YENİ VE ARTIK KROM KOBALT ALAŞIMI KULLANILARAK HAZIRLANAN İSKELET BÖLÜMLÜ PROTEZLERDE INTERNAL POROZITENTN RADYOGRAFIK OLARAK İNCELENMESİ

RADIOGRAPHIC EVOLUTION OF POROSITES IN REMOVABLE PARTIAL DENTURE CASTING USING NEW METAL AND REUSE EXCESS COBALT- CHROMIUM ALLOYS

Journal Name:

  • Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 2003

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
Chromium-cobalt alloy have been used to construct cast removable partial denture frameworks since 1933. Although the Cr- Co alloys have desirable properties, fracture of the various metallic elements of the removable partial denture is common and may be caused by structural defects (voids, porosities and inclusions). The purpose of this study was to determine the effect of reuse excess Cr-Co alloys existence of structural delects removable partial denture frameworks by means of radiographs. 40 removable partial denture frameworks for upper law were obtained from Cr-Co alloy {Wironit). The specimens were divided 4 casting groups. 1- 100% new metal used 2- 25 % reuse excess alloy 3- 50 % reuse excess alloy 4- 100 % reuse excess alloy Removable denture framework evaluated with occlusal radiographs for existence of internal porosities. Statistical evaluation was performed with one-way A NOVA (analysis of variance) (1V0.001). The multiple comparisons of means were used Duncan's post hoc. Test, The lowest internal porosities (structural defects) were seen in new metal groups. There were statistical difference between 10Û % new metal and 75-100% reuse excess alloy.
Bookmark/Search this post with
Abstract (Original Language): 
Krom Kobalt alaşımları döküm hareketli protezlerin yapımında 1933'ten bu yana kullanılmaktadır. Krom Kobalt alaşımlarının iyi özellikleri yanında hareketli parsiyel protezin çeşitli metalik parçalarının kırılması oldukça yaygındır. Buna çukurcuk, porozite gibi yapısal defektler sebep olmaktadır. Bu çalışmada Cr-Co alaşımının tekrar kullanılmasının hareketli parsiyel protez iskeleti içinde oluşan defekt-İcrin radyografik olarak tespit edilmesi amaçlanmıştır. Üst çene modeli için 40 hareketli bölümlü protez iskeleti Cr-Co alaşımı (Wironit) kullanılarak elde edilmiştir. Örnekler 4 gruba ayrılmıştır. % 100 yeni metal % 25 arlık meta! % 50 artı k metal % 100 artık metal İskelet dökümlerin internal poroziteleri oklüzal radvojırafilerle değerlendirildi. İstatistiksel değerlendirme tek yönlü" varyans anali/i ile yapıldı (P<Ü.00l). Ortalamaların çoklu karşılaşürılması Duncan testiyle yapıldı. En düşük internal porozite % 1Ü0 saf metal dökümlerde tespit edildi, % 100 saf döküm ile % 75-100 atık metal kullanımı arasında istatistiksel utarak fark tespit edildi.
FULL TEXT (PDF): 
PDF icon arastirmax-yeni-artik-krom-kobalt-alasimi-kullanilarak-hazirlanan-iskelet-bolumlu-protezlerde-internal-porozitentn-radyografik-olarak-incelenmesi.pdf
  • 2
1-6
  • Turkish

REFERENCES

References: 

1. O'Brien W.J. Dental materials: Properties and £c]cciion; Quintesencc Publishing Co. Chicago, 1989, 363-367,
2. Wataha J. Alloys for prosihodontic restorations. J Prosthet Dent 87: 351-63,2002.
3. Moffa J .P., Lugassy AA, Guckes AD, Gitttcman L. An evaluation of non-precious alloys for use with porselen veners pail 1, Physical properties: J Prosthet Dent 30: 424; 1973.
4. Hugest EF, Ciujan S, Dııivedi NN: Characterization of two newly developed nickel- chrome alloys. J Denl Res ( special issue) 53: 328, 3974 ( Aks I No. 733).
5. Bcıı.ur Z, Patael H, Cordash HS, Haharov H. The fracture of cobalt chromium alloy removable partial dentures Quint.lnt 17; 797-301, 1986.
6. Van Noort R, l^amb D.I. A scanning electron microscope study of Co- Cr partial dentures, fractured in service J Dent 12, 122-6, 1984.
7. Lewis AJ. Failure of removable partial denture casting during service J Prosthet Dent 39: 147-9,1978.
8. Earnshaw R. Fatigue tests on a dental cobalt-chromium alloy Br Dent J 110: 341-6, 1961.
9. Hesby DA, Kobe s P, Garver DG, Pcllcv GB.
Physical properties of repeatedly used nonpreeious metal alloy J Prosthet Dent 44:3, 291-93, 1980.
10.
Akso
y G, Orgcv V, Bıçakçı A: Farklı eritme yöntemlerinin yeni baz metal alaşımları ile bunlara değişik oranlarda artık alaşım karıştırılmış olanlarının yüzey niteliği ve sertlikleri üzerindeki etkilerinin karşılaştırılması. Ege Diş HekFakDerg 16: 144-151, 1995.
11. Hcnriques GET, Consani S, Almeida Rollo J. MD, İsilva FA. Soldering and remelting influence on fatigue strength of cobalt- chromium alloy. J Prosthet Dent 78: 146-52. 1997.
5
Atatürk Üniv.Diş Hek.Fak.Derg, Cilt: 13, Sayı:2, Sayfa: 1-6,2003
BAYINDIR. AKYALÇIN
12. Lewis AJ: Radiographic evaluation of porosities in removable partial denture castings. J Prothet Dent 39: 278,1978,
13. Pascoe DF,Wiıııırıer J: A radiographic technique for detection of internal defects in dental castings. J Prosthet Dent 39: 150, 1978.
14. Henrikson CO, Wictorin L, Osterberg J: Radiographic detection of defects in soldered joints of dental gold alloys, Odorit Rev. 24: 161, 1973.
15. Wictorin L, Julin P, Mollersten L: Roentgenological detection of casting defects in cobalt-chromium alloy frameworks J Oral Rehabil. 6: 137, 1979.
10. Eisenburger M, Addy N. Radiological examination of dental castings, a review of tho metod and comparison of the equipment J Oral Reh 29; 7, 609, 2002.
17. Elorbi , Ismail Y, Azarbal M, Saini TS. Radiographic detection of porosities in removable partial denture casting. J Prosthet Dent 54: 5,674-77,1985.
IS. Strandman E, Lockwandt P: Equipment for standardizing casting of Co-Cr alloys in dentistry. Odont Revy.27: 145 154,1975.
19. Phillips WR; Elements of dental materials, Chapters WB Sounders Company i 977.
20.
Ate
ş M. Şakar O, Beyli MS. Döküm bölümlü protezlerde metalin tekrar kullanıl masının poroziteye etkisi Diş HekDcrg 30:204-208,1998.
21.
Ate
ş M, Şakar O, Beyti MS, Aydın Z. Kıymetsiz metal alaşımlarının tekrar dökülmesinin sitotoksisite yününden incelenmesi. Bölüm 1. Dış Hek Derg 30: 227-231,1998.

Thank you for copying data from http://www.arastirmax.com