METAL-KOMPOZİT RESİN ARAYÜZÜNDE ORTAYA ÇİKAN MİKROSIZINTIYA RETANSİYON SİSTEMLERİNİN ETKİSİNİN ARAŞTIRILMASI

INVESTIGATION OF THE EFFECT OF RETENTIVE SYSTEMS TO MICROLEAKAGE AT THE METAL-RESIN INTERFACE

Journal Name:

  • Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi

Publication Year:

  • 2004

Key Words:

Keywords (Original Language):

Author NameUniversity of AuthorFaculty of Author
Abstract (2. Language): 
The bonding between framework metals and resins requires further study because adhesive failures can promote microleakage, discoloration and stains in composites. Several factors affect the microleakage between metal alloys and resins used in prosthodontics. The aim of this in vitro study was to investigate and compare the effects of various metal surface treatments on microleakage between a metal alloy and a resin used in the fabrication of a fixed partial denture. A total eighty-cylindrical metal specimens (15 mm diameter X 1.1 mm thickness) were cast in Ni-Cr alloy, divided into 4 equal groups corresponding to 4 types of retention: sandblasting, chemical, mechanical with 0.4 mm and 0,6 mm beads, A composite resin material were light polimcrized in the unit according to the manufacturer's spesifications. Each specimen was immersed for 4 hours in Ca45 isotope solution. Microleakage at the metal-resin interlace was determined by using the autoradiographic method immediately following the polimeri/.ation and third month. The highest microleakage was measured in sandblasted specimens at the the third month, while the less microleakage measured in mechanical retention. It was concluded that microleakage is inevitable at the metal-resin interface, but it can be reduced by using some methods of retention
Bookmark/Search this post with
Abstract (Original Language): 
Metal altyapı ve resin arasında bağlantıdaki adheziv ataların kompozitlcrde mikrosızıntı, renk değişikliği ve enar renklenmesi yaratabilmesi nedeniyle araştırılması .erekli bir konudur. Protctik amaçlı kullanılan metal ve esinlerin arasında ortaya çıkan mikro s izinliyi etkileyen 'irçok faktör mevcuttur. Bu in vitro çalışmanın amacı sabit TOtezlerin yapımında kullanılan bir metal alaşımı ile resin lateryali arasında ortaya çıkan mikrosızıntı üzerinde çeşitli ıetal yüzey hazırlama uygulamalarının etkisini araştırmak e karşılaştırmaktır. Toplam seksen silindirik metal örnek 15 mm çap X 1.1 mm kalınlık) bir Ni-Cr alaşımıyla löküldü. Örnekler.kumlama, kimyasal, 0.4 ve 0.6 mm bilya aplı mekanik retansiyon şekillerini oluşturacak şekilde lort grupta hazırlandı. Bir kompozit resin materyal metal Ityapı üzerine üretici firma direktifleri doğrultustınca ışık ihazında polimerice edildi. Örnekler Ca45 izotop olUsyaniuda 4 saat süre ile bekletildi. Metal-resin j-ayüzünde mikrosızıntı, polimerizasyonu takiben hemen re üç ay sonra otoradyografik yöntem kullanılarak telirlendi. En düşük mikrosızıntı mekanik retansiyon öııteminde belirlenirken, en yüksek mikrosızıntı kumlama 'apılmış. örneklerde üç ayhk sürede ortaya çıkmıştır, »letal-resin arayüzünde mikrosizinlinin kaçınılmaz olduğu mcak bazı retansiyon yöntemlerinin uygulanmasıyla Lzaltılabileeegi sonucuna varılmıştır.
FULL TEXT (PDF): 
PDF icon arastirmax-metal-kompozit-resin-arayuzunde-ortaya-cikan-mikrosizintiya-retansiyon-sistemlerinin-etkisinin-arastirilmasi.pdf
  • 2
17-23
  • Turkish

REFERENCES

References: 

1.
Kocabalka
n E. Di seçkimi iğin de kullanılan materyallerin günümüzdeki uygulamaları, DÜ Dişhek Fak Der 1992;3:141-4.
2.
Kocabalka
n E. Dişhekimliğinde mikrosızıntı ve tespit yöntemleri. Atatürk Üni Diş Hek Fak Derg 1993;3:52-6.
3. Crim GA, Garcia-Godoy F. Microleakage: the effect of storage and cycling duration, J Prosthet Dent 1987;57:574-6.
4. Oruç S, Kama B. Investigation of microleakage between titanium and porcelain. J Oral Rchabil 1999;26:529-33.
5. Taylor MJ, Lynch E, Microleakage. J Dent 1992;20:3-10.
6. Kocabalkan
E
. İki farklı pnlimerizasyon yönteminin resin-metal ara yüzünde ortaya çıkan mikrosjzınüya etkisi. GÜ Dişhek Fak Der 1993;10:41-8.
7. Kocabalkan E, Dönmez F, Dcmirköprülü H. Marginal adaptation of resin in relation to application technique and use of a dental adhesive system. JMU Dent Fac 1994;2:424-&
8. Kocabalkan
E
, Dönmez. F. Kron yapıştırılmasında kullanılan materyallerin mikrosızınLisınm in vitro olarak saptanması. Atatürk Üni- Diş Hek. Fak. Derg 1994;4:39-43.
9.
Kocabalka
n E, Dönmez F. Üç farklı resin inley uygulamasının mikrosızıntı açısından karşılaştırılması. AtaLürk Üni Diş Hek Fak Derg 1994;4:58-64.
10.
Burga
z Y, Kocabalkan E. Üç farklı retansiyon yöntemi uygulanmış meta! altyapı üzerine hazırlanan iki kompozit resinin metal-resin arayüzünde ortaya çıkan mikrosızıntısmın değerlendirilmesi. GÜ Dişhek Fak Der 1993;10:23-40.
22
Atatürk Üniv.Diş Hek.Fak.Derg. Cilt: 14, Sayı 2, Sayfa: 17-23, 2004
TURGUT, YALÇIN
11.
Kocabalka
n E, Burmaz Y, Demirköprülü H. Resin bağlı köprülerde diş-metal arayüzünde ortaya çıkan ınikrosıznnTımn saptanması. GÜ Dışhek Fak Der 1993;10:65-76.
12. Rominıı M, Laktos S, Florita Z, Negrutiu M. Investigation of microleakage at the interface between a Co-Cr based alloy and four polymeric veneering materials. J Prosthet Dent 2002;87:620-4.
13. Sharp B, İVfarton D, Clark AK, KfTectiveness of surface treatments in controlling microleakage of the acrylic resin-mctal framework interface. J Prosthet Dent 2000;84:617-22.
14. Bnrgaz Y, Kocabalkan
E
. Sabit protezlerde kıymetsiz metal alaşımı ile akrilik resin estetik materyal bağlantısında klasik metodla RBS bonding tekniğinin karşılaştırılması. GÜ Di5hck Fak Der 1992;10:1-11.
15. Bar/iky I, Myers ML, Cooper LB, Graser ON. Mechanical and chemical retention of laboratory- cured composite to mead surfaces. J Prosthet Dent 1988;59:131-7.
16. Matsnmura H, Nakabayashı N. Adhesive 4-META/MMA-TBB opaque resin with poly(methyl meihacrylate)-coated titanium diokside. J Dent Res 1988;67:29-32.
17. Tanaka T, Fujiyama E, Shiıniîu H, Atsiıta M. Surface treatment of nonprecious alloys for adhesion-fixed partial dentures. J Prosthet Dent 1986;55:456-62.
18. Staffaiiau RS. Hembree JH, Rıvçrs JA, Myeri ML, Kilgorc JL leakage study of three cslheric veneering materials. J Prosthet Dent 1985;54:204-6.
19. Kern M, Thompson VP. Influence of prolonged thermal cycling and water storage on the tensile bond strength of composite to NiCr alloy. Dent Mater 1994;10:19-25.

Thank you for copying data from http://www.arastirmax.com