATION ON THE CARBOTHERMAL REDUCTION OF CHROMITE WITH METALLURGICAL COKE
Journal Name:
- Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi
Keywords (Original Language):
| Author Name | University of Author | Faculty of Author |
|---|---|---|
Abstract (2. Language):
The carbothermal reduction of mechanically activated chromite with metallurgical coke under an argon atmosphere
was investigated at temperatures between 1100 and 1400°C and the effects of the mechanical activation on chromite
structure were analyzed by x-ray diffraction (XRD) and scanning electron microscopy (SEM). An increase in specific
surface area resulted in more contact points. The activation procedure led to amorphization and structural
disordering in chromite and accelerated the degree of reduction and metalization in the mixture of chromite and
metallurgical coke. Carbothermal reduction products were analzed by using scanning electron microscopy
(SEM/EDS).
Bookmark/Search this post with
Abstract (Original Language):
Mekanik aktive edilmiş kromitin argon atmosferi altında metalurjik kokla karbotermal redüksiyonu 1100 – 1400°C
sıcaklık aralığında incelenmiş ve kromit yapısına mekanik aktivasyonun etkisi X-ışını difraksiyonu (XRD) ve taramalı
elektron mikroskobisi (SEM) ile analiz edilmiştir. Yüzey alanındaki artış daha fazla temas noktasının oluşmasına
neden olmuştur. Aktivasyon prosedürü kromitte amorflaşma ve yapısal düzensizliğe neden olmuş ve kromit ile
metalurjik kok karışımında redüksiyon derecesini ve metalleşmeyi hızlandırmıştır. Karbotermal redüksiyon ürünleri
taramalı elektron mikroskobisi (SEM/EDS) ile analiz edilmiştir.